[Stimulated emission characteristics of ZnO thin films deposited by magnetron sputtering on SiO2 substrates].
ZnO thin films were deposited by magnetron sputtering on SiQ2 substrates. The temperature dependence of the absorption spectra and the photoluminescence spectra was studied for ZnO thin film. The absorption of the longitudinal optical (LO) phonons and the free-excitons was observed at room temperature. The free-exciton emission was only observed in PL spectra at room temperature, the results indicate that ZnO thin films have excellent quality and low density of defects. The stimulated emission properties of ZnO thin films were investigated. When excitation intensity is above threshold, the FWHM o f stimulated emission peak increases and stimulated emission peak shows red shift with increasing excitation intensity. Our analysis shows that the optical gain is due to electronhole plasma emission.
Jing
Wang
W
Key Laboratory of Information Storage and Display, Institute of Optoelectronic Technology, Beijing Jiaotong University, Beijing 100044, China.
Xi-qing
Zhang
Z
Xiao-ying
Teng
T
De-ping
Xiong
X
Peng
Lin
L
Li
Wang
W
Shi-hua
Huang
H