[An investigation of HAP/organic polymer composite coating prepared by electrochemical co-deposition technique (II) characterization of XRD, SEM and mechanic properties].
Electrodeposition hydroxyapatite(HAP) coatings of ceramics were studied by Nano Indent. The bonding force between the coating and metal substrate was distinctly increased. The experiments about XPS and SIMS showed that there is the act of organic polymer enriching at negative. It ensues that minor organic polymer is compounded to HAP coatings at molecular level and forms that HAP/Organic polymer compound coating.
Hu
Haobing
H
State Key Laboratory for Physical Chemistry of Solid Surfaces, Department of Chemistry, Department of Materials Science and Engineering, Xiamen University, Xiamen 361005.
Lin
Changjian
C
Leng
Yang
Y
D020099:Coated Materials, Biocompatible / Q000138:chemical synthesis / Q000737:chemistry*; D017886:Durapatite / Q000138:chemical synthesis / Q000737:chemistry*; D004563:Electrochemistry; D008422:Materials Testing; D019563:Mechanics; D008855:Microscopy, Electron, Scanning; D013499:Surface Properties; D014961:X-Ray Diffraction
D020099:Coated Materials, Biocompatible; D017886:Durapatite