The effects of microgravity on nanoparticle size distributions generated by the ultrasonic reduction of an aqueous gold-chloride solution.
A solution of gold chloride was reduced using ultrasound irradiation to prepare metallic gold nanoparticles under conditions of microgravity and normal gravity at sea level. Particle size distributions were measured using TEM analysis. A mean particle diameter of 10 nm was obtained in microgravity while a mean diameter of 80 nm was obtained in the laboratory. Absorbance measurements on the reacted solution found an enhanced reduction rate in the reduction of gold chloride in microgravity compared to that in the laboratory.