Crystallization behaviors of nanosized MgO particles from magnesium alkoxides.
The effects of the size of the alkoxy group on the thermal decomposition behavior of magnesium alkoxides (magnesium methoxide and ethoxide) and the crystallization behavior of MgO was investigated using thermogravimetry, Fourier-transformed infrared spectroscopy, X-ray powder diffraction, and transmission electron microscopy. As the size of the alkyl group increased, the decomposition temperature decreased and resultant MgO crystallization of the alkoxide precursor was enhanced. In an inert N(2) atmosphere, the decomposition temperature of magnesium ethoxide was about 260 degrees C, which was lower than that of magnesium methoxide by approximately 70 degrees C. The degree of the crystallization of MgO particles from the ethoxide was also significantly higher than that of the methoxide. This result is explained in terms of the O-R bonding strength of the alkoxide. With use of the Kissinger method, the activation energy for the thermal decomposition of magnesium alkoxide was found to be dependent on the size of the alkyl group. The activation energies were 161+/-23 and 130+/-24 kJ/mol for the magnesium methoxide and the magnesium ethoxide, respectively.
Jung
Hyun Suk
HS
School of Materials Science & Engineering, Seoul National University, South Korea.
Lee
Jung-Kun
JK
Kim
Jin-Young
JY
Hong
Kug Sun
KS