Processing of grain-size functionally gradient bioceramics for implant applications.
This paper reports work on the processing of functionally gradient alumina bioceramics with a continuously decreasing grain size across the thickness, with the view of ultimately utilizing high-quality nano/ultrafine powders only at the surface of an implant to provide superior wear and mechanical properties. A model of disc geometry is used to examine the feasibility of producing this brand of materials. Wet processing/ball milling and sequential slip casting procedures were used to de-agglomerate alumina powders and deposit green layers of varying particle sizes from 50 to 250 nm. Both pressure-less sintering and hot pressing were evaluated as high temperature sintering/consolidation processes. The results indicate that pressure-less sintering may not be suitable. Hot pressing, however, achieved very promising results producing near fully dense product with a grain size that gradually changes across its thickness.
Morsi
K
K
Department of Mechanical Engineering, San Diego State University, San Diego, California 92182, USA. kmorsi@mail.sdsu.edu
Keshavan
H
H
Bal
S
S
D000537:Aluminum Oxide / Q000737:chemistry*; D001672:Biocompatible Materials / Q000737:chemistry; D002516:Ceramics / Q000737:chemistry*; D008854:Microscopy, Electron; D008855:Microscopy, Electron, Scanning; D019736:Prostheses and Implants
D001672:Biocompatible Materials; D000537:Aluminum Oxide