A single-crystal neutron diffraction study of RbTiOAsO(4).
A rubidium titanyl arsenate single-crystal has been studied by neutron diffraction (lambda = 1.207 A). The polished sample used was 5 x 3 x 2 mm and was cut from a crystal made by top-seeded solution growth. The crystal showed severe extinction. It was, however, possible to obtain a structural model with well defined oxygen sites and reasonable anisotropic displacement parameters.