Surface modifications of alumina-silica glass fiber.
A commercial glass fiber with Al(2)O(3) (68.4%) and SiO(2) (27.6%) as major components and CaO, TiO(2), Fe(2)O(3), and CuO as minor components was used as substrate in a silica sol-gel coating process. After cleaning, fiber samples were immersed into tetraethoxysilane (TEOS) at room temperature for 1 h, and then individual fiber samples were soaked into a simulated body fluid (SBF) solution,1 and removed after 5, 10, 15, and 20 days. Zeta potential and Energy Dispersive Spectroscopy (EDS) analyses showed that the fiber surfaces were effectively coated with a silica layer, which improved the formation of an HA layer upon immersion into SBF solution for 5 days. The coating became even more continuous after 10-day immersion. Fourier Transform Infrared Spectroscopic (FTIR) analyses confirmed that the coating layer has P--O vibration bands characteristic of hydroxyapatite (HA) near 1060 and 600 cm(-1).
Andrade
A L
AL
Departamento de Química, ICEx, Universidade Federal de Minas Gerais, Av. Antônio Carlos, 6627, CEP 31270-901, Belo Horizonte, Brazil.
Ferreira
J M F
JM
Domingues
R Z
RZ
D000537:Aluminum Oxide / Q000737:chemistry*; D001826:Body Fluids / Q000737:chemistry*; D017886:Durapatite / Q000737:chemistry; D012821:Silanes / Q000737:chemistry*; D012822:Silicon Dioxide / Q000737:chemistry*; D017550:Spectroscopy, Fourier Transform Infrared; D013499:Surface Properties
D012821:Silanes; C040733:tetraethoxysilane; D012822:Silicon Dioxide; D017886:Durapatite; D000537:Aluminum Oxide