Comparison of cross-linked polyethylene materials for orthopaedic applications.
Cross-linked polyethylenes are being marketed by orthopaedic manufacturers to address the problem of osteolysis caused by polyethylene particulate wear debris. Wear testing of these cross-linked polyethylenes in hip simulators has shown dramatic reduction in wear rate compared with standard ultrahigh molecular weight polyethylene, either gamma irradiated in air or nitrogen - or ethylene oxide-sterilized. However, this reduction in wear rate is not without cost. The cross-linking processes can result in materials with lower mechanical properties than standard ultrahigh molecular weight polyethylene. To evaluate the effect of the various cross-linking processes on physical and mechanical properties of ultrahigh molecular weight polyethylene, commercially available cross-linked polyethylenes from six orthopaedic manufacturers were tested. This study was the culmination of collaboration with these manufacturers, who provided cross-linked polyethylene for this study, wear characteristics of the material they provided, and review of the physical and mechanical properties measure for their polyethylene. Cross-linked materials were evaluated as received and after an accelerated aging protocol. Free radical identity and concentration, oxidation, crystallinity, melt temperature, ultimate tensile strength, elongation at break, tensile stress at yield, and toughness are reported for each material. By comparing these physical and mechanical properties, surgeons can evaluate the trade-off that results from developing materials with substantially lower wear rates.
Collier
John P
JP
Thayer School of Engineering, Dartmouth College, Hanover, NH 03755, USA.
Currier
Barbara H
BH
Kennedy
Francis E
FE
Currier
John H
JH
Timmins
Graham S
GS
Jackson
Simon K
SK
Brewer
Robin L
RL
D009682:Magnetic Resonance Spectroscopy; D008422:Materials Testing; D019637:Orthopedic Procedures; D010084:Oxidation-Reduction; D011095:Polyethylenes; D013718:Tensile Strength
D011095:Polyethylenes