Characterization and protein-adsorption behavior of deposited organic thin film onto titanium by plasma polymerization with hexamethyldisiloxane.
Plasma polymerized hexamethyldisiloxane (HMDSO) thin film was deposited onto titanium using a radio-frequency apparatus for the surface modification of titanium. A titanium disk was first polished using colloidal silica at pH=9.8. Plasma-polymerized HMDSO films were firmly attached to the titanium by heating the titanium to a temperature of approximately 250 degrees C. The thickness of the deposited film was 0.07-0.35mum after 10-60min of plasma polymerization. The contact angle with respect to double distilled water significantly increased after HMDSO coating. X-ray photoelectron spectroscopy revealed that the deposited thin film consisted of Si, C, and O atoms. No Ti peaks were observed on the deposited surface. The deposited HMDSO film was stable during 2-weeks immersion in phosphate buffer saline solution. Fourier transform reflection-absorption spectroscopy showed the formation of Si-H, Si-C, C-H, and Cz.dbnd6;O bonds in addition to Si-O-Si bonds. Quartz crystal microbalance-dissipation measurement demonstrated that the deposition of HMDSO thin films on titanium has a benefit for fibronectin adsorption at the early stage. In conclusion, plasma polymerization is a promising technique for the surface modification of titanium. HMDSO-coated titanium has potential application as a dental implant material.
Hayakawa
Tohru
T
Department of Dental Materials, Research Institute of Oral Science, Nihon University School of Dentistry at Matsudo, 2-870-1, Sakaecho-nishi, Matsudo, Chiba 271-8587, Japan. hayakawa@masact.nihon-u.ac.jp
Yoshinari
Masao
M
Nemoto
Kimiya
K
D000327:Adsorption; D020099:Coated Materials, Biocompatible / Q000138:chemical synthesis / Q000737:chemistry*; D003460:Crystallization / Q000379:methods*; D005353:Fibronectins / Q000737:chemistry*; D005740:Gases / Q000737:chemistry; D006358:Hot Temperature; D008422:Materials Testing; D009930:Organic Chemicals / Q000737:chemistry; D011108:Polymers / Q000138:chemical synthesis / Q000737:chemistry; D011485:Protein Binding; D012833:Siloxanes / Q000737:chemistry*; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry*
D020099:Coated Materials, Biocompatible; D005353:Fibronectins; D005740:Gases; D009930:Organic Chemicals; D011108:Polymers; D012833:Siloxanes; D014025:Titanium; C015917:hexamethyldisiloxane