Bond strength comparison of 2 self-etching primers over a 3-month storage period.
The purpose of this in vitro study was to evaluate the shear-peel bond strength of 2 self-etching primer systems, Transbond Plus (3M/ Unitek, Monrovia, Calif) and First Step (Reliance Orthodontic Products, Itasca, Ill), with their respective adhesives, and compare them with a control adhesive system (Transbond XT, 3M/ Unitek) over a 3-month period. Two hundred seventy extracted human premolars were obtained and randomly divided into 9 groups of 30 teeth. Metal orthodontic brackets were bonded to the enamel, and each adhesive group was stored for 24 horrs (T1), 30 days (T2), or 3 months (T3) in deionized water at 37 degrees C. All bonded specimens were thermocycled at 10 degrees C and 50 degrees C for 24 hours before debonding. Brackets were debonded by using a shear-peel load on a testing machine at a cross-head speed of 2 mm/min. Bond failure was also evaluated. The shear-peel bond strengths of the 3 bonding systems were clinically acceptable with the possible exception of First Step at 30-day storage. Repeated measures analysis of variance showed a statistically significant (P < .0001) difference in mean bond strengths between the 3 adhesive systems. The shear-peel bond strength of the adhesives over the 3 time intervals showed statistically significant (P = .005) changes. In each group, there were statistically significant differences in shear-peel bond strength between time intervals T1-T2 and T2-T3 for Transbond Plus and T2-T3 for First Step. The change in mean shear-peel bond strength of the 3 adhesives demonstrated a consistent pattern of behavior over the 3 storage intervals. The lowest mean shear-peel bond strength values were noted at the 30-day storage. Bond failure analysis (adhesive remnant index) demonstrated mainly cohesive bond failures.
Trites
Brian
B
Division of Graduate Orthodontics, School of Dentistry, University of Western Ontario, London, Ontario, Canada.
Foley
Timothy F
TF
Banting
David
D
D000134:Acid Etching, Dental / Q000379:methods*; D000269:Adhesives / Q000737:chemistry*; D001840:Dental Bonding; D003743:Dental Enamel / Q000648:ultrastructure; D003764:Dental Materials / Q000737:chemistry*; D003799:Dental Stress Analysis / Q000295:instrumentation; D000431:Ethanol / Q000737:chemistry; D006801:Humans; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D016910:Orthodontic Brackets; D019279:Resin Cements / Q000737:chemistry; D033081:Shear Strength; D013314:Stress, Mechanical; D013499:Surface Properties; D013997:Time Factors
D000269:Adhesives; D003764:Dental Materials; D008689:Methacrylates; D019279:Resin Cements; C429625:Transbond Plus Self-Etching Primer; C477790:Transbond XT; C458821:Transbond moisture-insensitive primer; D000431:Ethanol