Structural and magnetic properties of Fe and Co nanoparticles embedded in powdered Al2O3.
The structural and magnetic properties of powdered composites consisting of nanosized Fe and Co particles embedded in alumina grains have been investigated. The composites were synthesized by a novel and simple method using co-precipitation from a hybrid gel solution containing layered double hydroxide and aluminium hydroxide. After a vacuum annealing procedure, the Fe composites have a negligible number of Fe(+3) ions and a high concentration of crystalline alpha-Fe nanoparticles having truncated polyhedron shapes with an average diameter of 20 nm that are physically well separated from each other. Magnetization measurements as a function of temperature revealed a superparamagnetic-like behavior characteristic of an assembly of fine particles. A spurious ferromagnetism related to surface interaction between magnetic particles from different powder grains and the formation mechanism of the composites are also discussed.
Santini
Otávio
O
Departamento de Física, Universidade Federal do Paraná, Centro Politécnico, Curitiba, PR, Brazil.
de Moraes
Adriano R
AR
Mosca
Dante H
DH
de Souza
Paulo E N
PE
de Oliveira
Adilson J A
AJ
Marangoni
Rafael
R
Wypych
Fernando
F
D000537:Aluminum Oxide / Q000138:chemical synthesis / Q000737:chemistry*; D003035:Cobalt / Q000737:chemistry*; D003460:Crystallization; D007501:Iron / Q000737:chemistry*; D008280:Magnetics; D053758:Nanoparticles / Q000737:chemistry*; D010316:Particle Size; D011208:Powders / Q000737:chemistry; D013499:Surface Properties; D013696:Temperature
D011208:Powders; D003035:Cobalt; D007501:Iron; D000537:Aluminum Oxide