Metal ion reduction and resultant deposition on viologen-functionalized LDPE films and viologen-containing microporous membranes.
Photo-induced reduction of gold and platinum metal salt solutions was carried out using viologen graft copolymerized on low-density polyethylene (LDPE) films and viologen-containing poly(vinylidene fluoride) (PVDF-PVBV) microporous membranes. The effects of the UV irradiation time and concentration of the metal salt solutions on the metal ion reduction process and the resultant metal deposition on the polymeric substrates were investigated. The metal-polymer composites were characterized using X-ray photoelectron spectroscopy (XPS), scanning and transmission electron microscopy (SEM and TEM), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), and UV-visible absorption spectroscopy. The amount of metal uptake, the state of the metal, and the size of the metal particles were found to be strongly dependent on the UV irradiation time and the type and concentration of the metal salt solution. The microporous structure and the high viologen content of the PVDF-PVBV membrane constitute an effective matrix for metal ion reduction and preparation of metal nanoparticles.
Wang
W C
WC
Department of Chemical and Biomolecular Engineering, National University of Singapore, Kent Ridge, 119260, Singapore.
Neoh
K G
KG
Kang
E T
ET
Lim
S L
SL
Yuan
D
D
D006046:Gold / Q000737:chemistry*; D008567:Membranes, Artificial; D008970:Molecular Weight; D049329:Nanostructures / Q000737:chemistry; D010084:Oxidation-Reduction; D010777:Photochemistry; D010984:Platinum / Q000737:chemistry*; D020959:Polyethylene / Q000737:chemistry*; D011145:Polyvinyls / Q000737:chemistry*; D016062:Porosity; D013499:Surface Properties; D013997:Time Factors; D014755:Viologens / Q000737:chemistry*; D005465:Fluorocarbon Polymers
D006046:Gold; D008567:Membranes, Artificial; D010984:Platinum; D020959:Polyethylene; D011145:Polyvinyls; D014755:Viologens; C024865:polyvinylidene fluoride; D005465:Fluorocarbon Polymers