Effect of alloy type and surface conditioning on roughness and bond strength of metal brackets.
The effect of 5 different surface conditioning methods on bonding of metal brackets to cast dental alloys was examined. The surface conditioning methods were fine (30-microm) or rough (125-microm) diamond bur, sandblasting (50-microm or 110-microm aluminum oxide [Al2O3]), and silica coating (30-microm silica). Fifty disc-shaped specimens of 5 different alloys (gold-silver, palladium-silver, nickel-chromium, cobalt-chromium, and titanium) were ground with 1200-grit silicone carbide abrasive and polished before being reused for each conditioning method. Polished surfaces were used as negative controls. After measuring surface roughness (RZ), metal brackets were bonded to the conditioned alloys with a self-curing resin composite. Specimens were thermocycled (5000 times, 5 degrees-55 degrees C, 30 seconds), and shear bond tests were performed. Significantly higher (P<.001) surface roughnesses were observed with use of the rough diamond bur (RZ approximately 33 microm), 110-microm Al2O3 (RZ approximately 14 microm), and fine diamond bur (RZ approximately 10 microm), compared with the controls (RZ approximately 1 microm). Silica coating (RZ approximately 4 microm) and 50-microm Al2O3 (RZ approximately 4 microm) demonstrated no significant difference (P>.001) in roughness when compared with the controls. The control group showed no resistance to shear forces (0 MPa). Bond values were greater (19 MPa) when silica coating was used, compared with 50-microm Al2O3 (7 MPa) and 110-microm Al2O3 (8 MPa) for all alloys tested. However, interaction between alloys and conditioning methods exhibited significant differences (P<.0001).
Nergiz
Ibrahim
I
Department of Operative and Preventive Dentistry, Dental School, University of Hamburg, Germany.
Schmage
Petra
P
Herrmann
Wolfram
W
Ozcan
Mutlu
M
D000704:Analysis of Variance; D003722:Dental Alloys / Q000737:chemistry*; D001840:Dental Bonding / Q000379:methods*; D045662:Dental Etching / Q000379:methods*; D003799:Dental Stress Analysis; D008422:Materials Testing; D016910:Orthodontic Brackets; D033081:Shear Strength; D012825:Silicon; D013499:Surface Properties
D003722:Dental Alloys; D012825:Silicon