Microleakage study of three adhesive systems.
The purpose of this in vitro study was to evaluate the efficacy of three hydrophilic dentin adhesive systems to reduce class II restoration microleakage. A total of 60 human molar teeth were used in which two box cavities were made on the distal and mesial surfaces, with a cervical margin in dentin. These cavities were randomly divided into 3 groups (n = 40 each), according to adhesive system tested: G1: OptiBond SOLO; G2: Amalgambond Plus; G3: Etch & Prime 3.0. The cavities were restored with the composite resin Z-100. The groups were thermocycled 2000 times (5 +/- 1 degrees C and 55 +/- 1 degrees C) with a dwell time of 1 min. The teeth were then immersed in 2% methylene blue, pH 7.0, for 4 h, sectioned and observed with a stereomicroscope MEIJI 2000 (35X). The evaluation was made using scores (0-4) and the results were expressed through the sum of the ranks. G1 = 1994.00; G2 = 2294.00; G3 = 2972.00. The three groups were significantly different. The self-etching adhesive system Etch & Prime 3.0 was less effective in preventing microleakage. The OptiBond SOLO adhesive was the most effective in reducing microleakage in dentin margins when compared with Amalgambond Plus and Etch & Prime 3.0.
Arias
Vanessa Gallego
VG
Department of Restorative Dentistry, Dental School of Piracicaba, UNICAMP, Piracicaba, SP, Brazil.
Campos
Inger Teixeira
IT
Pimenta
Luiz André Freire
LA
D017438:Bisphenol A-Glycidyl Methacrylate / Q000737:chemistry; D004396:Coloring Agents; D003188:Composite Resins / Q000737:chemistry; D001840:Dental Bonding; D003737:Dental Cavity Preparation / Q000145:classification; D003763:Dental Leakage / Q000145:classification*; D003764:Dental Materials / Q000737:chemistry; D003793:Dental Restoration, Permanent / Q000145:classification; D003804:Dentin / Q000648:ultrastructure; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D000431:Ethanol / Q000737:chemistry; D006801:Humans; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D008751:Methylene Blue; D010710:Phosphates / Q000737:chemistry; D019279:Resin Cements / Q000737:chemistry; D012822:Silicon Dioxide / Q000737:chemistry; D013499:Surface Properties; D013696:Temperature; D013997:Time Factors; D015040:Zirconium / Q000737:chemistry
C070606:Amalgambond; D004396:Coloring Agents; D003188:Composite Resins; D003764:Dental Materials; D017220:Dentin-Bonding Agents; C469823:Etch&Prime 3.0; D008689:Methacrylates; C428805:OptiBond SOLO; D010710:Phosphates; D019279:Resin Cements; C083568:Z100 composite resin; D000431:Ethanol; D017438:Bisphenol A-Glycidyl Methacrylate; D012822:Silicon Dioxide; D015040:Zirconium; D008751:Methylene Blue