Changes in properties of polyacid-modified composite resins (compomers) following storage in acidic solutions.
The interaction of three polyacid-modified composite resins (compomers) with various acidic storage solutions, and also water, over periods of time up to 6 months has been studied and compared with those of a glass-ionomer and a composite resin. This interaction has been shown to vary in a complex way with length of storage and nature of the acid, and citric acid was found to be the most aggressive storage medium for glass-ionomer cement, and also for the compomers. The pure composite resin, by contrast, was relatively unaffected by all of the acid solutions examined. In all acids, the compomers showed a distinct buffering effect, i.e. they increased the pH towards neutral, as did the glass-ionomer. The extent of this also varied with duration of storage and nature of the acid. The biaxial flexure strength was determined and found to be essentially unaffected by the complex chemical interactions with acidic storage solutions. Values obtained for the compomers were lower than those of the composite resin, but above those of the glass-ionomer. Fourier-transform infrared (FT-IR) spectroscopy was employed to study the changes in the compomers following storage in the aqueous media, but bands were broad and no detailed assignments could be made. There were changes in the region of the spectra associated with metal carboxylates however, and this indicates that the secondary acid-base reaction had occurred following water uptake.
Nicholson
J W
JW
School of Chemical and Life Sciences, University of Greenwich, Kent, UK. J.W.Nicholson@gre.ac.uk
Gjorgievska
E
E
Bajraktarova
B
B
McKenzie
M A
MA
D000143:Acids / Q000737:chemistry; D000704:Analysis of Variance; D020770:Compomers / Q000737:chemistry*; D003188:Composite Resins / Q000737:chemistry; D004356:Drug Storage; D005899:Glass Ionomer Cements / Q000737:chemistry; D006801:Humans; D008422:Materials Testing
D000143:Acids; D020770:Compomers; D003188:Composite Resins; D005899:Glass Ionomer Cements