title: Comparison of the recyclability of flame-retarded plastics.
abstract: Mechanical recycling of plastics from waste from electrical and electronical equipment (WEEE) is increasingly expected by regulators and demanded by original equipment manufacturers (CEMs); however, mechanical recycling is generally recognized to be the most economically costly and technically challenging method of recovering WEEE plastics. With 12% of WEEE plastics requiring the use of flame-retardants in order to ensure appropriate levels of consumer fire safety, there is a distinct need for data from comparative tests on recyclability of various flame-retarded plastics. Ten commercially available flame-retarded plastic grades commonly used in electronic equipment (eight "halogen-free" grades and two grades containing brominated flame-retardants (BFRs)) were subjected to two different recycling scenarios. A standard recycling scenario was carried out by repeatedly extruding the materials and an accelerated hydrolysis scenario was carried out to study the influence of humidity from air during use on the process. Both, virgin and recycled materials were tested for a potential formation of polybrominated dibenzodioxins/furans (PBDD/Fs), their mechanical properties were assessed and the fire safety rating was determined. Results indicate that none of the tested materials showed a potential to form the PBDD/Fs regulated by the German Chemicals Banning Ordinance. The halogen-free plastic grades showed a significant deterioration of mechanical properties after recycling, whereas those plastics containing BFRs were able to pass all test criteria, thus maintaining their original properties. With respect to the fire safety rating, none of the eight tested halogen-free plastic grades could maintain their fire safety rating after five recycling loops, whereas both BFR plastics continued to achieve their fire safety ratings. Therefore the tested BFR containing plastic materials showed superior recycling properties compared to the tested halogen-free plastic grades with respect to all investigated parameters.
authors.affiliation: Techno Polymer Co., Ltd., 100 Kawajiri-cho, Yokkaichi, Mie 510-0871, Japan.
authors.forename: Takaretu
authors.initials: T
authors.lastname: Imai
authors.forename: Stephan
authors.initials: S
authors.lastname: Hamm
authors.forename: Klaus P
authors.initials: KP
authors.lastname: Rothenbacher
mesh_terms: D003247:Conservation of Natural Resources; D004581:Electronics; D005411:Flame Retardants / Q000032:analysis*; D006813:Humidity; D006868:Hydrolysis; D008422:Materials Testing; D010969:Plastics; D018570:Risk Assessment
chemical_list: D005411:Flame Retardants; D010969:Plastics