IPM/DOSS/water microemulsions as reactors for silver sulfadiazine nanocrystal synthesis.
The first goal of this work was the preparation of a water-in-oil microemulsion from components generally regarded as safe for use in humans. Stable formulations without need of a co-surfactant were prepared from isopropyl myristate (IPM), dioctyl sodium sulfosuccinate (DOSS), and water. A ternary phase diagram was prepared for the IPM/DOSS/water system. The IPM/DOSS/water microemulsions were characterized by conductivity and dynamic laser light scattering (DLS). The results obtained from conductivity experiments indicate conductivity values of less than 1 muS/cm and were consistent with the formation of w/o microemulsions. The DLS results showed that the emulsified water droplets had an average diameter range of 9.2 to 19.7 nm, depending on composition. Modulation of the droplet size is possible by varying the water to DOSS molar ratio and DOSS to IPM ratio. The second goal of this work was the preparation of silver sulfadiazine (AgSD) nanoparticles. It was hypothesized that two separate microemulsions containing dispersed aqueous droplets of either sodium sulfadiazine or silver nitrate would react when mixed. The DLS results are consistent with the successful formation of submicron AgSD crystals.
Nesamony
Jerry
J
School of Pharmacy, The University of Louisiana, Monroe, LA 71209, USA.
Kolling
William M
WM
D003460:Crystallization; D004143:Dioctyl Sulfosuccinic Acid / Q000008:administration & dosage*; D004553:Electric Conductivity; D004655:Emulsions; D008027:Light; D009226:Myristates / Q000008:administration & dosage*; D010316:Particle Size; D012542:Scattering, Radiation; D012837:Silver Sulfadiazine / Q000008:administration & dosage* / Q000737:chemistry
D004655:Emulsions; D009226:Myristates; C008205:isopropyl myristate; D004143:Dioctyl Sulfosuccinic Acid; D012837:Silver Sulfadiazine