Tissue reactions adjacent to well-fixed hydroxyapatite-coated acetabular cups. Histopathology of ten specimens retrieved at reoperation after 0.3 to 5.8 years.
Ten acetabular cups coated with hydroxyapatite (HA) had originally been inserted in five primary and five revision total hip replacements. The thickness of the HA was 155 +/- 35 microm. The cups, which were well-fixed, were retrieved, with their adherent tissue, at reoperation after 0.3 to 5.8 years because of infection (five hips), wear of polyethylene (three hips), and instability (two hips). Undecalcified sections showed a direct contact between bone and osteoid-like tissue which had formed directly onto the HA coating. The area within the threads and their mirror images, as well as the implant-tissue interfaces consisted of similar amounts of bone and soft tissue. Degradation of HA was seen in all hips. The mean thickness of the remaining HA coating was 97 microm (95% CI 94 to 101). The metal interface comprised 66% HA. The HA-tissue interface contained more bone than soft tissue (p = 0.001), whereas the metal-tissue interface included more soft tissue than bone (p = 0.019). Soft tissue at the implant interface and poor replacement of HA by bone may interfere with long-term fixation.
Orthopaedic Department, National Hospital, Oslo, Norway.
M
M
Røkkum
A
A
Reigstad
C B
CB
Johansson
T
T
Albrektsson
D000077:Acetabulum; D000328:Adult; D000368:Aged; D019644:Arthroplasty, Replacement, Hip / Q000295:instrumentation*; D001847:Bone Diseases / Q000473:pathology; D020099:Coated Materials, Biocompatible / Q000009:adverse effects*; D003240:Connective Tissue Diseases / Q000473:pathology*; D005260:Female; D005549:Foreign-Body Reaction / Q000209:etiology / Q000473:pathology*; D006621:Hip Joint; D006801:Humans; D006882:Hydroxyapatites / Q000009:adverse effects*; D007592:Joint Diseases / Q000473:pathology* / Q000601:surgery; D008297:Male; D008875:Middle Aged; D011475:Prosthesis Failure; D012086:Reoperation
D020099:Coated Materials, Biocompatible; D006882:Hydroxyapatites