Gravity spinning of polycaprolactone fibres for applications in tissue engineering.
Poly(epsilon-caprolactone) (PCL) fibres have been produced by wet spinning from solutions in acetone under low shear (gravity flow) conditions. The tensile strength and stiffness of as-spun fibres were highly dependent on the concentration of the spinning solution. Use of a 6% w/v solution resulted in fibres having strength and stiffness of 1.8 MPa and 0.01 GPa, respectively, whereas these values increased to 9.9 MPa and 0.1 GPa when fibres were produced from 20% w/v solutions. Cold drawing to an extension of 500% resulted in further increases in fibre strength (up to 50 MPa) and stiffness (0.3 GPa). The surface morphology of as-spun fibres was modified, to yield a directional grooved pattern by drying in contact with a mandrel having a machined topography characterised by a peak-peak separation of 91 microm and a peak height of 30 microm. Limited in vitro studies of cell behaviour in contact with the fibres were performed using cell culture. The number of attached fibroblasts and myoblasts on as-spun PCL fibres after 5 days in cell culture was lower than on tissue culture plastic by a factor 2 and 1.5, respectively, but higher than on Dacron monofilament by a factor of 4 and 11, respectively. The high fibre compliance and the potential for controlling the fibre surface architecture to promote contact guidance effects together with the maintained proliferation of fibroblasts and myoblasts on as-spun PCL fibres in vitro recommends their use for 3-D scaffold production in soft tissue engineering.
Williamson
Matthew R
MR
Aston Pharmacy School, Aston University, Aston Triangle, Birmingham B4 7ET, UK.
Coombes
Allan G A
AG
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry; D002455:Cell Division; D002460:Cell Line; D002478:Cells, Cultured; D005347:Fibroblasts / Q000378:metabolism; D006112:Gravitation; D008422:Materials Testing; D051379:Mice; D008855:Microscopy, Electron, Scanning; D032446:Myoblasts / Q000378:metabolism; D011091:Polyesters / Q000737:chemistry*; D011108:Polymers / Q000737:chemistry; D041701:Swiss 3T3 Cells; D013696:Temperature; D013718:Tensile Strength; D013997:Time Factors; D023822:Tissue Engineering / Q000379:methods*
D001672:Biocompatible Materials; D011091:Polyesters; D011108:Polymers; C016240:polycaprolactone