Adhesion and proliferation of OCT-1 osteoblast-like cells on micro- and nano-scale topography structured poly(L-lactide).
The impact of the surface topography of polylactone-type polymer on cell adhesion was to be concerned because the micro-scale texture of a surface can provide a significant effect on the adhesion behavior of cells on the surface. Especially for the application of tissue engineering scaffold, the pore size could have an influence on cell in-growth and subsequent proliferation. Micro-fabrication technology was used to generate specific topography to investigate the relationship between the cells and surface. In this study the pits-patterned surfaces of polystyrene (PS) film with diameters 2.2 and 0.45 microm were prepared by phase-separation, and the corresponding scale islands-patterned PLLA surface was prepared by a molding technique using the pits-patterned PS as a template. The adhesion and proliferation behavior of OCT-1 osteoblast-like cells morphology on the pits- and islands-patterned surface were characterized by SEM observation, cell attachment efficiency measurement and MTT assay. The results showed that the cell adhesion could be enhanced on PLLA and PS surface with nano-scale and micro-scale roughness compared to the smooth surfaces of the PLLA and PS. The OCT-1 osteoblast-like cells could grow along the surface with two different size islands of PLLA and grow inside the micro-scale pits of the PS. However, the proliferation of cells on the micro- and nano-scale patterned surface has not been enhanced compared with the controlled smooth surface.
Wan
Yuqing
Y
State Key Laboratory of Polymer Physics & Chemistry, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China.
Wang
Yong
Y
Liu
Zhimin
Z
Qu
Xue
X
Han
Buxing
B
Bei
Jianzhong
J
Wang
Shenguo
S
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry*; D002448:Cell Adhesion / Q000502:physiology*; D018929:Cell Culture Techniques / Q000379:methods; D002460:Cell Line; D049109:Cell Proliferation; D048429:Cell Size; D006801:Humans; D008422:Materials Testing; D049329:Nanostructures / Q000737:chemistry* / Q000648:ultrastructure; D010006:Osteoblasts / Q000166:cytology* / Q000502:physiology*; D011091:Polyesters / Q000737:chemistry*; D013499:Surface Properties; D023822:Tissue Engineering / Q000379:methods*
D001672:Biocompatible Materials; D011091:Polyesters; C033616:poly(lactide)