Phase stability after aging and its influence on pin-on-disk wear properties of Ce-TZP/Al2O3 nanocomposite and conventional Y-TZP.
Recently zirconia/alumina composites have been examined by many researchers as the new generation of bearing materials in total joint replacements. In this study, the phase stability of a Ce-TZP/Al(2)O(3) nanocomposite and conventional Y-TZP after aging, and its influence on wear resistance, were investigated. Very slight phase transformation was observed in both types of ceramics 18 months after the implantation of Ce-TZP/Al(2)O(3) or Y-TZP samples into rabbit tibiae. However, Y-TZP showed marked phase transformation (approximately 80%) after aging in an autoclave (121 degrees C) for 190 h or in physiological saline at 62 degrees C for 18 months, whereas the new composite remained almost resistant to degradation. According to the results of self-pairing pin-on-disk wear tests using ceramic specimens with or without autoclave aging, the wear factor was almost the same between Ce-TZP/Al(2)O(3) samples with and without aging (6.74 +/- 0.36 x 10(-8) and 6.04 +/- 0.95 x 10(-8) mm(3)/Nm, respectively). In contrast, although non-aged Y-TZP had the lowest wear factor (4.88 +/- 0.51 x 10(-8) mm(3)/Nm) of all specimens tested, aged Y-TZP showed 10-fold greater wear than nonaged Y-TZP. The present study suggests that Ce-TZP/Al(2)O(3) nanocomposite has much greater phase stability than Y-TZP, and that its wear properties are not influenced by aging.
D000537:Aluminum Oxide; D001672:Biocompatible Materials; D002563:Cerium; D006358:Hot Temperature; D008855:Microscopy, Electron, Scanning; D011312:Pressure; D013997:Time Factors; D015040:Zirconium
D001672:Biocompatible Materials; C475766:Ce-TZP-Al2O3; D002563:Cerium; D015040:Zirconium; D000537:Aluminum Oxide