Cyclic loading response of bioprosthetic heart valves: effects of fixation stress state on the collagen fiber architecture.
Biologically derived, chemically modified collagenous tissues are being increasingly used to fabricate cardiac valve prostheses and as biomaterials in cardiovascular repair. A stress-free state during chemical modification has been shown to preserve the collagen fiber architecture of the native tissue, potentially preserving native mechanical properties and improving prostheses durability. However, it is not known if the native collagen fiber architecture is stable during long-term in vivo operation. To address this question, we obtained porcine aortic valves chemically treated at (i) 0 mmHg transvalvular pressure (with 40 mmHg aortic pressure) and (ii) 4 mmHg transvalvular pressure, then subjected the valves to 0, 1 x 10(6), 50 x 10(6), and 200 x 10(6) in vitro accelerated wear testing (AWT) cycles. The resulting changes in collagen fiber architecture were quantified using small angle light scattering analysis (SALS). SALS measurements indicated that collagen fibers in the 0 mmHg pressure-fixed leaflets became more aligned between 1 x 10(6) and 50 x 10(6) AWT cycles. In contrast, only minor changes (not statistically significant) in collagen fiber orientation occurred in the 4 mmHg pressure-fixed valvular tissue with cycling. It was also noted that although the 0 mmHg group was fixed without transvalvular pressure, distention of the root induced significant changes in collagen structure of the leaflets. Overall, our observations suggest that the native collagen fiber crimp of the 0 mmHg pressure-fixed leaflets were rapidly lost after only 50 x 10(6) AWT cycles (equivalent to approximately 1.6 patient years) and thus may not be maintained over a sufficient period of time to be clinically beneficial. Further, the collagen structure of the native aortic valve is exquisitely sensitive to dimensional change in the aortic root-independent of the presence of transvalvular pressure. Our findings also suggest that without in vivo remodeling, any collagenous tissue used to fabricate BHV may undergo similar degenerative, irreversible changes in vivo.
Wells
Sarah M
SM
Engineered Tissue Mechanics Laboratory, Department of Bioengineering, McGowan Institute for Regenerative Medicine, University of Pittsburgh, 100 Technology Drive, Room 234, Pittsburgh, PA 15219, USA.
Sellaro
Tiffany
T
Sacks
Michael S
MS
D001021:Aortic Valve / Q000502:physiology* / Q000648:ultrastructure*; D001705:Bioprosthesis; D001794:Blood Pressure / Q000502:physiology; D004548:Elasticity; D019544:Equipment Failure Analysis / Q000379:methods*; D024022:Fibrillar Collagens / Q000502:physiology* / Q000648:ultrastructure*; D006350:Heart Valve Prosthesis; D040542:Mechanotransduction, Cellular / Q000502:physiology; D010507:Periodicity; D010812:Physical Stimulation / Q000379:methods; D011312:Pressure; D011475:Prosthesis Failure; D013314:Stress, Mechanical; D013718:Tensile Strength; D016474:Weight-Bearing / Q000502:physiology
D024022:Fibrillar Collagens