Characterization of the enhancement effect of Na2CO3 on the sulfur capture capacity of limestones.
It has been known for a long time that certain additives (e.g., NaCl, CaCl2, Na2CO3, Fe2O3) can increase the sulfur dioxide capture-capacity of limestones. In a recent study we demonstrated that very small amounts of Na2CO3 can be very beneficial for producing sorbents of very high sorption capacities. This paper explores what contributes to these significant increases. Mercury porosimetry measurements of calcined limestone samples reveal a change in the pore-size from 0.04-0.2 microm in untreated samples to 2-10 microm in samples treated with Na2CO3--a pore-size more favorable for penetration of sulfur into the particles. The change in pore-size facilitates reaction with lime grains throughout the whole particle without rapid plugging of pores, avoiding premature change from a fast chemical reaction to a slow solid-state diffusion controlled process, as seen for untreated samples. Calcination in a thermogravimetric reactor showed that Na2CO3 increased the rate of calcination of CaCO3 to CaO, an effect which was slightly larger at 825 degrees C than at 900 degrees C. Peak broadening analysis of powder X-ray diffraction data of the raw, calcined, and sulfated samples revealed an unaffected calcite size (approximately 125-170 nm) but a significant increase in the crystallite size for lime (approximately 60-90 nm to approximately 250-300 nm) and less for anhydrite (approximately 125-150 nm to approximately 225-250 nm). The increase in the crystallite and pore-size of the treated limestones is attributed to an increase in ionic mobility in the crystal lattice due to formation of vacancies in the crystals when Ca is partly replaced by Na.
Laursen
Karin
K
Pulp and Paper Centre, University of British Columbia, Vancouver, Canada. karin@cheme.kyoto-u.ac.jp
Kern
Arnt A
AA
Grace
John R
JR
Lim
C Jim
CJ
D000327:Adsorption; D000393:Air Pollutants / Q000032:analysis; D000397:Air Pollution / Q000517:prevention & control*; D002119:Calcium Carbonate / Q000737:chemistry; D002254:Carbonates / Q000032:analysis / Q000737:chemistry*; D010316:Particle Size; D016062:Porosity; D013458:Sulfur Dioxide / Q000737:chemistry*
D000393:Air Pollutants; D002254:Carbonates; D013458:Sulfur Dioxide; C005686:sodium carbonate; D002119:Calcium Carbonate