[A study of bone-like apatite formation on calcium phosphate ceramics in different kinds of animals in vivo].
Bone-like apatite formation on the surface of calcium phosphate ceramics has been believed to be necessary for new bone to grow on the ceramics and to be related to the osteoinductivity of the material. The research of bone-like apatite formation is a great help to understanding the mechanism of osteoinduction. Synthetic porous calcium phosphate ceramics (HA/TCP = 70/30) were implanted intramuscularly in pigs, dogs, rabbits and rats to make a comparative study of the bone-like apatite formation onto the porous HA/TCP ceramics in different animals. Specimens were harvested at 14 days after implantation. Samples were detected for the surface morphology with SEM. The chemical composition of the sample surface after implantation was analyzed with reflection infrared (R-IR). Obvious bone-like apatite formation could be detected in the sections of porous specimens harvested from all animals after 14 days intramuscular implantation. Crystal deposition could be only observed on the surface of the concave regions of the samples collected from dogs, rabbits and rat. On the contrary, evenly distributed flake-shaped crystal could be found on the pore surface and also on the outer surface of the materials implanted in pigs. The morphology of bone-like apatite in pigs was different from that in the others animals. Bone-like apatite was not observed in dense specimen implanted intramuscularly. Bone-like apatite formed faster on specimens implanted in rabbit than that in other animals. This formation sequence is different from the sequence of osteoinductivity of biphasic calcium phosphate ceramics implanted in these animals. The results demonstrated that the formation of bone-like apatite on materials is a prerequisite condition to their osteoinduction but other factors also play important roles in osteoinduction.
Duan
Yourong
Y
Engineering Research Center in Biomaterials, Sichuan University, Chengdu 610064.
Wu
Yao
Y
Wang
Chaoyuan
C
Chen
Jiyong
J
Zhang
Xingdong
X
D000818:Animals; D001031:Apatites / Q000138:chemical synthesis*; D001826:Body Fluids / Q000737:chemistry; D018786:Bone Substitutes / Q000138:chemical synthesis* / Q000737:chemistry; D002130:Calcium Phosphates / Q000737:chemistry*; D002516:Ceramics / Q000737:chemistry*; D004285:Dogs; D008297:Male; D008422:Materials Testing; D019736:Prostheses and Implants; D011817:Rabbits; D051381:Rats; D013552:Swine
D001031:Apatites; D018786:Bone Substitutes; D002130:Calcium Phosphates; C485828:alpha-tricalcium phosphate; C485830:tetracalcium phosphate; C485838:calcium phosphate, monobasic, anhydrous; C020243:calcium phosphate; C485829:calcium phosphate, dibasic, anhydrous