title: Clinical evaluation of fiber-reinforced composite inlay FPDs.
abstract: OBJECTIVE
  This clinical study evaluated the behavior of inlay fixed partial dentures (IFPD) with conventional and modified framework designs over a period of 12 to 48 months.
  
  
  METHODS
  Forty-one glass fiber-reinforced composite IFPDs were made to replace one missing maxillary or mandibular tooth. The frameworks were made only with parallel fibers in 19 restorations (group 1) and built with parallel and woven fibers modifying the design of the pontic element in 22 IFPDs (group 2) according to the manufacturer's instructions. All restorations were evaluated by color match, marginal discoloration, secondary caries, surface texture, marginal adaptation, fracture, and postoperative sensitivity.
  
  
  RESULTS
  Three partial adhesive-cohesive veneering composite fractures occurred in the pontic element in group 1 after 3, 4, and 8 months, respectively. One cohesive fracture occurred in an abutment in group 2 after 46 months. Group 1 showed a 16% fracture failure rate; group 2 showed a 5% failure rate. However, no statistical difference was detected between the groups. IFPDs received the highest score at the following rates: color match 71%, marginal discoloration 96%, secondary caries 99%, surface texture 88%, marginal adaptation 98%, fracture 90%, and postoperative sensitivity 100%. Statistical analysis indicated significant deterioration of color match from baseline to last recall.
  
  
  CONCLUSIONS
  There were nonsignificantly fewer fractures of the veneering composite with the modified design of the framework than with the conventional design. Repair of the fractured veneer of IFPDs may lengthen the lifespan of the restorations, but it is advisable only for slight damage.
authors.affiliation: Department of Prosthetic Dentistry, School of Dentistry, University of Bologna, Italy. monacocarl@libero.it
authors.forename: Carlo
authors.initials: C
authors.lastname: Monaco
authors.forename: Marco
authors.initials: M
authors.lastname: Ferrari
authors.forename: Gian Paolo
authors.initials: GP
authors.lastname: Miceli
authors.forename: Roberto
authors.initials: R
authors.lastname: Scotti
mesh_terms: D000293:Adolescent; D000328:Adult; D002484:Cementation; D016009:Chi-Square Distribution; D003188:Composite Resins; D019232:Dental Restoration Failure; D003779:Denture Design; D003780:Denture Repair; D003830:Denture, Partial, Fixed; D005260:Female; D005898:Glass; D005899:Glass Ionomer Cements; D006801:Humans; D007284:Inlays; D008297:Male; D008875:Middle Aged; D016017:Odds Ratio; D019279:Resin Cements; D012823:Silicate Cement; D018709:Statistics, Nonparametric; D016019:Survival Analysis
chemical_list: D003188:Composite Resins; D005899:Glass Ionomer Cements; D019279:Resin Cements; C111282:dental polyglass; C009753:fiberglass; D012823:Silicate Cement; C103502:Variolink