Solubility and rheological behavior of silk fibroin (Bombyx mori) in N-methyl morpholine N-oxide.
As an important direct solvent for cellulose, N-methyl morpholine N-oxide (NMMO) is environmentally friendly, and potentially very economical. Silk fibroin (SF) (Bombyx mori) can also be dissolved directly in NMMO.H2O. However, it is unexpectedly difficult to obtain a silk fibroin solution with a concentration higher than 10wt.% in this way, and extensive degradation of silk fibroin occurs if the dissolution temperature is higher than 110 degrees C. On the other hand, it is found that regenerated silk fibroin (RSF) film is much easier to dissolve in NMMO.H2O than ordinary SF. The RSF in NMMO.H2O can be easily concentrated to a range from 10 to 25wt.%. The structural differences between the degummed silk fiber and the RSF film lead to this different solubility in NMMO.H2O. The rheological behavior of concentrated RSF/NMMO.H2O solutions were also investigated. Regenerated silk fiber was spun from this type of solution, and its strength can reach up to 3.07 cN/dtex.
Xu
Ying
Y
State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Material Science and Engineering, Donghua University, Shanghai, 200051, PR China.
Zhang
Yaopeng
Y
Shao
Huili
H
Hu
Xuechao
X
D000818:Animals; D012831:Bombyx / Q000737:chemistry*; D003497:Cyclic N-Oxides / Q000737:chemistry*; D005349:Fibroins / Q000737:chemistry*; D009025:Morpholines / Q000737:chemistry*
D003497:Cyclic N-Oxides; D009025:Morpholines; D005349:Fibroins; C067960:4-methylmorpholine N-oxide