Thermal hysteresis in the photoresponsivity of a langmuir film of amphiphilic spiropyran.
We have found a thermal hysteresis in the photoresponsivity of a Langmuir film for the first time. The Langmuir film of an amphiphilic spiropyran, 1',3'-dihydro-3',3'-dimethyl-6-nitro-1'-octadecyl-8-(docosanoyloxymethyl)spiro[2H-1-benzopyran-2,2'-(2H)-indole] (SP) was fabricated at 13 degrees C at 10 mN m-1, followed by heating to a given temperature. UV irradiation of this film caused only the isomerization of SP to the corresponding merocyanine (MC) up to 29 degrees C. Light-induced J-aggregation of MC occurred at 30 degrees C. On the other hand, once the film was heated to 30 degrees C, light-induced J-aggregation was observed down to 27 degrees C. The hysteresis should be related with the phase transitions that occur in the bulk of SP at similar temperatures. No significant morphological change occurred by light-induced J-aggregation in the Langmuir-Blodgett (LB) film of SP by the present method, in contrast to the case of the LB films fabricated under isothermal conditions at 30 degrees C. This feature enabled us to pattern the LB film with J-aggregate of MC by UV irradiation through a photomask of lines with a width of 5 mum each.
Matsumoto
Mutsuyoshi
M
Nanotechnology Research Institute, National Institute of Advanced Industrial Science and Technology, AIST Tsukuba Central 5-2, 1-1-1 Higashi, Tsukuba 305-8565, Japan. mutsuyoshi.matsumoto@aist.go.jp
Nakazawa
Takahiro
T
Mallia
V Ajay
VA
Tamaoki
Nobuyuki
N
Azumi
Reiko
R
Sakai
Hideki
H
Abe
Masahiko
M