In vitro surface corrosion of stainless steel and NiTi orthodontic appliances.
Simulated fixed orthodontic appliances were constructed, immersed and incubated in artificial saliva for periods up to three months. Two types of stainless steel archwires and two types of NiTi wires were used. The surface corrosion of the archwires was determined macroscopically, with scanning electron microscopy, and with spectrophotometry. The deposits on the wires were identified with X-ray diffraction. Uniform corrosion was observed on stainless steel wires, and a slight colour change was detected on the NiTi wires beneath stainless steel ligatures. The corrosion product on the stainless steel wires increased with immersion time, and the surface oxide films were easily detached from the underlying matrix. Crevice corrosion was observed under deposits of oxide, and at the interface between bracket and band. Such corrosion may weaken a wire or weld leading to fracture. In contrast, the NiTi archwires did not corrode, and there was no significant difference in surface morphology. The stainless steel archwires showed a significant loss of reflectance after heat treatment and immersion in artificial saliva. The NiTi archwires had the same reflectance before and after the immersion test. NiTi archwires are significantly more stable and resistant to corrosion than stainless steel archwires.
Shin
Ji-Soo
JS
Shin Ji-Soo Dental Clinic, Seoul, Korea.
Oh
Keun-Taek
KT
Hwang
Chung-Ju
CJ
D003116:Color; D003343:Corrosion; D003722:Dental Alloys / Q000737:chemistry*; D004868:Equipment Failure; D006358:Hot Temperature; D006801:Humans; D007101:Immersion; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D009532:Nickel / Q000737:chemistry*; D016910:Orthodontic Brackets; D009969:Orthodontic Wires; D010087:Oxides / Q000737:chemistry; D012464:Saliva, Artificial / Q000737:chemistry; D013053:Spectrophotometry; D013193:Stainless Steel / Q000737:chemistry*; D013499:Surface Properties; D013997:Time Factors; D014025:Titanium / Q000737:chemistry*; D014961:X-Ray Diffraction
D003722:Dental Alloys; D010087:Oxides; D012464:Saliva, Artificial; C040654:titanium nickelide; D013193:Stainless Steel; D009532:Nickel; D014025:Titanium