The role of poly(ethylene glycol) in the formation of silver nanoparticles.
Silver nanoparticles were prepared under mild conditions by exploiting poly(ethylene glycol) (PEG) in the absence of other chemicals. The chain length of PEG was discovered to play the key role in the formation of silver nanoparticles. Ethylene glycol, which was used as a reducing agent for the preparation of metal particles at high temperatures (>170 degrees C), was inactive for the reducing of Ag+ at 80 degrees C. Surprisingly, Ag+ can be smoothly reduced to silver nanoparticles at the same condition in PEG 2000. Further studies demonstrated that the reducing rate of Ag+ to nano-Ag was remarkably enhanced with the increase of polymer chain length of PEG. The particle size depended upon the reaction temperature and concentration of the precursor and an increase in temperature effected a shift of particle size range from ca. 10 to 80 nm. In addition, a noticeable change of sphere to polyprism nanosilver was observed when the reaction temperature was elevated to 120 degrees C.
Luo
Chengcai
C
Department of Chemistry, Zhejiang University, Hangzhou 310027, China.
Zhang
Yuhong
Y
Zeng
Xiaowei
X
Zeng
Yuewu
Y
Wang
Yanguang
Y
D049329:Nanostructures / Q000737:chemistry*; D010316:Particle Size; D011092:Polyethylene Glycols / Q000737:chemistry*; D012834:Silver / Q000737:chemistry*; D013499:Surface Properties; D013696:Temperature
D012834:Silver; D011092:Polyethylene Glycols