Adsorption of a polymeric siloxane surfactant on carbon black particles dispersed in mixtures of water with polar organic solvents.
The adsorption of a rake-type polymeric siloxane surfactant (polydimethylsiloxane-graft-polyether copolymer) on carbon black (CB) particles dispersed in mixtures of water with polar organic solvents (ethanol, formamide, or glycerol) has been investigated. The adsorption obeys the Langmuir isotherm at low surfactant concentrations (below the critical micelle concentration, CMC). At these conditions, the average surface area occupied by one siloxane surfactant follows the sequence water+glycerol mixture >plain water >water+ethanol mixture. At higher surfactant concentrations in the solution in contact with the particles, a sharp increase in the adsorbed amount is observed. The adsorbed layer thickness has been determined by dynamic light scattering. Below the CMC the adsorbed layer thickness is less than 10 nm. Above the CMC, the adsorbed layer thickness increases to 20-30 nm, a length scale comparable to the diameter of the siloxane surfactant micelles in aqueous solution. This fact, together with SANS data that we have obtained in the absence of added polar organic solvent, indicates that the structure of the adsorbed layer is similar to that of micelles. The findings presented here are relevant to waterborne coatings and ink formulations, where polymeric surfactants are used in conjunction with polar organic solvents.
Lin
Yining
Y
Department of Chemical Engineering, University at Buffalo, The State University of New York, Buffalo, NY 14260-4200, USA.
Smith
Thomas W
TW
Alexandridis
Paschalis
P