A comparative evaluation of the tensile strength of silver soldered joints of stainless steel and cobalt chromium orthodontic wires with band material--an in vitro study.
The present study was conducted to compare and evaluate the tensile strength of silver soldered joints of stainless steel and cobalt-chromium orthodontic wires with band material. An attempt was made to observe the effect of joint site preparation by incorporation of tack welding and increasing metal to metal surface contact area by flattening an end of the wire prior to soldering along with the regularly used round wires without tack welding. A total of 180 wire specimens were soldered to 180 band specimens. Fifteen samples according to joint site preparation were included for each of the wire groups i.e. Gloria (S.S.), Remanium (S.S.) and Remaloy (Co-Cr) wires of 0.036" in diameter. The findings of the study were suggestive that all three wires may be used for preparing silver soldered joints irrespective of the quality of the wire. However, when subjecting the wire to joint site preparation, Gloria (S.S.) wire showed less tensile strength as compared to Remanium and Remaloy.
Dua
R
R
Department of Pedodontics and Preventive Dentistry J. S. S. Dental College and Hospital, S. S. Nagar, Bannimantap, Mysore, Karnataka.
Nandlal
B
B
D000704:Analysis of Variance; D002858:Chromium Alloys; D003722:Dental Alloys; D012994:Dental Soldering; D003799:Dental Stress Analysis; D008422:Materials Testing; D009969:Orthodontic Wires; D012834:Silver; D013193:Stainless Steel; D013718:Tensile Strength; D014896:Welding
D002858:Chromium Alloys; D003722:Dental Alloys; D013193:Stainless Steel; D012834:Silver