EC STM investigations of corrosion due to chloride solutions on thin CrN coatings.
The focus of the investigations presented is to evaluate local alterations caused by chloride ions affecting thin, magnetron-sputtered CrN layers. Scanning-probe microscopy and analysis techniques are used for this estimation. Thin CrN layers were deposited by reactive magnetron sputtering. They were investigated in electrochemical scanning tunnelling microscopy (EC STM) by cyclic voltammetry in 1 mol L(-1) NaCl. Simultaneously, the surface topography changes were recorded with STM. Above 100 mV the anodic oxidation leads to formation of chromium(III) hydroxide and at sample potentials above 350 mV oxidation of Cr(OH)(2) and Cr(OH)(3) towards chromium(VI) as a soluble chromate starts. Transpassive dissolution of the coating takes place above 900 mV. Yellow colour of the electrolyte is a visible sign for the formation of chromium(VI). Changes of the surface topography indicate the formation of surface layers at anodic potentials. At cathodic potentials increase in current is measured due to the reduction of chromium(III) hydroxide to divalent chromium and metallic chromium. Roughness of surface topography increases.Follow-up explorations with scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), atomic-force microscopy (AFM), scanning tunnelling microscopy/scanning tunnelling spectroscopy (STM/STS) and X-ray photoelectron spectroscopy (XPS) not only evidence the formation of various chromium oxides, but also indicate the existence of chromium hydroxide.
Zahn
Wieland
W
Westsächsische Hochschule Zwickau, Fachbereich Physikalische Technik/Informatik, Dr-Friedrichs-Ring 2A, 08056, Zwickau, Germany. wieland.zahn@fh-zwickau.de
Zösch
Antje
A
Schnabel
Hans Dieter
HD