Polymer depletion-induced instability of silica suspensions in the presence of flexible and semiflexible polymers.
Polymer depletion-induced instability of silica suspensions in dilute toluene solutions of flexible polystyrene (PS) or semiflexible poly(hexyl isocyanate) (PHIC) was investigated by direct observation and oscillatory moduli measurements as functions of silica volume fraction and polymer molecular weight. Addition of the respective polymers to the gelled silica suspensions induces a gel settling. Below the silica volume fraction phi=4 vol%, PS chains compress the volume of the sediment silica phase, whereas PHIC chains expand it and play a role in swelling agents. Thus, PHIC chains lead to the formation of aggregates in the silica suspensions that are larger and less compact than those formed by the PS chains. On the other hand, above phi=4 vol% where the silica suspension occurs gelation, the effect of nonadsorbing polymers on changes in the volume of the silica phase is opposite. Moreover, polymer depletion interaction results in a mechanically stronger gelled phase, leading to the storage modulus G' values larger than those without polymer, but the effects of polymer concentration and polymer molecular weight on the G' values are not clear.
Yamazaki
Sayaka
S
Department of Chemistry for Materials, Faculty of Engineering, Mie University, 1515 Kamihama, Tsu-shi, Mie, 514-8507, Japan.
Kawaguchi
Masami
M
Kato
Tadaya
T