title: The effect of long-term storage on the microleakage of composite resin restorations: qualitative and quantitative evaluation.
abstract: The aim of this study was to evaluate the influence of storage periods of 24 hours and 3 months on the microleakage of class II cavities. Two methods of assessing microleakage were also compared. Class II cavities were prepared in sound human molars. MO cavities were restored using ABF experimental (Kuraray Medical Inc.) + Z250 composite resin (3M ESPE), and DO cavities were restored using Single Bond (3M ESPE) + Z250. After different storage periods, specimens were thermocycled, immersed in a dye (0.5% methylene blue solution for 4 h) and longitudinally sectioned. Dye penetration was scored according to a 0-4 scale. The extent of microleakage was measured using the ImageLab 2000 program. A statistically significant correlation was verified between both evaluation methods (r = 0.978, p < 0.001). ANOVA revealed a statistically significant difference between the tested adhesive systems regarding microleakage (p < 0.001), although it was not influenced by the different storage periods.
authors.affiliation: Department of Dental Materials, School of Dentistry, University of São Paulo, Brazil.
authors.forename: Fernanda Tranchesi
authors.initials: FT
authors.lastname: Sadek
authors.forename: Sandra Kiss
authors.initials: SK
authors.lastname: Moura
authors.forename: Rafael Yagüe
authors.initials: RY
authors.lastname: Ballester
authors.forename: Antonio
authors.initials: A
authors.lastname: Muench
authors.forename: Paulo Eduardo Capel
authors.initials: PE
authors.lastname: Cardoso
mesh_terms: D017438:Bisphenol A-Glycidyl Methacrylate / Q000494:pharmacology; D003188:Composite Resins; D003763:Dental Leakage; D003793:Dental Restoration, Permanent; D017220:Dentin-Bonding Agents / Q000494:pharmacology*; D006801:Humans; D008963:Molar; D013048:Specimen Handling; D013997:Time Factors
chemical_list: D003188:Composite Resins; D017220:Dentin-Bonding Agents; C115612:single bond; D017438:Bisphenol A-Glycidyl Methacrylate