SEM and TEM study of the hierarchical structure of C57BL/6J and C3H/HeJ mice trabecular bone.
Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) were used to study the hierarchical structure of trabecular bone from C57BL/6J (low bone mass) and C3H/HeJ mice (high bone mass). Bone was harvested from two different anatomical locations: femoral metaphysis and L5 vertebra. This investigation focused on three structural scales: the mesostructural (porous network of trabecular struts), the microstructural (collagen fibril arrangements in trabecular packets), and the nanostructural (collagen fibril and apatite crystals) levels. At the mesostructural level, no distinct differences were found in the trabecular structure of femoral metaphysis but thinner trabecular struts were observed in L5 vertebra for C57BL/6J mice strain. At the microstructural level, the collagen fibrils forming the rotated, twisted, and orthogonal plywood arrangements were distinguished as well as atypical arrangements. At the nanostructural level, the shape and size of apatite crystals, and their arrangement with respect to collagen fibrils were studied. In spite of very different bone mass densities, both mice strains had similar structures at the nanostructural and microstructural levels.
Rubin
Matthew A
MA
The G.W.W. School of Mechanical Engineering, Georgia Institute of Technology, Atlanta 30332-0405, USA. mrubin77@yahoo.com
Rubin
Janet
J
Jasiuk
Iwona
I
D000818:Animals; D001031:Apatites / Q000032:analysis; D015519:Bone Density; D001842:Bone and Bones / Q000737:chemistry / Q000648:ultrastructure*; D005260:Female; D005269:Femur / Q000737:chemistry / Q000648:ultrastructure; D024022:Fibrillar Collagens / Q000648:ultrastructure; D051379:Mice; D008809:Mice, Inbred C3H; D008810:Mice, Inbred C57BL; D008855:Microscopy, Electron, Scanning; D046529:Microscopy, Electron, Transmission; D013131:Spine / Q000737:chemistry / Q000648:ultrastructure
D001031:Apatites; D024022:Fibrillar Collagens