CO oxidation on Pt-modified Rh(111) electrodes.
The CO electro-oxidation reaction was studied on platinum-modified Rh(111) electrodes in 0.5 M H2SO4 using cyclic voltammetry and chronoamperometry. The Pt-Rh(111) electrodes were generated during voltammetric cycles at 50 mV s(-1) in a 30 microM H2PtCl6 and 0.5 M H2SO4 solution. Surfaces generated by n deposition cycles were investigated (Ptn-Rh(111) with n=2, 4, 6, 8, 10, and 16). The blank cyclic voltammograms of these surfaces are characterized by a pronounced sharpening of the hydrogen/(bi)sulfate adsorption/desorption peaks, typical for Rh(111), and the appearance of contributions between 0.1 and 0.4 V, which were ascribed to hydrogen/(bi)sulfate adsorption/desorption on the deposited platinum. At higher potentials, the surface oxidation of Rh(111) is enhanced by the presence of platinum. The structure of the Pt-modified electrodes was investigated by STM imaging. At low Pt coverages (Pt2-Rh(111)), monoatomically high islands are formed, which grow three dimensionally as the number of deposition cycles increases. After eight cycles, the monolayer islands have grown in diameter and range from mono- to multiatomic height. At even higher Pt coverage (Pt16-Rh(111)), the islands grow to particles of approx. 10 nm in diameter, which are 5-6 atoms high. The CO stripping voltammetry on these surfaces is characterized by two peaks: A low-potential, structure-insensitive peak, ascribed to CO reacting at the platinum monolayer islands, whose onset is shifted 150, 250, and 100 mV negatively with respect to pure Rh(111), Pt(111), and polycrystalline Pt, respectively, indicating the enhanced CO electro-oxidation properties of the Pt overlayer system. A peak at higher potentials displays strong structure sensitivity (particle-size effect) and was ascribed to CO reacting on the islands of multiatomic height. Current-time transients recorded on the surface with the highest amount of monolayer islands (Pt4-Rh(111)) also indicate enhanced CO-oxidation kinetics. Comparison of the Pt4-Rh(111) current-time transients recorded at 0.635, 0.675, and 0.750 V versus RHE (reversible hydrogen electrode) with those of pure Rh(111) and Pt(111) shows greatly reduced reaction times. A Cottrellian decay at long times indicates surface-diffusion-limited CO oxidation on the bare Rh(111) surface, while the peak visible at short times is indicative of CO reacting at the monolayer platinum islands. The results presented here show that, as indicated by density functional theory (DFT) calculations, the CO-adlayer oxidation for this system is enhanced compared to both pure Rh and Pt.
Housmans
T H M
TH
Schuit Institute of Catalysis, Laboratory of Inorganic, Chemistry and Catalysis, Eindhoven University of Technology, 5600 MB Eindhoven, The Netherlands. T.H.M.Housmans@tue.nl
Feliu
J M
JM
Gómez
R
R
Koper
M T M
MT
D002248:Carbon Monoxide / Q000737:chemistry*; D004566:Electrodes; D016252:Microscopy, Scanning Tunneling / Q000379:methods; D010084:Oxidation-Reduction; D010316:Particle Size; D010984:Platinum / Q000737:chemistry*; D012238:Rhodium / Q000737:chemistry*; D012680:Sensitivity and Specificity; D013499:Surface Properties; D013997:Time Factors
D010984:Platinum; D002248:Carbon Monoxide; D012238:Rhodium