New amine-templated zinc phosphates with a temperature-induced increase of structural dimensionality.
Three new amine-templated zinc phosphates, [C4N2H14][Zn(HPO4)2].H2O, AU-I, [C4N2H14][Zn2(H(0.5)PO4)2(H2PO4)], AU-II, and [C4N2H14][Zn5(H2O)(PO4)4], AU-III, are prepared by hydrothermal synthesis using an organic amine, N,N'-dimethylethylendiamine CH3NHCH2CH2NHCH3, as structure-directing agent. The three materials are prepared from the same reaction mixture, 1Zn(CH3CO2)2:3.05H3PO4:2.25CH3NHCH2CH2NHCH3:138H2O (pH = 5.1), AU-I at RT, AU-II at 60 degrees C, and AU-III at 170 degrees C. The materials are built from corner-sharing ZnO4 and PO4 tetrahedra forming chains, layers, or framework structures for AU-I to III, respectively, and are linked together by hydrogen bonds via the diprotonated amine ions. The complete hydrogen-bond scheme is resolved for these new compounds and reveals some interesting phenomena, for example, a hydrogen shared between two phosphate groups in AU-II, thereby forming H(0.5)PO4 groups. Furthermore, the water molecules are different; that is, in AU-I they act as hydrogen-bond donor and acceptor, whereas they act as ligand in AU-III with coordination to Zn. The structures of the compounds are determined by single-crystal X-ray diffraction analysis. AU-I, [C4N2H14][Zn(HPO4)2].H2O, crystallizes in the triclinic space group P-1, a = 8.215(2), b = 8.810(3), c = 8.861(3) A, alpha = 88.001(4) degrees , beta = 89.818(5) degrees , and gamma = 89.773(5) degrees , Z = 2. AU-II, [C4N2H14][Zn2(H(0.5)PO4)2(H2PO4)], is monoclinic, P2/n, a = 11.7877(4), b = 5.2093(2), c = 12.2031(4) A, beta = 98.198(1) degrees , Z = 2. AU-III, [C4N2H14][Zn5(H2O)(PO4)4], crystallizes in the orthorhombic space group Pna2(1) with lattice parameters, a = 20.723(2), b = 5.2095(6), c = 17.874(2) A, Z = 4. The phase stability investigated by systematic hydrothermal synthesis is presented, and the materials are further characterized by 31P solid-state MAS NMR, for example, by determination of 31P chemical shift anisotropies for AU-III, while the thermal behavior is investigated by thermogravimetry (TG).
Jensen
Torben R
TR
Interdisciplinary Nanoscience Center (iNANO), University of Aarhus, DK-8000 Arhus C, Denmark. trj@chem.au.dk
Gérentes
Nicolas
N
Jepsen
Josua
J
Hazell
Rita G
RG
Jakobsen
Hans J
HJ