Optical studies on chemical bath deposited nanocrystalline CdS thin films.
Nanocrystalline cadmium sulphide thin films were prepared by the chemical bath (CB) deposition using a mixed aqueous solution of cadmium chloride, thiourea, and ammonium chloride. The XRD patterns showed that the CdS films were of hexagonal phase with preferred (002) orientation. From ellipsometric measurements, the film thickness was found to be in order of 66 nm and the optical band gap was estimated to be 2.4 eV.
Pradhan
Basudev
B
Nanotechnology Research Laboratories, The Department of Materials, Queen Mary College, University of London, Mile End Road, London, E1 4NS, UK.
Sharma
Ashwani K
AK
Ray
Asim K
AK
D000643:Ammonium Chloride / Q000737:chemistry; D019256:Cadmium Chloride; D019187:Cadmium Compounds / Q000737:chemistry*; D003460:Crystallization; D003461:Crystallography; D004563:Electrochemistry; D046911:Macromolecular Substances / Q000737:chemistry; D008422:Materials Testing; D008956:Models, Chemical; D015233:Models, Statistical; D036103:Nanotechnology / Q000295:instrumentation / Q000379:methods*; D012825:Silicon / Q000737:chemistry; D013053:Spectrophotometry; D013440:Sulfides / Q000737:chemistry*; D013499:Surface Properties; D013890:Thiourea / Q000737:chemistry; D014961:X-Ray Diffraction
D019187:Cadmium Compounds; D046911:Macromolecular Substances; D013440:Sulfides; D000643:Ammonium Chloride; C034939:cadmium sulfide; D013890:Thiourea; D019256:Cadmium Chloride; D012825:Silicon