Effects of nano HAP on biological and structural properties of glass bone cement.
A novel type of glass-based nanoscale hydroxyapatite (HAP) bioactive bone cement (designed as GBNHAPC) was synthesized by adding nanoscale hydroxyapatite crystalline (20-40 nm), into the self-setting glass-based bone cement (GBC). The inhibition rate of nanoscale HAP and micron HAP on osteosarcoma U2-OS cells was examined. The effects of nanoscale HAP on the crystal phase, microstructure and compressive strength of GBNHAPC were studied, respectively. It was concluded that nanoscale HAP could inhibit the cell proliferation, whereas micron HAP could not, and that nanoscale HAP could be dispersed in the cement evenly and the morphology did not change significantly after a longer immersion time. XRD and FTIR results show nanoscale HAP did not affect the setting reaction of the cement. Furthermore, GBNHAPC had a higher compressive strength (92.6 +/- 3.8 MPa) than GBC (80.1 +/- 3.0 MPa). It was believed that GBNHAPC might be a desirable biomaterial that could not only fill bone defects but also inhibit cancer cell growth.
Fu
Qiang
Q
School of Materials Science and Engineering, Tongji University, Shanghai, 200092, PR China. fuharry@hotmail.com
Zhou
Nai
N
Huang
Wenhai
W
Wang
Deping
D
Zhang
Liying
L
Li
Haifeng
H
D001843:Bone Cements; D045744:Cell Line, Tumor; D003470:Culture Media; D005898:Glass; D006801:Humans; D006882:Hydroxyapatites / Q000737:chemistry; D008422:Materials Testing; D008855:Microscopy, Electron, Scanning; D015394:Molecular Structure; D036103:Nanotechnology; D012516:Osteosarcoma / Q000473:pathology; D014961:X-Ray Diffraction
D001843:Bone Cements; D003470:Culture Media; D006882:Hydroxyapatites