title: Temperature dependence of formation of nanorods and dots of iodine compounds on an H-terminated Si(111) surface in a concentrated HI solution.
abstract: Immersion of atomically flat, H-terminated Si(111) surfaces in 7.6 M HI for 0.5 - 4 h caused spontaneous formation of nanosized clusters at the Si surface. X-ray photoelectron spectroscopy analysis suggested that the clusters were composed of silicon iodides (such as SiHxI4-x), produced most probably by Si etching with HI. Atomic force microscopy inspection revealed that the immersion at a low temperature below about 30 degrees C led to the formation of long rod-shaped clusters, oriented in the (112) direction or equivalents, whereas the immersion at a high temperature above 30 degrees C led to the formation of circular dot clusters, their size and shape changing abruptly at about 70 degrees C. It is shown experimentally that the formation of dot clusters at a high immersion temperature is explained on the basis of thermodynamics, whereas that of oriented rod clusters at a low temperature is explained by a kinetics-controlled mechanism.
authors.affiliation: Division of Chemistry, Graduate School of Engineering Science, Osaka University, Toyonaka, Osaka 560-8531, Japan.
authors.forename: Akihito
authors.initials: A
authors.lastname: Imanishi
authors.forename: Takeshi
authors.initials: T
authors.lastname: Hayashi
authors.forename: Yoshihiro
authors.initials: Y
authors.lastname: Nakato