Effect of water and saliva contamination on shear bond strength of brackets bonded with conventional, hydrophilic, and self-etching primers.
This study assessed the effect of water and saliva contamination on the shear bond strength and bond failure site of 3 different orthodontic primers (Transbond XT, Transbond Moisture Insensitive Primer, and Transbond Plus Self Etching Primer; 3M Unitek, Monrovia, Calif) used with a light-cured composite resin (Transbond XT). Bovine permanent mandibular incisors (315) were randomly divided into 21 groups (15 in each group). Each primer-adhesive combination was tested under 7 different enamel surface conditions: (1) dry, (2) water application before priming, (3) water application after priming, (4) water application before and after priming, (5) saliva application before priming, (6) saliva application after priming, and (7) saliva application before and after priming. Stainless steel brackets were bonded in each test group with composite resin. After bonding, all samples were stored in distilled water at room temperature for 24 hours and then tested for shear bond strength. Noncontaminated enamel surfaces had the highest bond strengths for conventional, hydrophilic, and self-etching primers, which produced the same strength values. In most contaminated conditions, the self-etching primer had higher strength values than either the hydrophilic or conventional primers. The self-etching primer was the least influenced by water and saliva contamination, except when moistening occurred after the recommended 3-second air burst. No significant differences in debond locations were found among the groups bonded with the self-etching primer under the various enamel conditions.
Cacciafesta
Vittorio
V
Department of Orthodontics, University of Pavia, Italy. vcacciafesta@hotmail.com
Sfondrini
Maria Francesca
MF
De Angelis
Marco
M
Scribante
Andrea
A
Klersy
Catherine
C
D000134:Acid Etching, Dental; D000269:Adhesives / Q000737:chemistry; D000818:Animals; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D002417:Cattle; D016009:Chi-Square Distribution; D003188:Composite Resins / Q000737:chemistry; D003722:Dental Alloys / Q000737:chemistry; D001840:Dental Bonding; D003743:Dental Enamel / Q000648:ultrastructure; D000431:Ethanol; D008422:Materials Testing; D008689:Methacrylates; D016910:Orthodontic Brackets; D011897:Random Allocation; D019279:Resin Cements / Q000737:chemistry*; D012463:Saliva / Q000737:chemistry*; D013193:Stainless Steel / Q000737:chemistry; D018709:Statistics, Nonparametric; D013314:Stress, Mechanical; D013499:Surface Properties; D014867:Water / Q000737:chemistry*; D017155:Wettability
D000269:Adhesives; D003188:Composite Resins; D003722:Dental Alloys; D008689:Methacrylates; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer; C458821:Transbond moisture-insensitive primer; D014867:Water; D013193:Stainless Steel; C065742:Transbond; D000431:Ethanol; D017438:Bisphenol A-Glycidyl Methacrylate