Effect of thermal and mechanical load cycling on microtensile bond strength of a total-etch adhesive system.
To evaluate the effect of thermal and mechanical cycles on dentin bond strength to cervical margins of Class II restorations, 80 box-type Class II cavities were prepared on the surfaces of bovine incisors. The cavities were restored with Single Bond (3M-ESPE) and Z-250 composite (3M-ESPE) according to manufacturer's instructions. The incisors were divided into four groups: G1-Control, G2- Thermal cycling (2,000 cycles, 5 degrees C-55 degrees C), G3- Mechanical cycling (100,000 cycles; 50N) and G4- Thermal and mechanical cycling (2,000 cycles 5 degrees C-55 degrees C/100,000 cycles; 50N). The restorations were sectioned perpendicular to the cervical bonded interface into 0.7 +/- 0.2 mm-thick slabs. The slabs were further trimmed at the interface to 1.4 +/- 0.2 mm with a fine diamond bur to produce a cross-sectional surface area of 1 mm2. All specimens were then subjected to microtensile bond testing. Means and standard deviations were expressed in MPa. The bond strength data were analyzed by one-way ANOVA and Fisher's PLSD test (p<0.05). Fracture mode analysis was performed using SEM. Bond strengths were significantly lower when thermal and mechanical cycling were performed [G4-2.41 (8.57)] when compared to the other groups [G1-28.15 (14.03); G2-27.60 (10.14); G3-27.59 (8.67)]. No differences were observed among Groups 1, 2 and 3. Interfacial fracture of the control (G1) and thermocycling (G2) groups mainly occurred between the deepest portion of the adhesive resin and the top layer of the demineralized dentin (Interphase). Mixed failure was predominant and increased when mechanical cycling was applied (G3 and G4).
Bedran-de-Castro
A K B
AK
Department of Restorative Dentistry, Piracicaba School of Dentistry/Unicamp-Piracicaba-SP-Brazil. anakarina_bedran@dentistry.unc.edu
Pereira
P N R
PN
Pimenta
L A F
LA
Thompson
J Y
JY
D000134:Acid Etching, Dental; D000704:Analysis of Variance; D000818:Animals; D017438:Bisphenol A-Glycidyl Methacrylate; D002417:Cattle; D016009:Chi-Square Distribution; D003188:Composite Resins; D001840:Dental Bonding; D018772:Dental Marginal Adaptation; D019232:Dental Restoration Failure; D003793:Dental Restoration, Permanent / Q000379:methods*; D003799:Dental Stress Analysis; D017220:Dentin-Bonding Agents; D006358:Hot Temperature; D008422:Materials Testing; D019279:Resin Cements; D013718:Tensile Strength; D019237:Tooth Cervix
D003188:Composite Resins; D017220:Dentin-Bonding Agents; C444701:Filtek Z250; D019279:Resin Cements; C115612:single bond; D017438:Bisphenol A-Glycidyl Methacrylate