Potential of restorative systems with simplified adhesives: quantitative analysis of wear and marginal adaptation in vitro.
OBJECTIVE
This in vitro study evaluated: (1) marginal adaptation and (2) attritional wear of composite resin materials with simplified bonding systems.


METHODS
36 standardized Class II MOD cavities were prepared in human mandibulary first molars and divided randomly in six equal groups. Restorations were placed with combinations of resin composites and simplified bonding systems: A = Arabesk and Solobond, B = Z 100 and Scotchbond 1, C = Prodigy and OptiBond, D = FHC Merz light and Resulcin Aqua Prime/Monobond as well as E = Sculpt-It and Bond 1. F = Amelogen Universal in combination with the classical 3 part adhesive system Permaquick served as control for marginal adaptation. For wear rates, enamel versus human enamel served as control. All specimens were subjected to long-term thermomechanical stress in a computer-controlled masticator. Human enamel cusps served as antagonists. Marginal adaptation was evaluated by SEM quantitatively before and after stress. Attritional wear in occlusal contact areas was measured on specimens and antagonists with a surface analyzer. Results were tested for statistical significance with ANOVA.


RESULTS
SEM marginal analysis exhibited variations from 45.1 +/- 19.9% (D) to 7.9 +/- 5.4% (E) continuous margin after thermomechanical loading in test groups. All groups achieved statistically significant lower scores (P < 0.05) for marginal adaptation than the control (F: 87.4 +/- 15.5%). Total attritional wear (specimen + antagonist) varied from 153.2 +/- 32.3 microm (D) to 272.3 +/- 132.7 microm (A). Wear of A and F was statistically significantly higher (P < 0.05) than enamel versus enamel (162.2 +/- 111.2 microm).
Göhring
Till Nicolaus
TN
Division of Cariology, Center for Dental and Oral Medicine, University of Zurich, Switzerland. goehring@zzmk.unizh.ch
Schönenberger
Kathrin Anna
KA
Lutz
Felix
F
D000704:Analysis of Variance; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003737:Dental Cavity Preparation / Q000145:classification; D003738:Dental Cements / Q000737:chemistry; D003743:Dental Enamel / Q000648:ultrastructure; D018772:Dental Marginal Adaptation; D019554:Dental Restoration Wear; D003793:Dental Restoration, Permanent / Q000145:classification; D017220:Dentin-Bonding Agents / Q000737:chemistry; D006801:Humans; D008689:Methacrylates / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry*; D012822:Silicon Dioxide; D015040:Zirconium
C425826:Arabesk; C115611:BOND-1 adhesive; D003188:Composite Resins; D003738:Dental Cements; D017220:Dentin-Bonding Agents; C446261:Merz FHC Hybrid Composite; D008689:Methacrylates; C076808:Monobond S; C092987:Optibond; C119199:PermaQuik; C099128:Prodigy; D019279:Resin Cements; C122122:Resulcin aquaPrime; C425825:Solobond M; C083568:Z100 composite resin; C106662:amelogen; D012822:Silicon Dioxide; C041330:Scotchbond; D015040:Zirconium