Enamel demineralization inhibition by cements at orthodontic band margins.
OBJECTIVE
To examine the demineralization inhibition effects of glass ionomer cement and polyacid-modified resin-based composite cement, in comparison to non-fluoride releasing zinc phosphate cement.


METHODS
Twenty-seven extracted molars were obtained and randomly assigned to three groups. An orthodontic band was sized and cemented using one of three cements. The teeth were painted with an acid-protective varnish, excluding a 1 mm area gingival to the orthodontic band. The teeth were placed in separate closed environments of a non-fluoridated acid challenge to induce demineralization for 5 days. The teeth were then sectioned two times buccolingually and two times mesiodistally. The sections were photographed with polarized light microscopy in an imbition media of water. The body of each lesion was measured with a computerized imaging system. The areas of the lesions, from each cement group, were compared.


RESULTS
An analysis of variance (ANOVA) indicated significance in variance among groups (P < 0.001). Results of a multiple comparison analysis demonstrated significantly less demineralization adjacent to the glass ionomer cement group compared with the polyacid-modified resin cement group and non-fluoride releasing zinc phosphate control group (P < 0.05). There was no significant difference in adjacent demineralization inhibition between the zinc phosphate cement group and polyacid-modified resin cement group (P < 0.05).
VanMiller
Eric James
EJ
Department of Pediatric Dentistry, Dental School, University of Texas Health Science Center at San Antonio, 7703 Floyd Curl Drive, San Antonio, TX 78229, USA.
Donly
Kevin J
KJ
D000704:Analysis of Variance; D002327:Cariostatic Agents / Q000737:chemistry; D020770:Compomers / Q000737:chemistry; D001840:Dental Bonding; D003738:Dental Cements / Q000737:chemistry*; D003743:Dental Enamel / Q000473:pathology*; D005459:Fluorides / Q000737:chemistry; D005899:Glass Ionomer Cements / Q000737:chemistry; D006801:Humans; D007091:Image Processing, Computer-Assisted; D008277:Magnesium Oxide / Q000737:chemistry; D008859:Microscopy, Polarization; D016910:Orthodontic Brackets; D011076:Polycarboxylate Cement / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D013499:Surface Properties; D017001:Tooth Demineralization / Q000517:prevention & control*; D015034:Zinc Oxide / Q000737:chemistry; D015036:Zinc Phosphate Cement / Q000737:chemistry
C104870:Band-Lok; D002327:Cariostatic Agents; D020770:Compomers; D003738:Dental Cements; C061504:Flecks; D005899:Glass Ionomer Cements; D011076:Polycarboxylate Cement; D019279:Resin Cements; D008277:Magnesium Oxide; D015036:Zinc Phosphate Cement; C040235:Ketac-cem; D005459:Fluorides; D015034:Zinc Oxide