Property variations in the prism and the organic sheath within enamel by nanoindentation.
Atomic force microscopy (AFM) combined with nanoindentation technique was used to definitely, site-specifically, test the nanomechanical properties, including nanohardness and elastic modulus, of the isolated domains within single enamel, the prisms and the surrounding sheaths, of mature human maxillary third molars. In this way, it is for the first time that evident differences of nanomechanical properties were revealed between these domains. The nanohardness and elastic modulus of the sheaths were about 73.6% and 52.7% lower than those of the prisms, respectively. Measuring the residual impressions with AFM supported the similar conclusion. The variations of mechanical properties in these domains are considered to be mainly relative to their different component and fibrils arrangement.
Ge
J
J
Biomaterials Laboratory, Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, China.
Cui
F Z
FZ
Wang
X M
XM
Feng
H L
HL
D001696:Biomechanical Phenomena; D003743:Dental Enamel / Q000648:ultrastructure*; D006244:Hardness; D006245:Hardness Tests; D006801:Humans; D018625:Microscopy, Atomic Force / Q000379:methods*; D008964:Molar, Third / Q000648:ultrastructure*; D036103:Nanotechnology; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors; D014070:Tooth / Q000033:anatomy & histology / Q000648:ultrastructure; D014077:Tooth Erosion