Re-cycling of sugar-ash: a raw feed material for rotary kilns.
Large amounts of sugar-ash, a material rich in calcium carbonate, are produced as a by-product in the Greek Sugar Industry. This work explores the possibility of re-cycling sugar-ash for use in the lime industry. A representative sample of sugar-ash from the Plati Imathias sugar plant was studied by PXRD, TG/DTG, calcination experiments at temperatures between 650 and 1150 degrees C and experiments to determine the quality of the quicklime produced at temperatures between 850 and 1150 degrees C following methods described in ASTM C110 standard. The sugar-ash was found to consist of 90 wt% calcium rich minerals (calcite and monohydrocalcite) and 10 wt% amorphous material. Traces of quartz were also detected. The quicklime of highest quality was produced at 950 degrees C. It is concluded that this "useless" material (sugar-ash) can be re-cycled for use in rotary kilns in the lime industry at calcination temperatures up to 950-1000 degrees C.
Kantiranis
Nikolaos
N
Department of Mineralogy-Petrology-Economic Geology, School of Geology, Faculty of Sciences, Aristotle University of Thessaloniki, GR-54124 Thessaloniki, Greece. kantira@geo.auth.gr
D017610:Calcium Compounds; D004736:Energy-Generating Resources; D019649:Food Industry; D017745:Incineration; D007220:Industrial Waste; D010087:Oxides; D013395:Sucrose
D017610:Calcium Compounds; D007220:Industrial Waste; D010087:Oxides; D013395:Sucrose; C016538:lime