Photochemical preparation of poly(N-vinyl-2-pyrrolidone)-stabilized platinum colloids and their deposition on titanium dioxide.
Preparation processes for Pt-deposited TiO(2) (Pt/TiO(2)) by the synthesis of Pt nanoparticles and their deposition were pursued by transmission electron microscopy, extended X-ray absorption fine structure, UV-vis spectroscopy, and Fourier transform infrared spectroscopic studies. Colloidal dispersions of Pt particles stabilized by poly(N-vinyl-2-pyrrolidone) (PVP) were photochemically synthesized in aqueous ethanol solution. The average diameter of Pt particles was estimated to be 2.0 +/- 0.5 nm, which was almost unchanged by changing the reducing agent from ethanol to methanol and 2-propanol. The PVP-stabilized Pt particles were distributed over a TiO(2) surface only by mixing the Pt colloidal dispersions and TiO(2). CO was chemically coordinated on the Pt particles on a TiO(2) surface after heat treatment was carried out in an O(2) flow at 673 K to completely remove the residual PVP on Pt/TiO(2). Hydrogen reduction at 473 K did not increase the amount of CO adsorbed on Pt sites. The Pt/TiO(2) catalyst after the oxidation treatment showed higher activity for CO photooxidation than that obtained for pure TiO(2) catalyst. The CO photooxidation rate was not unchanged by the H(2) reduction.
Einaga
Hisahiro
H
National Institute of Advanced Industrial Science and Technology, AIST Tsukuba West, 16-1, Onogawa, Tsukuba, Ibaraki 305-8569, Japan. h-einaga@aist.go.jp
Harada
Masafumi
M