Nanoindentation of injection molded PLA and self-reinforced composite PLA after in vitro conditioning for three months.
Poly(lactic acid) (PLA) is used for medical devices such as sutures or orthopedic screws. A standard way to determine the loss of mechanical properties of a degradable polymer would be to soak the polymer in phosphate buffered saline (PBS) and test the desired property as a function of immersion time. This method is not sensitive enough to discern changes in mechanical properties through the cross-section of the polymer and neglects the degradation that is occurring at the molecular level. This article presents results of a nanoindentation study carried out with PLA. The modulus and hardness of PLA is characterized as a function of processing method, immersion time in PBS, and location of the indent. Measuring local properties with the nanoindenter allowed detection of differences in material properties as a function of all three of these variables. The mechanical properties on the edge were lower than the interior of the sample after in vitro degradation, and changes were seen earlier for nanoindentation than for traditional flexural or tensile tests. The nanoindenter is a valuable tool for quantifying changes in material properties and may have applicability for accelerated tests to screen biomaterials.
Wright-Charlesworth
Debra D
DD
Department of Biomedical Engineering, Michigan Technological University, 1400 Townsend Dr., Houghton, Michigan 49931, USA. wright@mtu.edu
Miller
Darinda M
DM
Miskioglu
Ibrahim
I
King
Julia A
JA
D001672:Biocompatible Materials; D002021:Buffers; D019344:Lactic Acid; D036103:Nanotechnology; D011091:Polyesters; D011108:Polymers; D012965:Sodium Chloride; D013997:Time Factors
D001672:Biocompatible Materials; D002021:Buffers; D011091:Polyesters; D011108:Polymers; D019344:Lactic Acid; D012965:Sodium Chloride; C033616:poly(lactide)