Theoretical and experimental study of the adsorption of neutral glycine on silica from the gas phase.
The adsorption of neutral glycine onto amorphous silica was investigated both theoretically and experimentally. DFT calculations were performed at the BLYP-631++G** level using a cluster approach. Several possible configurations involving the formation of H bonds between glycine and one, two, or three silanol groups (SiOH) were considered. The most favorable bonding of glycine with one silanol group (45 kJ mol(-1)) occurs through the COOH moiety, thus forming a cycle in which the CO group is an H-bond acceptor whereas the acidic OH group is an H-bond donor. With two or three silanol groups, additional H bonds are formed between the amine moiety and the silanol groups, which leads to an increased adsorption energy (70 and 80 kJ mol(-1) for two and three silanol groups, respectively). Calculated nu(CO), delta(HNH), and delta(HCH) values are sensitive to the adsorption mode. A bathochromic shift of nu(CO) as compared to the nu(CO) of free glycine (calculated in the 1755-1790 cm(-1) range) is found for glycine in interaction with silanol(s). The more H bonds are formed between the COOH moiety and silanol groups, the higher the bathochromic shift. For delta(HNH), no shift is found for glycine adsorbed on one and two silanol groups (where the amine is either not bound or an H-bond donor), whereas a bathochromic shift is calculated with three silanols when the amine moiety is an H-bond acceptor. Experimental FTIR spectra performed at room temperature for glycine adsorbed at 160 degrees C on Aerosil amorphous silica exhibit bands at 1371, 1423, 1630, and 1699 cm(-1). The experimental/calculated frequencies have their best correspondence for glycine adsorbed on two silanol groups. It is important to note that the forms giving the best correspondence to experimental frequencies are the most stable ones.
Lomenech
C
C
Laboratoire de Réactivité de Surface, UMR CNRS 7609, Université Pierre et Marie Curie, case courrier 178, 4 Place Jussieu, 75252 Paris Cedex 05, France.
Bery
G
G
Costa
D
D
Stievano
L
L
Lambert
J F
JF
D000327:Adsorption; D005998:Glycine / Q000737:chemistry*; D008962:Models, Theoretical; D012822:Silicon Dioxide / Q000737:chemistry*; D017550:Spectroscopy, Fourier Transform Infrared
D012822:Silicon Dioxide; D005998:Glycine