Effect of cooled composite inserts in the sealing ability of resin composite restorations placed at intraoral temperatures: an in vitro study.
Polymerization shrinkage causes microleakage of resin composite restorations. New materials and operative techniques should be developed in order to reduce polymerization shrinkage. This research studied the effects of cooled composite inserts and room-temperature composite inserts in the sealing ability of resin composite restorations placed at intraoral temperatures. Forty-eight extracted human molars (providing a total of 155 sections) were kept at intraoral temperatures, and Class V cavities were restored with an ormocer-based resin composite (Admira, Voco). Three restorative techniques were used: conventional bulk insertion (Group I or control group) (n = 53 sections), room-temperature resin composite inserts (Group II) (n = 52) and cooled resin composite inserts (Group III) (n = 50). Microleakage and penetrating microleakage were studied under the microscope. Cooled composite inserts reduce microleakage at the gingival margins with respect to Groups I (p = 0.002) and II (p = 0.014). When small-size cooled composite inserts were used, the sealing ability at the gingival margins of Class V composite restorations was improved with respect to the bulk insertion technique and the room-temperature composite inserts technique.
de la Torre-Moreno
Francisco José
FJ
Universidad de Granada, Granada, Spain. fjtorre@ugr.es
Rosales-Leal
Juan Ignacio
JI
Bravo
Manuel
M
D001831:Body Temperature; D002516:Ceramics / Q000737:chemistry; D016009:Chi-Square Distribution; D003080:Cold Temperature; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003737:Dental Cavity Preparation / Q000145:classification; D003763:Dental Leakage / Q000209:etiology; D018772:Dental Marginal Adaptation; D003793:Dental Restoration, Permanent / Q000145:classification; D006801:Humans; D008422:Materials Testing; D011108:Polymers / Q000737:chemistry; D013499:Surface Properties; D013696:Temperature
D003188:Composite Resins; D011108:Polymers