Broad-band antireflection coating at near-infrared wavelengths by a breath figure.
We prepared a porous thin film by spin-coating of a cellulose acetate butyrate (CAB) solution in tetrahydrofuran under a humid environment. Due to evaporative cooling during spin-coating, condensed water droplets were formed by a breath figure on the CAB solution, and these developed a porous structure after complete drying. By varying the solution concentration and rotating speeds, two distinct morphologies were generated: top and bottom layers with higher and lower porosities, respectively. We found that the two-layer porous film coated on glass exhibited low reflectance of less than 1% in the near-infrared (NIR) regime corresponding to wavelengths between 900 and 2200 nm. Since the porous structure was very uniform over a large area, the film could be easily employed for broad-band antireflection coating at NIR wavelengths.
Park
Min Soo
MS
Department of Chemical Engineering and Polymer Research Institute, Electric and Computer Engineering Division, Pohang University of Science and Technology, Kyungbuk 790-784, Korea.
Kim
Jin Kon
JK