Modulation of the responses of human osteoblast-like cells to physiologic mechanical strains by biomaterial surfaces.
In a previous study we demonstrated that MG-63 cells cultured on Ti-6Al-4V discs covered by alumina ceramic and submitted to intermittent mechanical strain (IMS) presented morphological alteration associated with enhanced differentiation. Here we examine how the mechanical response of osteoblasts can be modulated by the nature of the substrate. MG-63 cells were cultured on four materials: polystyrene and Ti-6Al-4V (average roughness = 0.48 microm) as smooth substrates; Ti-6Al-4V (average roughness = 5.76 microm) and Ti-6Al-4V covered with alumina (average roughness = 5.21 microm) as rough substrates. Mechanical strains were applied for 15 min, three times a day for 1-5 days with a 600 microstrains magnitude and a 0.25 Hz frequency. IMS stimulated alkaline phosphatase activity by 25-35% on all substrates and had no effect on cell growth on either substrate. Fibronectin (FN) was chosen as representative of cell-matrix interaction. FN production was increased by 60% after 1 day of stretching only on alumina-coated discs. FN organization examined on smooth substrates was affected by 5 days of IMS, showing a thickening of the fibres. The same modifications induced by IMS were previously observed on alumina-covered discs. Vinculin expression was not affected by IMS whatever the substrate. Cell-cell interactions were determined by N-cadherin immunoblotting. N-cadherin expression was increased by IMS specifically on rough substrates. Our results suggest that the nature of the surface did not influence the up-regulation of alkaline phosphatase activity induced by IMS, but modulates specifically cell-substrate as well as cell-cell interactions in response to IMS.
Di Palma
Fabrice
F
Laboratoire de Biologie du Tissu Osseux, Faculté de Médecine 15 rue Ambroise Paré, Université Jean Monnet, Equipe INSERM E366, Saint-Etienne 42023, Cedex 02, France.
Guignandon
Alain
A
Chamson
Annette
A
Lafage-Proust
Marie-Hélène
MH
Laroche
Norbert
N
Peyroche
Sylvie
S
Vico
Laurence
L
Rattner
Aline
A
D000497:Alloys; D001672:Biocompatible Materials / Q000737:chemistry; D002454:Cell Differentiation / Q000502:physiology; D002460:Cell Line; D049109:Cell Proliferation; D002470:Cell Survival / Q000502:physiology; D006801:Humans; D008422:Materials Testing; D040542:Mechanotransduction, Cellular / Q000502:physiology*; D016348:Osseointegration / Q000502:physiology; D010006:Osteoblasts / Q000166:cytology* / Q000502:physiology*; D010012:Osteogenesis / Q000502:physiology; D019736:Prostheses and Implants; D013314:Stress, Mechanical; D013499:Surface Properties; D014025:Titanium / Q000737:chemistry*
D000497:Alloys; D001672:Biocompatible Materials; C031462:titanium alloy (TiAl6V4); D014025:Titanium