Roughness analysis of the cracked surfaces of a face centered cubic alloy.
Intergranular and transgranular fracture surfaces obtained in a face centered cubic alloy are studied using 3D maps reconstructed by scanning electron microscopy stereo imaging. The roughness exponents measured in the intergranular and transgranular surfaces, respectively, zeta = 0.83 +/- 0.05 and zeta = 0.75 +/- 0.05, are in agreement with the universal roughness value of 3D fractures. However, the slightly smaller value related to the transgranular surface could be a consequence of crystallographic transgranular zones disseminated on the surface whose roughness exponent zeta = 0.65 +/- 0.07 is close to the one usually measured on 2D fractures.