Probing slow dynamics in supported thin polymer films.
We have used variable cooling rate ellipsometric measurements to probe the slow dynamics in thin supported polystyrene films. For the slowest cooling rates (approximately 1 K/min) the measured Tg values are reduced below the bulk value with the measured Tg of 341 K for a 6 nm film. As the cooling rate is increased the Tg reductions become smaller until at cooling rates >90 K/min there is only slight evidence for a film-thickness-dependent Tg value. By relating the cooling rate to a relaxation time, we show that the relaxation dynamics of the thin films appears to become Arrhenius with an activation energy that decreases with decreasing film thickness. We discuss this in terms of a possible connection to a length scale for cooperative motion. Finally, the results can be used to resolve a number of outstanding contradictory reports in the literature.
Fakhraai
Zahra
Z
Department of Physics and Guelph-Waterloo Physics Institute, University of Waterloo, 200 University Avenue W., Waterloo, Ontario, Canada N2L 3G1.
Forrest
James A
JA