Hydroxyapatite coating on a titanium metal substrate by a discharging method in modified artificial body fluid.
OBJECTIVE
The aim of this study was to evaluate the formation of a hydroxyapatite coating on titanium plate by discharging in typical and modified artificial body fluids.


METHODS
Japanese Industrial Standard Grade 2 titanium plates were used as specimens. Discharging was performed on the specimens in each solution, and the surface topography of each coating was observed with a scanning electron microscope. The Ca/P atomic ratio and surface characterization of each coating were evaluated by x-ray photoelectron spectroscopy, and crystal phases of each coating were analyzed by Fourier transform infrared spectroscopy and x-ray diffraction.


RESULTS
Tricalcium phosphate formed on the titanium surface in a 1.5 Ca/P solution with high ion concentrations of calcium (2.5 mmol/L) and phosphorous (1.67 mmol/L). Crystalline HA was formed on the titanium surface in a 1.5 Ca/P solution (Hanks' balanced salt solution without organic molecules) with low ion concentrations of calcium (1.26 mmol/L) and phosphorus (0.83 mmol/L).


CONCLUSIONS
A solution containing organic pH buffer was insufficient to form stable coatings on the titanium surface. Coating properties strongly depended on the Ca/P chemical ratio of the applied solution. A Ca/P ratio of 1.5 was appropriate for preparing a calcium phosphate coating on a titanium surface, whereas a Ca/P ratio of 2.5 was excessively high.


CONCLUSIONS
These findings suggest that Hanks' balanced salt solution without organic molecules is the most suitable solution for forming crystalline hydroxyapatite coatings on titanium surfaces by the discharging method.
Takashima
Hidetoshi
H
Department of Oral Biomaterials and Technology, Showa University School of Dentistry, Tokyo, Japan. yookun@dent.showa-u.ac.jp
Shibata
Yo
Y
Kim
Tae-Young
TY
Miyazaki
Takashi
T
D001826:Body Fluids / Q000737:chemistry; D002130:Calcium Phosphates / Q000737:chemistry; D020099:Coated Materials, Biocompatible; D003460:Crystallization; D017886:Durapatite; D004573:Electrolytes / Q000737:chemistry; D004577:Electron Probe Microanalysis; D004595:Electroplating; D006863:Hydrogen-Ion Concentration; D007552:Isotonic Solutions / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D017550:Spectroscopy, Fourier Transform Infrared; D013499:Surface Properties; D014025:Titanium
D002130:Calcium Phosphates; D020099:Coated Materials, Biocompatible; D004573:Electrolytes; C072670:Hanks Balanced Salt Solution; D007552:Isotonic Solutions; C485828:alpha-tricalcium phosphate; C485830:tetracalcium phosphate; C485838:calcium phosphate, monobasic, anhydrous; D017886:Durapatite; C020243:calcium phosphate; D014025:Titanium; C485829:calcium phosphate, dibasic, anhydrous