[Preparation of a novel activated carbon coating fiber for solid phase micro-extraction and its application for halocarbon compound analysis in water].
A novel activated carbon coating fiber used for solid phase micro-extraction (SPME) was prepared using activated carbon powder and silica resin adhesive. The extraction properties of the novel activated carbon coating fiber were investigated. The results indicate that this coating fiber has high concentration ability, with enrichment factors for chloroform, carbon tetrachloride, trichloroethylene and tetrachloroethylene in the range of 13.8 to 18.7. The fiber is stable at temperature as high as 290 degrees C and it can be used for over 140 times at 250 degrees C. The activated carbon coating fiber was then applied to the analysis of the four halocarbon compounds mentioned above. A linear correlation with correlation coefficients between 0.995 2 and 0.999 4 and the detection limits between 0.008 and 0.05 microg/L were observed. The method was also applied to a real water sample analysis and the recoveries of these halocarbon compounds were from 95.5% to 104.6%.
Wang
Shutao
S
School of Municipal and Environmental Engineering, Harbin Institute of Technology, Harbin 150090, China. wychx@public.hr.hl.cn
Wang
Yan
Y
You
Hong
H
Liang
Zhihua
Z
D002251:Carbon Tetrachloride / Q000032:analysis*; D002606:Charcoal; D002725:Chloroform / Q000032:analysis; D002849:Chromatography, Gas / Q000379:methods; D009930:Organic Chemicals / Q000032:analysis*; D011095:Polyethylenes / Q000032:analysis; D014241:Trichloroethylene / Q000032:analysis; D014874:Water Pollutants, Chemical / Q000032:analysis*
D009930:Organic Chemicals; D011095:Polyethylenes; D014874:Water Pollutants, Chemical; D002606:Charcoal; D014241:Trichloroethylene; D002725:Chloroform; C039184:polychlorotrifluoroethylene; D002251:Carbon Tetrachloride