The resin-coating technique. Effect of a single-step bonding system on dentin bond strengths.
OBJECTIVE
An experimental single-step bonding system, RZ-II, has been developed as a resin coating material for crown preparation. The purpose of this study was to compare the dentin microtensile bond strengths (MTBSs) of RZ-II in direct and indirect use.


METHODS
Human molar dentin was used. The specimens were divided into three groups of n = 20 each. Group 1: RZ-II was applied to the dentin surface once or twice, and built up with a direct composite. Group 2: The dentin surface was provisionally covered and stored in water for 1 day. The provisional material was removed and an indirect composite was then bonded to the dentin surface. Group 3: RZ-II was applied to the dentin surface once or twice for "resin coating" before the placement and removal of provisional material. An indirect composite was then bonded to the coated dentin. After 1 day, MTBSs were measured at a crosshead speed of 1 mm/min. The data were analyzed using one-way ANOVA and Fisher's PLSD test (p < 0.05). The interface between the indirect composite and resin-coated dentin was also observed using a SEM.


RESULTS
The MTBSs of RZ-II in Groups 1 and 3 were significantly higher than those of Group 2 (p < 0.05). The thickness of the resin-coating layer and the hybrid layer were 5 to 6 microm and less than 1 microm, respectively.


CONCLUSIONS
The single-step bonding system, RZ-II, could be useful as a resin coating material for crown preparation.
Nikaido
Toru
T
Cariology and Operative Dentistry, Department of Restorative Sciences, Graduate School, Tokyo Medical and Dental University, Tokyo, Japan. nikaido.ope@tmd.ac.jp
Nakaoki
Yasuko
Y
Ogata
Miwako
M
Foxton
Richard
R
Tagami
Junji
J
D000268:Adhesiveness; D000704:Analysis of Variance; D003188:Composite Resins / Q000737:chemistry*; D001840:Dental Bonding; D003738:Dental Cements; D003804:Dentin / Q000648:ultrastructure; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D004338:Drug Combinations; D006801:Humans; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D008855:Microscopy, Electron, Scanning; D011145:Polyvinyls / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D013499:Surface Properties; D013718:Tensile Strength; D015034:Zinc Oxide / Q000737:chemistry
D003188:Composite Resins; D003738:Dental Cements; D017220:Dentin-Bonding Agents; D004338:Drug Combinations; D008689:Methacrylates; D011145:Polyvinyls; D019279:Resin Cements; C083618:new metacolor; C020873:Cavit G; D015034:Zinc Oxide