Humidity-dependent reversible aggregation of rhodamine 6G dye immobilized within layered niobate K4Nb6O17.
The spectroscopic behavior of rhodamine 6G (R6G) dye intercalated in layered hexaniobate K4Nb6O17 was investigated. R6G cations were intercalated into the niobate through displacement of preintercalated alkylammonium ions. Powder X-ray diffraction and elemental analysis indicated that the dye molecules were densely accommodated in the interlayer spaces of niobate. The spectroscopic behavior of intercalated R6G was characterized by humidity-dependent aggregation at room temperature. The dye molecules were present dominantly as monomers under humid conditions (93% relative humidity (RH)), while they formed dimers under relatively dry conditions (20% RH). The aggregation-deaggregation of dye occurred reversibly depending on the humidity. The reversible aggregation was not accompanied by a large alteration of the interlayer structure of the sample, because only a small amount of water was adsorbed/desorbed with a small change in the basal spacing of the intercalation compound during the humidity change.
Shinozaki
Ryota
R
Laboratory of Environmentally Benign Materials Chemistry, Faculty of Agriculture, Tokyo University of Agriculture and Technology, 3-5-8 Saiwai-cho, Fuchu-shi, Tokyo 183-8509, Japan.
Nakato
Teruyuki
T
D000327:Adsorption; D002412:Cations; D005456:Fluorescent Dyes / Q000737:chemistry*; D006813:Humidity; D036103:Nanotechnology; D009556:Niobium / Q000737:chemistry*; D012235:Rhodamines / Q000737:chemistry*; D013050:Spectrometry, Fluorescence; D013696:Temperature; D014961:X-Ray Diffraction
D002412:Cations; D005456:Fluorescent Dyes; D012235:Rhodamines; C026188:rhodamine 6G; D009556:Niobium