Intra-oral adhesive systems for ceramic repairs: a comparison.
The aim of this investigation was to compare the bond strength of restorative composite resin to dental ceramic conditioned with primers and adhesives of various commercial repair kits. Three intra-oral ceramic repair systems--Silistor (Heraeus Kulzer), Cimara (Voco), Ceramic Repair (Vivadent)--were used on all-ceramic (IPS Empress 2, Ivoclar-Vivadent) substrate. Shear bond strength of restorative composite resin to substrate was tested after thermocycling and without thermocycling (n = 10). Substrate surfaces of the specimen after loading were examined microscopically (SEM). The highest bond strengths in both water-stored (7.0 +/- 5.7 MPa) and thermocycled conditions (2.5 +/- 1.8 MPa) were obtained with the Vivadent repair system, while the lowest values were observed with the Cimara system (0.6 +/- 1.4 MPa and 0.0 +/- 0.0 MPa, respectively). Shear bond strengths appeared to be significantly affected by thermocycling (ANOVA, P < 0.05). It is concluded that there are significant differences in the bond strengths of resin composites and ceramic substrate. The roughened surface does not necessarily provide a better bond strength; the bond strength of composite decreases with storage in water and after thermocycling. Bond strength values were generally low for all of the tested materials.
Kumbuloglu
Ovul
O
Department of Prosthodontics, School of Dentistry, Ege University, Izmir, Turkey. kumbuloglu@hotmail.com
User
Atilla
A
Toksavul
Suna
S
Vallittu
Pekka K
PK
D000179:Acrylates / Q000737:chemistry; D000704:Analysis of Variance; D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D002516:Ceramics / Q000737:chemistry*; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003738:Dental Cements / Q000737:chemistry*; D003776:Dental Porcelain / Q000737:chemistry; D017269:Dental Prosthesis Repair; D006801:Humans; D018020:Lithium Compounds / Q000737:chemistry; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D020366:Methylmethacrylate / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D011092:Polyethylene Glycols / Q000737:chemistry; D011109:Polymethacrylic Acids / Q000737:chemistry; D011140:Polyurethanes / Q000737:chemistry; D033081:Shear Strength; D012821:Silanes / Q000737:chemistry; D013499:Surface Properties; D014867:Water / Q000737:chemistry
D000179:Acrylates; D003188:Composite Resins; D003738:Dental Cements; C118557:Empress 2; D018020:Lithium Compounds; D008689:Methacrylates; D011109:Polymethacrylic Acids; D011140:Polyurethanes; D012821:Silanes; C076810:Silistor; C121818:Tetric ceram; D014867:Water; D003776:Dental Porcelain; C029824:urethane dimethacrylate luting resin; C020946:triethylene glycol dimethacrylate; D020366:Methylmethacrylate; D011092:Polyethylene Glycols; D017438:Bisphenol A-Glycidyl Methacrylate; C040415:heliobond