Mechanical and thermal properties of hydroxyaptite filled poly (methyl methacrylate) heat processed denture base material.
The aim of this study was to evaluate the effect of powder-to-liquid ratio on the glass transition temperature (Tg) and the tensile properties of denture base material prepared from poly (methyl methacrylate) (PMMA) and hydroxyapatite (HA) previously treated with 3-trimethoxysilylpropyl methacrylate (gamma-MPS). Specimens for mechanical testing were prepared by adding composites powder (PMMA, BPO and HA) to the monomer (MMA and EGDMA) followed by hand mixing as in dental laboratory description usage. The glass transition temperature was studied by using differential scanning calorimetry (DSC). It was observed that the tensile properties and the Tg were affected by the powder-to-liquid ratio. The mechanical characterization of the materials were performed by using single edge notch-tension (SEN-T) specimens; the fracture toughness was slightly higher in formulation which contained HA filler compared to commercial denture base material.
Mohamed
S H
SH
School of Materials & Mineral Resources Engineering, Engineering Campus, Universiti Sains Malaysia.
Arifin
A
A
Mohd Ishak
Z A
ZA
Nizam
A
A
Samsudin
A R
AR
D001696:Biomechanical Phenomena; D002152:Calorimetry, Differential Scanning; D003819:Denture Bases / Q000592:standards; D017886:Durapatite; D006801:Humans; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D019904:Polymethyl Methacrylate; D013718:Tensile Strength
D019904:Polymethyl Methacrylate; D017886:Durapatite