Comparative investigation on copper oxides by depth profiling using XPS, RBS and GDOES.
Depth profiling has been performed by using X-ray photoelectron spectrometry (XPS) in combination with Ar-ion sputtering, Rutherford backscattering spectrometry (RBS) and glow discharge optical emission spectrometry (GDOES). The data obtained by XPS have been subjected to factor analysis in order to determine the compositional layering of the copper oxides. This leads to two or three relevant components within the oxide layers consisting of Cu(2)O or CuO dependent on the sample preparation. GDOES measurements show sputtering profiles which are seriously influenced by a varying sputter rate. To ensure the results obtained so far, RBS measurements of the oxide layers have been carried out in order to discover artefacts of the other methods used and to demonstrate the excellent suitability of RBS for quantitative analysis of these layers. Chemical analysis consisting of (1) carrier-gas fusion analysis (CGFA) and (2) selective dissolution of Cu(2)O/CuO allows the determination of the total amount of oxygen and copper, respectively, and can serve as a cornerstone of quantitative analysis.
Bubert
H
H
Institut für Spektrochemie und angewandte Spektroskopie (ISAS), Bunsen-Kirchhoff-Strasse 11, D-44139, Dortmund, Germany.
Grallath
E
E
Quentmeier
A
A
Wielunski
M
M
Borucki
L
L