Structure and dynamics of polymer-grafted clay suspensions.
The structure and dynamics of polymer-grafted two-dimensional silicate layers in solution were investigated. The geometry of the individual silicate layers was examined by looking at both polarized and depolarized light scattering from dilute solutions, while higher-concentration systems were used to study the interaction and dynamics of polymer-grafted silicate layers in suspension. The form factor for an oblate ellipsoid was used to fit the polarized intensity profile, and values of a approximately 80 nm and b approximately 380 nm for the semi-axes were obtained. The 80 nm value compares reasonably with the dimensions of the polymer brushes grafted on the surface of the silicate layers. The modulus of the grafted silicate in solution, as determined by Brillouin scattering, is of the order of 10 GPa. The cooperative diffusion mechanism, typical of interacting polymer chains, is suppressed due to the high polymer osmotic pressure. The osmotic pressure is also responsible for the weak interpenetration of the densely grafted polymer chains on the surface of the silicate layers. The scattering data indicates that the polymer-grafted nanoparticles move via collective diffusion and experience significant decrease in mobility above their overlap concentration.
Shah
D
D
Department of Chemistry and Chemical Biology, Cornell University, Ithaca, NY, USA.
Fytas
G
G
Vlassopoulos
D
D
Di
J
J
Sogah
D
D
Giannelis
E P
EP