157 nm F2-laser writing of silica optical waveguides in silicone rubber.
Silica (SiO2) optical waveguides have been fabricated on the surface of silicone [(SiO(CH3)2)n] rubber by photochemical modification of silicone rubber into silica with 157 nm F2-laser radiation. The 2 mm thick silicone was exposed through a thin (approximately 0.2 mm) air layer to generate oxygen radicals that chemically assisted in the silica transformation. Silica waveguides were defined in 8-16 microm wide exposure strips by a proximity Cr-on-CaF2 photomask. Optimum laser processing conditions are presented for generating crack-free waveguides with good optical transparency at red (635 nm) and infrared (1550 nm) wavelengths. A propagation loss of approximately 6 dB/cm is reported at the 1550 nm wavelength.