title: Microstructure and corrosion behavior of porous coatings on titanium alloy by vacuum-brazed method.
abstract: The microstructural evolution and electrochemical characteristics of brazed porous-coated Ti-6Al-4V alloy were analyzed and compared with respect to the conventionally 1300 degrees C sintering method. The titanium filler metal of low-melting-point (934 degrees C) Ti-15Cu-15Ni was used to braze commercially pure (CP) titanium beads onto the substrate of Ti-6Al-4V alloy at 970 degrees C for 2 and 8 h. Optical microscopy, scanning and transmission electron microscopy, and X-ray diffractometry (XRD) were used to characterize the microstructure and phase of the brazed metal; also, the potentiostat was used for corrosion study. Experimental results indicate that the bead/substrate contact interface of the 970 degrees C brazed specimens show larger contact area and higher radius curvature in comparison with 1300 degrees C sintering method. The microstructure of brazed specimens shows the Widmanstätten structure in the brazed zone and equiaxed alpha plus intergranular beta in the Ti-6Al-4V substrate. The intermetallic Ti2Ni phase existing in the prior filler metal diminishes, while the Ti2Cu phase can be identified for the substrate at 970 for 2 h, but the latter phase decrease with time. In Hank's solution at 37 degrees C, the corrosion rates of the 1300 degrees C sintering and the 970 degrees C brazed samples are similar at corrosion potential (E(corr)) in potentiodynamic test, and the value of E(corr) for the brazed sample is noble to the sintering samples. The current densities of the brazed specimens do not exceed 100 microA/cm2 at 3.5 V (SCE). These results suggest that the vacuum-brazed method exhibits the potentiality to manufacture the porous-coated specimens for biomedical application.
authors.affiliation: Institute of Oral Medicine, National Cheng Kung University, Tainan 701, Taiwan. tmlee@mail.ncku.edu.tw
authors.forename: T M
authors.initials: TM
authors.lastname: Lee
authors.forename: E
authors.initials: E
authors.lastname: Chang
authors.forename: C H
authors.initials: CH
authors.lastname: Yen
mesh_terms: D000497:Alloys / Q000138:chemical synthesis*; D020099:Coated Materials, Biocompatible / Q000138:chemical synthesis* / Q000737:chemistry; D003300:Copper; D003343:Corrosion; D008422:Materials Testing; D009532:Nickel; D016062:Porosity; D013696:Temperature; D014025:Titanium / Q000737:chemistry*; D014618:Vacuum
chemical_list: D000497:Alloys; D020099:Coated Materials, Biocompatible; D003300:Copper; D009532:Nickel; D014025:Titanium