title: Red mud addition in the raw meal for the production of Portland cement clinker.
abstract: The aim of the present research work was to investigate the possibility of adding red mud, an alkaline leaching waste, which is obtained from bauxite during the Bayer process for alumina production, in the raw meal for the production of Portland cement clinker. For that reason, two samples of raw meals were prepared: one with ordinary raw materials, as a reference sample ((PC)Ref), and another with 3.5% red mud ((PC)R/M). The effect on the reactivity of the raw mix was evaluated on the basis of the unreacted lime content in samples sintered at 1350, 1400 and 1450 degrees C. Subsequently, the clinkers were produced by sintering the two raw meals at 1450 degrees C. The results of chemical and mineralogical analyses as well as the microscopic examination showed that the use of the red mud did not affect the mineralogical characteristics of the so produced Portland cement clinker. Furthermore, both clinkers were tested by determining the grindability, setting time, compressive strength and expansibility. The hydration products were examined by XRD analysis at 2, 7, 28 and 90 days. The results of the physico-mechanical tests showed that the addition of the red mud did not negatively affect the quality of the produced cement.
authors.affiliation: Department of Mining and Metallurgical Engineering, Laboratory of Metallurgy, National Technical University of Athens, Greece 9, Iroon Polytechniou Street, 15780 Zografou, Athens, Greece. ptsakiri@central.ntua.gr
authors.forename: P E
authors.initials: PE
authors.lastname: Tsakiridis
authors.forename: S
authors.initials: S
authors.lastname: Agatzini-Leonardou
authors.forename: P
authors.initials: P
authors.lastname: Oustadakis
mesh_terms: D000537:Aluminum Oxide / Q000737:chemistry*; D019245:Compressive Strength; D003247:Conservation of Natural Resources; D003252:Construction Materials; D008422:Materials Testing; D012037:Refuse Disposal; D014961:X-Ray Diffraction
chemical_list: D000537:Aluminum Oxide