An evaluation of ion-textured aluminum oxide dental implants.
A study was undertaken to evaluate the ion-beam texturing of aluminum oxide as a means of providing a surface which will produce a biological prosthetic attachment. A wafflelike pattern of surface contours 150 x 75 x 35 microm deep was produced on cylindrical dental implants. The textured surfaces were compared to the as received surfaces in adult mongrel dogs. Implants were inserted into surgically modified healed extraction sites and were left in place for six months. Post-sacrifice mechanical testing was used to quantify the displacement response of the implants. The clinical, radiographic and mechanical testing evaluations did not reveal any statistically significant differences in the performance of the dental implants. However, it was observed that anatomical site and mandibular geometry with respect to implant size play a significant role in affecting implant retention.
Weinstein
A M
AM
Biomaterials Laboratory, Tulane University, New Orleans, Louisiana 70112, USA.
Cook
S D
SD
Klawitter
J J
JJ
Weinberg
L A
LA
Zide
M
M
D000537:Aluminum Oxide / Q000737:chemistry*; D000818:Animals; D015921:Dental Implants; D003799:Dental Stress Analysis; D004285:Dogs; D008334:Mandible / Q000000981:diagnostic imaging; D008422:Materials Testing; D011859:Radiography; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors
D015921:Dental Implants; D000537:Aluminum Oxide