[Study on the measurement of residual stresses around indentations in SiC/Al2O3 nanocomposite using fluorescence].
The residual stresses induced by an indentation were studied in 5% SiC/Al2O3 nanocomposite using fluorescence spectroscopy in this work. It was found that within the indentation and the region of about 10 microm outside the impression, the broadening of the R-lines is obvious, and that the compression shift is a strong function of the distance from the indentation centre. From the observed frequency shifts, the hydrostatic stresses in regions sampled in the indentation, and in the complex stress field surrounding it were measured. The same variation regularity of stresses exists along the diagonal direction and the side vertical bisector direction. The symmetry of the residual stress field around the indentation was also found.
Tao
Jie
J
Institute of Nanomaterials, Nanjing University of Aeronautics & Astronautics, Nanjing 210016, China.
Cui
Yi-hua
YH
Li
Yang
Y
D000465:Algorithms; D000537:Aluminum Oxide / Q000737:chemistry*; D017554:Carbon Compounds, Inorganic / Q000737:chemistry*; D019245:Compressive Strength; D008422:Materials Testing; D053761:Nanocomposites / Q000737:chemistry*; D017655:Silicon Compounds / Q000737:chemistry*; D013050:Spectrometry, Fluorescence
D017554:Carbon Compounds, Inorganic; D017655:Silicon Compounds; D000537:Aluminum Oxide; C022088:silicon carbide