Macroporous biodegradable natural/synthetic hybrid scaffolds as small intestine submucosa impregnated poly(D,L-lactide-co-glycolide) for tissue-engineered bone.
Poly(D,L-lactide-co-glycolide) (PLGA), a biodegradable synthetic polymer, is widely used in a variety of tissue-engineered applications, including drug-delivery systems. However, the PLGA scaffolds, macroporous and three-dimensional structure, are difficult to cell attachment and in-growth due to surface hydrophobicity. In order to introduce in new bioactive functionality from porcine small intestine submucosa (SIS) as natural source for PLGA, we fabricated SIS-powder-impregnated PLGA (SIS/PLGA) hybrid scaffolds. Fabrication parameters, including ratios of SIS, PLGA and salt, were optimized to produce the desired macroporous foam. The scaffolds had a relatively homogeneous pore structure, good interconnected pores from the surface to core region and showed an average pore size in the range 69.23-105.82 microm and over 90% porosity. The SIS/PLGA scaffolds degraded with a rate depending on the contents of the SIS. After the fabrication of the SIS/PLGA hybrid scaffolds the wettability of the scaffold was greatly enhanced, resulting in uniform cell seeding and distribution. So, it was observed that BMSC attachment to the SIS/PLGA scaffolds increased gradually with increasing SIS contents. Scaffolds of PLGA alone and SIS/PLGA were implanted subcutaneously under dorsal skin of athymic nude mouse to observe the osteoconductivity. It was found from the result that the effects of the SIS/PLGA scaffolds on bone formation are stronger than control PLGA scaffolds. In summary, the SIS/PLGA scaffolds have osteoconductive effects to allow remodeling and replacement by osseous tissue.
Lee
Sang Jin
SJ
Biomaterials Laboratory, Korea Research Institute of Chemical Technology, Yuseong, Daejeon 305-600, South Korea.
Lee
Il Woo
IW
Lee
Young Moo
YM
Lee
Hai Bang
HB
Khang
Gilson
G
D020341:Absorbable Implants; D000042:Absorption; D000818:Animals; D001842:Bone and Bones / Q000737:chemistry*; D006016:Glycolates / Q000737:chemistry*; D007413:Intestinal Mucosa / Q000737:chemistry* / Q000648:ultrastructure; D007421:Intestine, Small / Q000737:chemistry* / Q000648:ultrastructure; D019344:Lactic Acid; D008855:Microscopy, Electron, Scanning; D011100:Polyglycolic Acid; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D016062:Porosity; D013499:Surface Properties; D013552:Swine; D023822:Tissue Engineering; D014867:Water / Q000737:chemistry
D006016:Glycolates; D014867:Water; D000077182:Polylactic Acid-Polyglycolic Acid Copolymer; D011100:Polyglycolic Acid; D019344:Lactic Acid