An experimental investigation of the stability of ethylcellulose latex: correlation between zeta potential and sedimentation.
This paper aims at explaining the experimental observations of the stability and redispersibility of an aqueous ethylcellulose latex through the electrokinetic characterization of the particles. The surface charge and the electrical double layer thickness play an essential role in the stability of the system, hence the need for a full characterization of the polymeric particles. The effect of both pH and ionic strength of the dispersion medium were investigated. It was found that at acid pH values the latex displays "delayed" or "hindered" sedimentation: in such conditions, the electrophoretic mobility and zeta potential are rather low, indicating a small electrokinetic charge on the particles. At alkaline pH, when the dissociation of ionizable surface groups must be complete, the zeta potential is high and negative. The electrostatic repulsion between polymer particles is responsible for the low sedimentation volume and poor redispersibility of the latex. The effect of NaCl and CaCl(2) concentration on both the zeta potential and stability of the latexes was also investigated: it was found that CaCl(2) has the greatest influence, yielding flocculated, easily re-dispersible systems when its concentration in the dispersion medium is high enough. There qualitative observations were ascertained by means of calculations of the potential energy of interaction between particles. In the case of NaCl solutions, a high and relatively wide potential energy barrier was predicted, that may prevent the particle aggregation. Above 5mM NaCl a shallow minimum in the potential energy curves must lead to the formation of aggregates. Similar results were found with CaCl(2) solutions, although in this case the secondary minima are deeper and appear at lower concentrations.
Gallardo
V
V
Department of Pharmacy and Pharmaceutical Technology, School of Pharmacy, University of Granada, 18071 Granada, Spain. vglara@ugr.es
Morales
M E
ME
Ruiz
M A
MA
Delgado
A V
AV
D002122:Calcium Chloride; D002482:Cellulose / Q000031:analogs & derivatives* / Q000648:ultrastructure; D004355:Drug Stability; D004553:Electric Conductivity; D005427:Flocculation; D006863:Hydrogen-Ion Concentration; D007840:Latex / Q000138:chemical synthesis / Q000737:chemistry*; D008855:Microscopy, Electron, Scanning; D009994:Osmolar Concentration; D010316:Particle Size; D012965:Sodium Chloride; D013535:Suspensions / Q000737:chemistry*; D013997:Time Factors
D007840:Latex; D013535:Suspensions; D012965:Sodium Chloride; D002482:Cellulose; D002122:Calcium Chloride