Preparation and topotactical oxidation of ScVO3 with bixbyte structure: a low-temperature route to stabilize the new defect fluorite ScVO(3.5) metastable phase.
ScVO3 has been prepared by controlled reduction of a ScVO4 precursor under an H2/N2 flow at 1250 degrees C. The crystal structure of this material has been studied at room temperature by Rietveld refinement of high-resolution neutron powder diffraction (NPD) data. Sc3+ and V3+ are distributed at random over the metal sites of a C-M2O3 bixbyite-type structure, space group Ia3, a = 9.6182(1) Angstroms. The thermal analysis of ScVO3 in an air flow shows two subsequent oxidation processes, with a final reversal to ScVO4 above 600 degrees C. An intermediate phase of composition ScVO(3.5), containing V4+ cations, can be isolated by isothermal annealing at 350 degrees C in air. This metastable phase has been identified by X-ray diffraction (XRD) as a fluorite-type oxide (space group Fm3m, a = 4.947(2) Angstroms), also showing a random distribution of Sc and V cations over the metal positions. The Rietveld refinement of the ScVO(3.5) structure from powder XRD data in a fluorite structural model yields abnormally high thermal factors for the oxygen atoms, suggesting oxygen mobility in this metastable material.
Alonso
José Antonio
JA
Instituto de Ciencia de Materiales, CSIC, Cantoblanco, 28049 Madrid, Spain.
Casais
María Teresa
MT
Martínez-Lope
María Jesús
MJ