Effect of high intensity vs. soft-start halogen irradiation on light-cured resin-based composites. Part I. Temperature rise and polymerization shrinkage.
OBJECTIVE
To determine polymerization shrinkage kinetics and temperature rise of light-cured resin-based composites after high intensity vs. soft-start quartz tungsten halogen irradiation.


METHODS
Shrinkage kinetics was evaluated using the "deflecting disk technique", modified for simultaneous measurement of temperature within the resin-based composite using a thermocouple. Additional irradiations after 60 and 65 minutes allowed the determination of temperature rises caused by radiation or by reaction heat. Four hybrids (Filtek Z250, Herculite, Solitaire 2, Tetric Ceram), an inhomogeneously filled hybrid (InTen-S) and a microfill (Filtek A110, formerly Silux Plus) were cured using the quartz tungsten halogen units Astralis 10 and Optilux 501 in the high intensity (A10 HiPo: 10 seconds at 1300 mW/cm2; OL Boost: 10 seconds at 1140 mW/cm2) or soft-start modes (A10 Pulse: increase to 700 mW/cm2 within 10 seconds, three periods of 2 seconds at 1300 mW/cm2 alternating with two periods of 2 seconds at 700 mW/cm2; OL Ramp: exponential increase within 10 seconds, followed by 10 seconds at 1140 mW/cm2).


RESULTS
The soft-start protocols produced less contraction, and polymerization shrinkage started later and progressed slower (or: more slowly), compared to high intensity irradiation [correction]. The lowest shrinkage was observed for InTen-S, followed by Filtek Z250 and A110, whereas Solitaire 2, Herculite and Tetric Ceram scored highest for this parameter. Temperature rise was caused more or less equally by radiation and by reaction heat and reached values of up to 28.9 degrees C relative to a baseline of 37 degrees C. For some combinations of curing modes and resin-based composites, less heat was generated by the soft-start protocols and by Optilux 501.
Department of Operative Dentistry and Periodontology, Julius-Maximilians-University of Würzburg, Germany. Norbert.Hofmann@mail.uni-wuerzburg.de
Norbert
N
Hofmann
Tanja
T
Markert
Burkard
B
Hugo
Bernd
B
Klaiber
D000704:Analysis of Variance; D003188:Composite Resins / Q000528:radiation effects*; D003748:Dental Equipment; D018772:Dental Marginal Adaptation; D003799:Dental Stress Analysis; D006219:Halogens; D007700:Kinetics; D008027:Light; D008422:Materials Testing; D011108:Polymers / Q000737:chemistry; D013696:Temperature; D013997:Time Factors
D003188:Composite Resins; D006219:Halogens; D011108:Polymers