Effect of bifunctional comonomers on mechanical strength and water sorption of amorphous calcium phosphate- and silanized glass-filled Bis-GMA-based composites.
This study seeks to elucidate structure-property relationships in a series of unfilled dental copolymers and their composites. The copolymers/composites were derived from photo-activated binary monomer systems based on 2,2-bis[p-2'-hydroxy-3'-methacryloxypropoxy)phenyl] propane (Bis-GMA) and equimolar amounts of a bifunctional, surface-active comonomer, i.e., 2-hydroxyethyl methacrylate (HEMA), glycerol dimethacrylate (GDMA) or ethylene glycol methacrylate phosphate (PHEMA). Triethyleneglycol dimethacrylate, a widely used comonomer for Bis-GMA, was used as a control. Two types of fillers were investigated: (1) a hydrophilic, silica-modified amorphous calcium phosphate (Si-ACP) and (2) a more hydrophobic, silanized nanosized silica (n-SiO(2)). Both the unfilled copolymers and their composites were evaluated for biaxial flexure strength (BFS), both dry and wet after 30 days immersion in buffered saline, and for water sorption (WS) and their WS kinetic profiles. The Bis-GMA copolymers and composites derived from HEMA and GDMA had BFS and WS values, as well as WS kinetic profiles, similar to the controls. Copolymers and composites based on Bis-GMA/PHEMA had lower BFS and higher WS values. Si-ACP composites had significantly lower BFS values (that were further diminished on soaking) than their copolymers. WS increased as the level of this filler was increased except for Bis-GMA/PHEMA composites. With n-SiO(2) as the filler, a more moderate reduction in BFS occurred compared to the unfilled copolymers. By contrast to Si-ACP composites, the WS of all the n-SiO(2) composites decreased with increasing filler level. From this study it is evident that both the chemical structure of the polymer matrix and the type of filler system can have significant effects on the strength and water-related properties of dental composites.
American Dental Association Health Foundation, Paffenbarger Research Center, National Institute of Standards and Technology, 100 Bureau Drive Stop 8546, Gaithersburg, MD 20899-8546, USA. drago.skrtic@nist.gov
Drago
D
Skrtic
Joseph M
JM
Antonucci
D000042:Absorption; D017438:Bisphenol A-Glycidyl Methacrylate / Q000138:chemical synthesis / Q000737:chemistry* / Q000528:radiation effects; D002130:Calcium Phosphates / Q000138:chemical synthesis / Q000737:chemistry* / Q000528:radiation effects; D003188:Composite Resins / Q000138:chemical synthesis / Q000737:chemistry / Q000528:radiation effects; D019245:Compressive Strength; D003764:Dental Materials / Q000138:chemical synthesis / Q000737:chemistry*; D003799:Dental Stress Analysis; D008027:Light; D008422:Materials Testing; D008689:Methacrylates / Q000138:chemical synthesis / Q000737:chemistry / Q000528:radiation effects; D012821:Silanes / Q000737:chemistry* / Q000528:radiation effects; D012965:Sodium Chloride / Q000737:chemistry; D013329:Structure-Activity Relationship; D013718:Tensile Strength; D014867:Water / Q000737:chemistry*
D002130:Calcium Phosphates; D003188:Composite Resins; D003764:Dental Materials; D008689:Methacrylates; D012821:Silanes; C485828:alpha-tricalcium phosphate; C519480:amorphous calcium phosphate; C485830:tetracalcium phosphate; D014867:Water; D012965:Sodium Chloride; D017438:Bisphenol A-Glycidyl Methacrylate; C485838:calcium phosphate, monobasic, anhydrous; C020243:calcium phosphate; C485829:calcium phosphate, dibasic, anhydrous