Reconstruction of a defect of the rotator cuff with polytetrafluoroethylene felt graft. Recovery of tensile strength and histocompatibility in an animal model.
We reconstructed defects in the infraspinatus tendon u sing polytetrafluoroethylene (PTFE) felt grafts in 31 beagle dogs and examined the mechanical responses and histocompatibility. Except for one infected specimen, all the reconstructed infraspinatus tendons healed. We examined eight specimens each immediately after surgery and at six and 12 weeks. The ultimate tensile strength of the reconstructed tendons was 60.84 N, 172.88 N, and 306.51 N immediately after surgery and at six and 12 weeks, respectively. The stiffness of the specimens at the PTFE felt-bone interface was 9.61 kN/m, 64.67 kN/m, and 135.09 kN/m immediately after surgery and at six and 12 weeks, respectively. Six tendons were examined histologically at three, six, 12 and 24 weeks. Histological analysis showed that there was ingrowth of fibrous tissue between the PTFE fibres. Foreign-body reactionswere found at the margin of the PTFE-bone interface between 12 and 24 weeks. The mechanical recovery and tissue affinity of PTFE felt to bone and to tendon support its use for reconstruction of the rotator cuff. The possible development of a foreign-body reaction should be borne in mind.
Kimura
A
A
Department of Orthopaedic Surgery, Sapporo Medical University School of Medicine, Japan.
Aoki
M
M
Fukushima
S
S
Ishii
S
S
Yamakoshi
K
K
D000818:Animals; D004195:Disease Models, Animal; D004285:Dogs; D005260:Female; D008422:Materials Testing; D011138:Polytetrafluoroethylene; D019736:Prostheses and Implants; D011475:Prosthesis Failure; D017006:Rotator Cuff / Q000473:pathology / Q000503:physiopathology / Q000601:surgery*; D000070636:Rotator Cuff Injuries; D013718:Tensile Strength
D011138:Polytetrafluoroethylene