The effect of Nb addition on mechanical properties, corrosion behavior, and metal-ion release of ZrAlCuNi bulk metallic glasses in artificial body fluid.
Bulk metallic glasses (BMGs) of Zr(65 - x)Nb(x)- Cu(17.5)Ni(10)Al(7.5) with Nb = 0, 2, and 5 at % were prepared by copper mold casting. Compression tests reveal that the two BMGs containing Nb exhibited superior strength and plasticity to the base alloy. The corrosion behavior of the alloys obtained was investigated in artificial body fluid by electrochemical measurements. It was found that the addition of Nb significantly enhanced the corrosion resistance of the Zr-based BMG, as indicated by a remarkable increase in corrosion potential and pitting potential. XPS analysis revealed that the passive film formed after anodic polarization was enriched in aluminum oxide and depleted in phosphate ions for the BMGs containing Nb, which accounts for the improvement of corrosion resistance. On the other hand, metal-ion release of different BMGs were determined in PPb (ng/mL) level with inductively coupled plasma mass spectrometry (ICP-MS) after being immersed in artificial body fluid at 37 degrees C for 20 days. It was found that the addition of Nb considerably reduced the ion release of all kinds of metals of the base system. This is probably attributed to the promoting effect of Nb on a rapid formation of highly protective film.
Qiu
C L
CL
The State Key Lab of Die & Mould Technology, Huazhong University of Science and Technology, 430074 Wuhan, China.
Liu
L
L
Sun
M
M
Zhang
S M
SM
D000535:Aluminum; D001672:Biocompatible Materials / Q000737:chemistry; D003300:Copper; D003343:Corrosion; D005898:Glass / Q000737:chemistry; D006358:Hot Temperature; D008670:Metals / Q000737:chemistry; D009532:Nickel; D009556:Niobium; D013057:Spectrum Analysis; D015040:Zirconium
D001672:Biocompatible Materials; D008670:Metals; D009556:Niobium; D003300:Copper; D009532:Nickel; D015040:Zirconium; D000535:Aluminum