The effect of dialysis environment on the mechanical behaviour of hollow polymeric fibers.
The effect of hemodialysis on the mechanical behavior of a cellulosic Hemophane ME-IOH and one Polysulfone type hollow fibers was investigated. Mechanical tests showed that the deformation of polysulfone type of hollow fibers is entirely different than that of the other dialyser for the samples used and unused in hemodialysis. All the samples exposed to the dialysis showed decreased in ductility. Fracture surface studies proved that there was some alignment on the fracture surface. XRD and DSC experiments revealed structural changes had occurred.
Konduk
B A
BA
Bogazici University, Institute of Biomedical Engineering, Department of Prostheses, Materials and Artificial Organs, 80815 Bebek-Istanbul/Turkey.
Ucisik
A H
AH
D001672:Biocompatible Materials; D001696:Biomechanical Phenomena; D002482:Cellulose / Q000031:analogs & derivatives*; D006801:Humans; D008422:Materials Testing; D008567:Membranes, Artificial; D008855:Microscopy, Electron, Scanning; D011108:Polymers; D006435:Renal Dialysis / Q000295:instrumentation*; D013450:Sulfones; D013499:Surface Properties
D001672:Biocompatible Materials; D008567:Membranes, Artificial; D011108:Polymers; D013450:Sulfones; C054645:Hemophan; C017662:polysulfone P 1700; D002482:Cellulose