Rendering poly(amidoamine) or poly(propylenimine) dendrimers temperature sensitive.
The poly(amidoamine) dendrimers having terminal isobutyramide (IBAM) groups were prepared by the reaction of isobutyric acid and the amine-terminated poly(amidoamine) dendrimers with generations (G) of 2 to 5 by using a condensing agent, 1,3-dicyclohexylcarbodiimide. 1H and 13C NMR revealed that an IBAM group was attached to essentially every chain end of the dendrimers. While the IBAM-terminated G2 dendrimer was soluble in water, the IBAM-terminated G3, G4, and G5 dendrimers exhibited the lower critical solution temperatures (LCSTs) at 75, 61, and 43 degrees C, respectively. Because the density of the terminal IBAM groups in the periphery of the dendrimer progressively increases with increasing dendrimer generation, the interaction of the IBAM groups might take place more efficiently, resulting in a remarkable decrease in the LCST. In addition, attachment of IBAM groups to poly(propylenimine) dendrimers could give the temperature-sensitive property, indicating that this is an efficient method to render dendrimers temperature sensitive.
Department of Applied Materials Science, Graduate School of Engineering, Osaka Prefecture University, 1-1 Gakuen-cho, Sakai, Osaka 599-8531, Japan.
Yasuhiro
Y
Haba
Atsushi
A
Harada
Toru
T
Takagishi
Kenji
K
Kono