Phase differentiation via combined EBSD and XEDS.
Electron backscatter diffraction (EBSD) and orientation imaging microscopy have become established techniques for analysing the crystallographic microstructure of single and multiphase materials. In certain instances, however, it can be difficult and/or time intensive to differentiate phases within a material by crystallography alone. Traditionally a list of candidate phases is specified prior to data collection. The crystallographic information extracted from the diffraction patterns is then compared with the crystallographic information from these candidate phases, and a best-fit match is determined. Problems may arise when two phases have similar crystal structures. The phase differentiation process can be improved by collecting chemical information through X-ray energy-dispersive spectroscopy (XEDS) simultaneously with the crystallographic information through EBSD and then using the chemical information to pre-filter the crystallographic phase candidates. This technique improves both the overall speed of the data collection and the accuracy of the final characterization. Examples of this process and the limitations involved will be presented and discussed.
Nowell
M M
MM
EDAX/TSL 392 East 12300 South, Draper, Utah 84020, USA. matt.nowell@ametek.com
Wright
S I
SI
D003300:Copper / Q000032:analysis; D018360:Crystallography, X-Ray; D008854:Microscopy, Electron; D009532:Nickel / Q000032:analysis; D013052:Spectrometry, X-Ray Emission; D013193:Stainless Steel / Q000032:analysis
D013193:Stainless Steel; D003300:Copper; D009532:Nickel