Mechanical characterization of micro/nanoscale structures for MEMS/NEMS applications using nanoindentation techniques.
Mechanical properties of micro/nanoscale structures are needed to design reliable micro/nanoelectromechanical systems (MEMS/NEMS). Micro/nanomechanical characterization of bulk materials of undoped single-crystal silicon and thin films of undoped polysilicon, SiO(2), SiC, Ni-P, and Au have been carried out. Hardness, elastic modulus and scratch resistance of these materials were measured by nanoindentation and microscratching using a nanoindenter. Fracture toughness was measured by indentation using a Vickers indenter. Bending tests were performed on the nanoscale silicon beams, microscale Ni-P and Au beams using a depth-sensing nanoindenter. It is found that the SiC film exhibits higher hardness, elastic modulus and scratch resistance as compared to other materials. In the bending tests, the nanoscale Si beams failed in a brittle manner with a flat fracture surface. The notched Ni-P beam showed linear deformation behavior followed by abrupt failure. The Au beam showed elastic-plastic deformation behavior. FEM simulation can well predict the stress distribution in the beams studied. The nanoindentation, scratch and bending tests used in this study can be satisfactorily used to evaluate the mechanical properties of micro/nanoscale structures for use in MEMS/NEMS.
Li
Xiaodong
X
Nanotribology Laboratory for Information Storage and MEMS/NEMS, Department of Mechanical Engineering, The Ohio State University, 206 West 18th Avenue, Columbus, OH 43210-1107, USA.
Bhushan
Bharat
B
Takashima
Kazuki
K
Baek
Chang-Wook
CW
Kim
Yong-Kweon
YK