Solid-state NMR studies of collagen-based parchments and gelatin.
Historical collagen-based parchments have been studied by solid-state NMR. In addition, new parchment (produced according to traditional methods) and gelatin from bovine skin were also studied. Wideline 1H and MAS 13C measurements were carried out directly on intact parchments. A simple approach is proposed for evaluation of the extent of parchment degradation based on the linewidth changes in the 13C CPMAS spectra relative to new parchment and gelatin. Structural (bound) water content was estimated from wideline 1H NMR lineshape and relaxation time measurements. It was found that the relative water content in parchments correlates linearly with 13C MAS linewidths. Its decrease on parchment degradation indicates that structural water molecules are of primary importance in stabilizing higher order collagen structures. Backbone and side chain dynamics of collagen in parchments were compared to those of gelatin based on the 13C dipolar-dephased experiments. Carbonyl 13C chemical shift anisotropies were measured to deduce the geometry of the collagen backbone motion. Unlike previous studies, we found that the collagen backbone motion is similar to that found in other proteins and occurs primarily via small-angle librations about internal bond directions.
Aliev
Abil E
AE
Department of Chemistry, University College London, 20 Gordon Street, London WC1H 0AJ United Kingdom. a.e.aliev@ucl.ac.uk
D002247:Carbon Isotopes; D003094:Collagen / Q000737:chemistry*; D005780:Gelatin / Q000737:chemistry*; D009682:Magnetic Resonance Spectroscopy / Q000379:methods*
D002247:Carbon Isotopes; D005780:Gelatin; D003094:Collagen