Structure and properties of novel fibers spun from cellulose in NaOH/thiourea aqueous solution.
Cellulose was dissolved rapidly in a NaOH/thiourea aqueous solution (9.5:4.5 in wt.-%) to prepare a transparent cellulose solution, which was employed, for the first time, to spin a new class of regenerated cellulose fibers by wet spinning. The structure and mechanical properties of the resulting cellulose fibers were characterized, and compared with those of commercially available viscose rayon, cuprammonium rayon and Lyocell fibers. The results from wide angle X-ray diffraction and CP/MAS 13C NMR indicated that the novel cellulose fibers have a structure typical for a family II cellulose and possessed relatively high degrees of crystallinity. Scanning electron microscopy (SEM) and optical microscopy images revealed that the cross-section of the fibers is circular, similar to natural silk. The new fibers have higher molecular weights and better mechanical properties than those of viscose rayon. This low-cost technology is simple, different from the polluting viscose process. The dissolution and regeneration of the cellulose in the NaOH/thiourea aqueous solutions were a physical process and a sol-gel transition rather than a chemical reaction, leading to the smoothness and luster of the fibers. This work provides a potential application in the field of functional fiber manufacturing.
Ruan
Dong
D
Department of Chemistry, Wuhan University, Wuhan 430072, China.
Zhang
Lina
L
Zhou
Jinping
J
Jin
Huiming
H
Chen
Hui
H
D002482:Cellulose / Q000737:chemistry*; D003460:Crystallization; D009682:Magnetic Resonance Spectroscopy; D008855:Microscopy, Electron, Scanning; D008970:Molecular Weight; D012972:Sodium Hydroxide / Q000737:chemistry*; D012996:Solutions; D013718:Tensile Strength; D013890:Thiourea / Q000737:chemistry*; D014867:Water / Q000737:chemistry*; D017155:Wettability; D014961:X-Ray Diffraction
D012996:Solutions; D014867:Water; D012972:Sodium Hydroxide; D002482:Cellulose; D013890:Thiourea