Ultimate tensile strength of tooth structures.
OBJECTIVE
This study determined the ultimate tensile strength (UTS) of enamel (E), dentin (D) and dentin-enamel junction (DEJ) using the microtensile technique. It was hypothesized that the UTS of dental structures varies according to location and nature.


METHODS
Intact occlusal enamel surfaces from extracted human third molars were etched with 37% phosphoric acid and bonded with a one-bottle adhesive system. The bonded occlusal surfaces received a resin composite build-up and teeth were serially, vertically sectioned into several 0.7 mm thick slabs. Each slab was then trimmed to a dumbbell-shaped specimen with irrigated diamond burs to reduce the cross-sectional area to approximately 0.5 mm2 at E, D or DEJ. E was tested according to its prismatic orientation (parallel, EP; and transversally, ET) and D as function of depth (superficial, DS; middle, DM and deep, DD). Specimens were tested in tension in an Instron testing machine at 0.5 mm/min. Results were analyzed by one-way ANOVA and Duncan's Multiple Range test.


RESULTS
UTS mean values (N = 20) were, MPa (SD): DEJ, 46.9 (13.7)b; EP, 42.1 (11.9)b; ET, 11.5 (4.7)d; DS, 61.6 (16.2)a; DM, 48.7 (16.6)b and DD, 33.9 (7.9)c. Enamel stressed transversally to its prismatic orientation was significantly weaker (p < 0.05) Dentin depth significantly affected its UTS (p < 0.05) DEJ presented UTS that was similar to EP and DM (p > 0.05)


CONCLUSIONS
The UTS of dental structures varies according to its nature and location.
Giannini
Marcelo
M
Department of Restorative Dentistry, Piracicaba School of Dentistry, University of Campinas, Av. Limeira, 901, Piracicaba, SP, Brazil. giannini@fop.unicamp.br
Soares
Carlos José
CJ
de Carvalho
Ricardo Marins
RM
D000704:Analysis of Variance; D003461:Crystallography; D003743:Dental Enamel / Q000502:physiology*; D003799:Dental Stress Analysis; D003804:Dentin / Q000502:physiology*; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D008963:Molar; D018709:Statistics, Nonparametric; D013718:Tensile Strength; D019237:Tooth Cervix / Q000502:physiology*