Alginate microcapsules prepared with xyloglucan as a synthetic extracellular matrix for hepatocyte attachment.
In this study, xyloglucan (XG) was used as a new synthetic extracellular matrix (ECM) for primary mouse hepatocyte attachment in Ca-alginate (AL) capsules. The rates of hepatocytes adhesion onto collagen type I-, XG-coated and uncoated polystyrene (PS) surface were 89.1%, 91.1% and 25.5%, respectively, at 4 h after incubation at 37 degrees C. From the inhibition study in a cell adhesion assay, the adhesion rates of freshly isolated hepatocytes and preincubated hepatocytes with 20 mm galactose onto the XG-coated surface were 55.7 and 17.3%, respectively, after 30 min incubation at 37 degrees C. Flow cytometric analysis showed that the internalization of XG by freshly isolated hepatocytes was stronger than preincubated hepatocytes with 20 mm galactose. The concentration of XG in AL/XG capsules to perform the best liver-specific functions was 0.5 mg/ml, where the highest albumin secretion rates were obtained. The albumin secretion, ammonia elimination rates and cell viability of hepatocytes were slowly decreased with culture time in AL/XG capsules, whereas those were rapidly decreased in AL capsules, indication of the more rapid formation of hepatocyte spheroids in AL/XG capsules than in AL capsules. More than 70% of the seeded hepatocytes in AL/XG capsules participated in spheroid formation after 2 days, whereas most hepatocytes in AL capsules remained as single cells and only a few cells began to form aggregates after 3 days. Intercellular molecule genes, such as connexin (Cx) 32 and E-cadherin, of hepatocyte spheroids in AL or AL/XG capsules were detected by reverse transcriptase-polymerase chain reaction. Cx32 and E-cadherin genes in AL/XG capsules were more rapidly reexpressed and expressed, respectively, than in AL ones. The results suggest that the multicellular spheroid formation of hepatocytes can enhance the liver-specific functions in the three-dimensional space in the presence of XG as a new synthetic ECM owing to the specific interaction between the galactose moieties of XG and asialoglycoprotein receptors of hepatocytes.
Seo
Seog-Jin
SJ
School of Agricultural Biotechnology, Seoul National University, Seoul 151-742, South Korea.
Akaike
Toshihiro
T
Choi
Yun-Jaie
YJ
Shirakawa
Mayumi
M
Kang
Inn-Kyu
IK
Cho
Chong-Su
CS
D000464:Alginates / Q000737:chemistry*; D000818:Animals; D040761:Biomimetic Materials / Q000737:chemistry; D002448:Cell Adhesion / Q000502:physiology*; D018929:Cell Culture Techniques / Q000379:methods; D002478:Cells, Cultured; D020099:Coated Materials, Biocompatible / Q000737:chemistry; D005109:Extracellular Matrix / Q000737:chemistry* / Q000502:physiology*; D005936:Glucans / Q000737:chemistry*; D020723:Glucuronic Acid / Q000737:chemistry*; D022781:Hepatocytes / Q000166:cytology* / Q000502:physiology*; D006603:Hexuronic Acids / Q000737:chemistry*; D008099:Liver; D019164:Liver, Artificial; D008297:Male; D008422:Materials Testing; D051379:Mice; D008813:Mice, Inbred ICR; D008863:Microspheres; D018874:Spheroids, Cellular / Q000166:cytology / Q000502:physiology; D023822:Tissue Engineering / Q000379:methods*; D014990:Xylans / Q000737:chemistry*
D000464:Alginates; D020099:Coated Materials, Biocompatible; D005936:Glucans; D006603:Hexuronic Acids; D014990:Xylans; C029353:xyloglucan; D020723:Glucuronic Acid