Evaluation of TEM samples of an Mg-Al alloy prepared using FIB milling at the operating voltages of 10 kV and 40 kV.
Transmission electron microscopy (TEM) samples of an Mg-Al alloy has been prepared using a Ga-focused ion beam (FIB) milling at two different operating voltages of 10 kV and 40 kV to investigate the influence of the FIB energy on the sample quality. The fine structures of the samples have been studied using a high resolution TEM, and the concentration of the implanted Ga was analysed using an energy dispersive X-ray (EDX) analysis. The result of the TEM observation revealed that point defects were introduced to the sample finally milled at 40 kV but not at 10 kV. However, crystal lattice images and electron diffraction patterns were clearly observed on both the samples. The typical influence of the FIB energy was indicated in the elemental analysis. The relative Ga concentration in the thin sample finally milled at 10 kV was 1.0-2.0 at% that is less than half of 4.0-6.0 at% of the Ga concentration in the sample finally milled at 40 kV. A comparison between the experimental results of the Ga concentration measurement with simulation was also discussed.
Kamino
Takeo
T
Hitachi Science Systems, Ltd., Hitachinaka, Ibaraki 312-0057, Japan. kamino-takeo@naka.hitachi-hitec.com
Yaguchi
Toshie
T
Kuroda
Yasushi
Y
Ohnishi
Tsuyoshi
T
Ishitani
Tohru
T
Miyahara
Yuichi
Y
Horita
Zenji
Z
D000497:Alloys; D000535:Aluminum; D005707:Gallic Acid; D008274:Magnesium; D046529:Microscopy, Electron, Transmission; D013048:Specimen Handling / Q000379:methods*
D000497:Alloys; D005707:Gallic Acid; D000535:Aluminum; D008274:Magnesium