Multilayer vesicles and vesicle clusters formed by the fullerene-based surfactant C60(CH3)5K.
The self-assembly behavior of a fullerene-based surfactant, C60(CH3)5K, in water was studied using a combination of static and dynamic light scattering, as well as transmission electron microscopy, and compared to that of the compound C60(C6H5)5K. Both fullerene surfactant systems spontaneously assemble into large vesicles consisting of closed spherical shells formed by bilayers, with critical aggregation concentrations (CAC) lower than 10(-6) g ml(-1). At low concentrations, the aggregate sizes of C60(CH3)5K (radius R approximately 26.8 nm) and C60(C6H5)5K (R approximately 17.0 nm) were found to be substantially different from each other, showing that the change of the substituents surrounding the polar cyclopentadienide head group makes it possible to control the size of the resulting aggregates. Furthermore, the C60(CH3)5K vesicles were found to exist in two qualitatively different types of aggregation with a critical reaggregation concentration (CRC) located at 3.30 x 10(-6) g ml(-1). Above the CRC, larger aggregates were observed (R approximately 37.6 nm), showing a more complex form of supramolecular aggregation, e.g., in terms of multi-bilayer vesicles and/or of clusters of bilayer vesicles.
Burger
Christian
C
Department of Chemistry, State University of New York at Stony Brook, Stony Brook, NY 11794-3400, USA.
Hao
Jingcheng
J
Ying
Qicong
Q
Isobe
Hiroyuki
H
Sawamura
Masaya
M
Nakamura
Eiichi
E
Chu
Benjamin
B