HAp physical investigation--the effect of sintering temperature.
The paper presents the effect of sintering temperature on the physical properties of porous hydroxyapatite (HAp In this study, the HAp was prepared using polymeric sponge techniques with different binder concentrations. The sintering process was carried out in air for temperature ranging from 1200 degrees C to 1600 degrees C. Different physical properties namely density and porosity were observed at different sintering temperatures. The HAp prepared with higher PVP binder showed a slightly decreased in apparent density with increasing sintering temperature, while those HAp prepared with lower PVP showed a slightly increase in apparent density with increasing sintering temperature. The total porosity was found to be approximately constant in the whole sintering temperature range. However, closed porosity decreases with increasing sintering temperature for HAp prepared by lower binder concentration. On the other hand, the HAp prepared by higher binder concentrations showed increasing closed porosity with increasing sintering temperature. Other features such as the influence of sintering temperatures on grain and strut would also be presented in this paper.
Malaysian Institute for Nuclear Technology Research (MINT), Bangi 43000 Kajang, Selangor.
Y M R
YM
Azran
B
B
Idris
M
M
Rusnah
C H
CH
Rohaida
D018786:Bone Substitutes / Q000032:analysis* / Q000138:chemical synthesis; D003720:Densitometry; D004305:Dose-Response Relationship, Drug; D017886:Durapatite / Q000032:analysis* / Q000138:chemical synthesis; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D016062:Porosity; D011205:Povidone / Q000138:chemical synthesis*; D013696:Temperature
D018786:Bone Substitutes; D017886:Durapatite; D011205:Povidone