title: Shear bond strengths of two composite core materials after using all-in-one and single-bottle dentin adhesives.
abstract: OBJECTIVE
  The purpose of this study was to compare the shear bond strengths of 2 composite core materials after using all-in-one and single-bottle dentin bonding materials.
  
  
  METHODS
  The occlusal surfaces of 100 extracted, intact human third molars were ground to expose a flattened area of dentin and polished with 600-grit silicon carbide paper. Specimens were divided into 5 main groups (n= 20). Three all-in-one (AQ Bond, One-Up Bond, Xeno-CF Bond) and 2 single-bottle adhesives (Single Bond, One-Step Plus) were used. Each group was further divided into 2 subgroups. Ti-Core and Built-it F.R. core materials were applied using a translucent plastic ring (diameter: 3 mm, height: 5 mm). After storage in 37 degrees C water for 24 hours, shear bond strengths were measured using a Universal testing machine with a crosshead speed of 0.5 mm/min. Debonded dentin surfaces were examined with SEM. Two-way analysis of variance (ANOVA) and multiple comparison (Tukey) tests were used for statistical analysis of data.
  
  
  RESULTS
  Two-way ANOVA revealed that the type of core material did not significantly influence the shear bond strength (p > 0.05), whereas there were significant differences in shear bond strength among the types of bonding agents (p < 0.0001). Shear bond strengths for single-bottle adhesive systems were significantly higher than those for all-in-one adhesive systems (p < 0.05). Furthermore, the interaction of these 2 parameters was not significant (p > 0.05). The fracture modes were predominantly adhesive for all-in-one adhesives and cohesive for single-bottle adhesives.
  
  
  CONCLUSIONS
  Bonding of composite core materials with the newly developed all-in-one dentin adhesives produced lower shear bond strengths as compared with single-bottle adhesives.
authors: Faculty of Dentistry, Department of Fixed Prosthodontics, Istanbul University, Istanbul, Turkey. denizsen65@hotmail.com
authors: Deniz
authors: D
authors: Sen
authors: Gökhan
authors: G
authors: Akgüngör
mesh_terms: D000704:Analysis of Variance; D017438:Bisphenol A-Glycidyl Methacrylate; D020770:Compomers; D003188:Composite Resins; D001840:Dental Bonding; D003793:Dental Restoration, Permanent / Q000379:methods*; D003799:Dental Stress Analysis; D017220:Dentin-Bonding Agents; D006801:Humans; D008422:Materials Testing; D008689:Methacrylates; D011897:Random Allocation; D019279:Resin Cements; D033081:Shear Strength; D018709:Statistics, Nonparametric
chemical_list: C453842:AQ bond; C483702:Build-it composite resin; D020770:Compomers; D003188:Composite Resins; D017220:Dentin-Bonding Agents; D008689:Methacrylates; C446260:One-Up-Bond F; D019279:Resin Cements; C417842:Xeno compomer; C115612:single bond; C079578:Ti-Core composite resin; D017438:Bisphenol A-Glycidyl Methacrylate