VO2+ ions in zinc lead borate glasses studied by EPR and optical absorption techniques.
Electron paramagnetic resonance (EPR) and optical absorption spectra of vanadyl ions in zinc lead borate (ZnO-PbO-B2O3) glass system have been studied. EPR spectra of all the glass samples exhibit resonance signals characteristic of VO2+ ions. The values of spin-Hamiltonian parameters indicate that the VO2+ ions in zinc lead borate glasses were present in octahedral sites with tetragonal compression and belong to C4V symmetry. The spin-Hamiltonian parameters g and A are found to be independent of V2O5 content and temperature but changing with ZnO content. The decrease in Deltag( parallel)/Deltag( perpendicular) value with increase in ZnO content indicates that the symmetry around VO2+ ions is more octahedral. The decrease in intensity of EPR signal above 10 mol% of V2O5 is attributed to a fall in the ratio of the number of V4+ ions (N4) to the number of V5+ ions (N5). The number of spins (N) participating in resonance was calculated as a function of temperature for VO2+ doped zinc lead borate glass sample and the activation energy was calculated. From the EPR data, the paramagnetic susceptibility was calculated at various temperatures and the Curie constant was evaluated from the 1/chi-T graph. The optical absorption spectra show single absorption band due to VO2+ ions in tetragonally distorted octahedral sites.
Prakash
P Giri
PG
Department of Physics, Sri Venkateswara University, Tirupati 517502, India.
Rao
J Lakshmana
JL
D000042:Absorption; D001881:Borates / Q000737:chemistry*; D002413:Cations, Divalent / Q000737:chemistry*; D004578:Electron Spin Resonance Spectroscopy; D005898:Glass / Q000737:chemistry*; D007854:Lead / Q000737:chemistry*; D055095:Optics and Photonics; D013053:Spectrophotometry; D013696:Temperature; D014638:Vanadates / Q000737:chemistry*; D015034:Zinc Oxide / Q000737:chemistry
D001881:Borates; D002413:Cations, Divalent; D007854:Lead; D014638:Vanadates; D015034:Zinc Oxide