Biological response to pre-mineralized starch based scaffolds for bone tissue engineering.
It is known that calcium-phosphate (Ca-P) coatings are able not only to improve the bone bonding behaviour of polymeric materials, but at the same time play a positive role on enhancing cell adhesion and inducing the differentiation of osteoprogenitor cells. Recently an innovative biomimetic methodology, in which a sodium silicate gel was used as a nucleative agent, was proposed as an alternative to the currently available biomimetic coating methodologies. This methodology is especially adequate for coating biodegradable porous scaffolds. In the present work we evaluated the influence of the referred to treatment on the mechanical properties of 50/50 (wt%) blend of corn starch/ethylene-vinyl alcohol (SEVA-C) based scaffolds. These Ca-P coated scaffolds presented a compressive modulus of 224.6 +/- 20.6 and a compressive strength of 24.2 +/- 2.20. Cytotoxicity evaluation was performed according ISO/EN 10993 part 5 guidelines and showed that the biomimetic treatment did not have any deleterious effect on L929 cells and did not inhibit cell growth. Direct contact assays were done by using a cell line of human osteoblast like cells (SaOS-2). 3 x 10(5) cells were seeded per scaffold and allowed to grow for two weeks at 37( composite function)C in a humidified atmosphere containing 5% CO(2). Total protein quantification and scanning electron microscopy (SEM) observation showed that cells were able to grow in the pre-mineralized scaffolds. Furthermore cell viability assays (MTS test) also show that cells remain viable after two weeks in culture. Finally, protein expression studies showed that after two weeks osteopontin and collagen type I were being expressed by SaOS-2 cells seeded on the pre-mineralized scaffolds. Moreover, alkaline phosphatase (ALP) activity was higher in the supernatants collected from the pre-mineralized samples, when compared to the control samples (non Ca-P coated). This may indicate that a faster mineralization of the ECM produced on the pre-mineralized samples was occurring. Consequently, biomimetic pre-mineralization of starch based scaffolds can be a useful route for applying these materials on bone tissue engineering.
Salgado
A J
AJ
3B's Research Group, Biomaterials, Biodegradables and Biomimetics, University of Minho, Campus de Gualtar, 4710-057 Braga, Portugal. asalgado@dep.uminho.pt
Figueiredo
J E
JE
Coutinho
O P
OP
Reis
R L
RL
D000469:Alkaline Phosphatase / Q000378:metabolism; D000818:Animals; D040761:Biomimetic Materials / Q000737:chemistry; D001826:Body Fluids / Q000502:physiology; D018786:Bone Substitutes; D002130:Calcium Phosphates / Q000737:chemistry*; D002448:Cell Adhesion; D018929:Cell Culture Techniques; D002460:Cell Line; D002470:Cell Survival; D024042:Collagen Type I / Q000378:metabolism; D006801:Humans; D008855:Microscopy, Electron, Scanning; D011145:Polyvinyls / Q000138:chemical synthesis / Q000737:chemistry*; D051381:Rats; D013213:Starch / Q000138:chemical synthesis / Q000737:chemistry*; D013499:Surface Properties; D023822:Tissue Engineering
D018786:Bone Substitutes; D002130:Calcium Phosphates; D024042:Collagen Type I; D011145:Polyvinyls; C439612:corn starch-co-ethylene vinyl alcohol blend; D013213:Starch; D000469:Alkaline Phosphatase
J Biomed Mater Res. 2002 Mar 15;59(4):690-6
11774331
Science. 1993 May 14;260(5110):920-6
8493529
Int J Oral Maxillofac Implants. 1999 Mar-Apr;14(2):239-47
10212541
J Biol Chem. 1998 Dec 4;273(49):32988-94
9830051
J Mater Sci Mater Med. 1999 Dec;10(12):827-35
15347960
Tissue Eng. 2001 Dec;7(6):679-89
11749726
J Orthop Res. 2002 May;20(3):473-82
12038620
J Biomed Mater Res. 2002 Oct;62(1):136-48
12124795
J Biomater Sci Polym Ed. 1998;9(10):1071-87
9806446
Crit Rev Oral Biol Med. 2000;11(3):279-303
11021631
Science. 1997 May 30;276(5317):1425-8
9162012
Biomaterials. 2000 Jun;21(11):1103-14
10817262
J Mater Sci Mater Med. 1997 Dec;8(12):897-905
15348812
Biomaterials. 2001 Oct;22(19):2617-23
11519781
Biomaterials. 2003 Jul;24(15):2575-84
12726711
J Biomed Mater Res. 2002 Apr;60(1):70-8
11835161
Tissue Eng. 2000 Dec;6(6):605-17
11103082
J Mater Sci Mater Med. 2001 Jun;12(6):491-5
15348263
Biomaterials. 2001 Jun;22(12):1467-74
11374445
Biomaterials. 2001 May;22(9):883-9
11311006
J Bone Miner Res. 1998 Feb;13(2):155-67
9495508
Cell. 1979 Apr;16(4):885-93
88265