[Light induced polymerization of resin composite restorative materials].
BACKGROUND
Dimensional stability of polymer-based dental materials is compromised by polymerization reaction of the monomer. The conversion into a polymer is accompanied by a closer packing of molecules, which leads to volume reduction called curing contraction or polymerization shrinkage. Curing contraction may break the adhesion between the adhesive system and hard tooth tissues forming microgaps which may result in marginal deterioration, recurrent caries and pulp injury. POLYMERIZATION SHRINKAGE OF RESIN-BASED RESTORATIVE DENTAL MATERIALS: Polymerization of the organic phase (nonomer molecules) of resin-based dental materials causes shrinkage. The space occupied by filler particles is not associated with polymerization shrinkage. However, high filler loading within certain limits, can contribute to a lesser curing contraction.
Polymerization shrinkage stress of polymer-based dental resins can be controlled in various ways. The adhesive bond in tooth-restoration interface guides the contraction forces to cavity walls. If leakage occurs, complications like secondary caries and pulpal irritation may jeopardize the longevity of a restoration. Stress relieve can be obtained by modifications of the monomer and photoinitiator, or by specially designed tooth preparation and application of bases and liners of low modulus of elasticity. The polymerization contraction can be compensated by water absorption due to oral cavity surrounding. The newest approach to stress relief is based on modulation of polymerization initiation.


CONCLUSIONS
This work deals with polymerization contraction and how to achieve leak-proof restoration. Restorative techniques that may reduce the negative effect of polymerization shrinkage stress need further research in order to confirm up-to-date findings.
Blazić
Larisa
L
Univerzitet u Novom Sadu, Medicinski fakultet, Novi Sad Klinika za stomatologiju.
Marković
Dubravka
D
Durić
Milanko
M
D003188:Composite Resins / Q000737:chemistry*; D008027:Light; D010777:Photochemistry; D011108:Polymers
D003188:Composite Resins; D011108:Polymers