New oxidation treatment of NiTi shape memory alloys to obtain Ni-free surfaces and to improve biocompatibility.
Various oxidation treatments were applied to nearly equiatomic NiTi alloys so as to form a Ni-free protective oxide on the surface. Sample surfaces were analyzed by X-ray Photoelectron Spectroscopy, and NiTi transformation temperatures were determined by differential scanning calorimetry (DSC) before and after the surface treatment. An ion release experiment was carried out up to one month of immersion in SBF for both oxidized and untreated surfaces. The results show that oxidation treatment in a low-oxygen pressure atmosphere leads to a high surface Ti/Ni ratio, a very low Ni surface concentration and a thick oxide layer. This oxidation treatment does not significantly affect the shape memory properties of the alloy. Moreover, the oxide formed significantly decreases Ni release into exterior medium comparing with untreated surfaces. As a consequence, this new oxidation treatment could be of great interest for biomedical applications, as it could minimize sensitization and allergies and improve biocompatibility and corrosion resistance of NiTi shape memory alloys.
Michiardi
A
A
Center of Reference for Bioengineering of Catalonia (CREBEC), Biomaterials and Biomechanics Division, Department of Materials Science and Metallurgy, Technical University of Catalonia (UPC), Avda. Diagonal 647, Barcelona, 08028, Spain.
Aparicio
C
C
Planell
J A
JA
Gil
F J
FJ
D000497:Alloys / Q000737:chemistry*; D001672:Biocompatible Materials / Q000737:chemistry*; D009532:Nickel / Q000032:analysis* / Q000737:chemistry; D010087:Oxides / Q000032:analysis; D010100:Oxygen / Q000737:chemistry; D013499:Surface Properties; D014025:Titanium / Q000032:analysis* / Q000737:chemistry
D000497:Alloys; D001672:Biocompatible Materials; D010087:Oxides; D009532:Nickel; D014025:Titanium; D010100:Oxygen