Structural characterization of room-temperature synthesized nano-sized beta-tricalcium phosphate.
A simple route for synthesizing nano-sized beta-tricalcium phosphate (beta-TCP) at room temperature has been developed in methanol solvent. The phase evolution from CaHPO4, intermediate amorphous calcium phosphate (ACP) phases (including ACP1 and ACP2 with different structures) to final beta-TCP with increasing aging time was observed. The formation of beta-TCP phase is favored due to the incorporation of carbonate which can suppress the transformation of ACP1 phase. High-resolution transmission electron microscopy image along [1-100] zone axis of beta-TCP reveals two types of lattice fringes (straight and wavy fringes) in beta-TCP structure due to structural imperfection. Furthermore, the observations of abnormal diffraction intensity and superlattice diffraction in selected-area diffraction patterns further confirm the chemical order-disorder characteristics in beta-TCP structure and can be used to elucidate the resorbability of beta-TCP in either in vivo or in vitro environment due to the imperfection in beta-TCP crystal.
Bow
Jong-Shing
JS
QA12A/FA of United Microelectronics Cooperation, Tainan 744, Taiwan, Republic of China.
Liou
Sz-Chian
SC
Chen
San-Yuan
SY
D001672:Biocompatible Materials / Q000737:chemistry*; D002130:Calcium Phosphates / Q000138:chemical synthesis / Q000737:chemistry*; D003460:Crystallization / Q000379:methods*; D008422:Materials Testing; D008968:Molecular Conformation; D036103:Nanotechnology / Q000379:methods*; D043942:Nanotubes / Q000737:chemistry* / Q000648:ultrastructure*; D010316:Particle Size; D044367:Phase Transition; D013499:Surface Properties; D013696:Temperature
D001672:Biocompatible Materials; D002130:Calcium Phosphates; C519480:amorphous calcium phosphate; C485817:beta-tricalcium phosphate