Influence of intense pulsed laser irradiation on optical and morphological properties of gold nanoparticle aggregates produced by surface acid-base reactions.
Gold nanoparticles were surface modified with an ionizable and pH-sensitive monolayer of thiobarbituric acid (TBA). By variation of the pH value of the solution, nanoparticle aggregates can be produced in a controlled way. The aggregates thus prepared were irradiated with an intense pulsed laser at 532 nm. The products in solution were examined by transmission electron microscopy (TEM) and optical absorption spectroscopy. The TEM images of the products revealed that the nanoparticle aggregates dissociate upon laser irradiation and form much smaller gold nanoparticles. The optical absorption spectra measured simultaneously show the gradual disappearance of the absorbance band of the aggregates at around 680 nm. Additionally, a blue shift (from 534 to 524 nm) of the resonance absorbance corresponding to isolated nanoparticles has been observed. All the observations suggest that the colloidal solution becomes more stable after laser irradiation. Both the reduced nanoparticle size and the stabilizing TBA ligands present on the particle surface contribute to the acquired stability of the colloidal solutions.
Peng
Zhangquan
Z
Walther
Thomas
T
Kleinermanns
Karl
K