Fabrication of synthetic apatites by solid-state reactions.
The paper presents a method of producing synthetic Hydroxyapatite (HA) Ca10(PO4)6(OH)2 and other apatites for biological use by solid-state reaction. The solid-state reaction involves mix-grinding dry powders of beta-tricalcium phosphate powder (TCP) and either calcium hydroxide (Ca(OH)2) or calcium carbonate (CaCO3) or combination thereof, from pure commercial chemicals or derived from natural limestone or from seashells, of total calcium/phosphorus molar ratio between 1.5 to 2.0, to particle size of less than 10 microns, and firing the resultant powder to temperature between 600 degrees C - 1250 degrees C in atmosphere or in controlled atmospheric condition. The resultant apatites formed were characterised using XRD, SEM-EDX and FTIR. The presented reaction process was found to be much simpler compared to conventional methods of producing synthetic apatites since it involves only dry mix-grinding of the reactants before firing at high temperatures based on the required levels of purity. It can also produce synthetic apatites with good reproducibility in a shorter time. Thus the presented method has a great industrial value.
AMREC, SIRIM Berhad, Lot 34, Jln. Hi-Tech 2/3, Kulim Hi-Tech Park, 09000 Kulim, Kedah, Malaysia.
F
F
Fazan
K B N
KB
Shahida
D001031:Apatites / Q000032:analysis / Q000138:chemical synthesis*; D001672:Biocompatible Materials / Q000032:analysis / Q000138:chemical synthesis*; D018786:Bone Substitutes / Q000032:analysis / Q000138:chemical synthesis*; D018360:Crystallography, X-Ray; D017886:Durapatite / Q000032:analysis / Q000138:chemical synthesis*; D006801:Humans; D008422:Materials Testing; D017550:Spectroscopy, Fourier Transform Infrared; D014961:X-Ray Diffraction
D001031:Apatites; D001672:Biocompatible Materials; D018786:Bone Substitutes; D017886:Durapatite