Th uptake on montmorillonite: a powder and polarized extended X-ray absorption fine structure (EXAFS) study.
The uptake process of Th(IV) onto montmorillonite was studied using powder and polarized-EXAFS (P-EXAFS) spectroscopy. Sorption samples were prepared in 0.1 M NaClO(4) solutions either undersaturated (pH 2 and 3, [Th](initial): 2.7x10(-6) to 4x10(-4) M) or supersatured (pH 5, [Th](initial): 4.3x10(-5) to 4x10(-4) M) with respect to amorphous ThO(2). Th loading varied between 1-157 micromol/g at pH 3 and 14-166 micromol/g at pH 5 and equaled 41 micromol/g at pH 2. At pH 5 and high surface loading the EXAFS spectrum resembled that of amorphous Th(OH)(4), suggesting the precipitation of a Th hydrous hydroxide. At low and intermediate surface coverage two O coordination shells at approximately 2.24 and approximately 2.48 A, and one Si shell at 3.81-3.88 A, were systematically observed regardless of pH. The formation of Th nucleation products and Th-Si solution complexes and the sorption of Th on a silica precipitate were excluded from the EXAFS spectra analysis and solution chemistry. In these conditions, Th was shown to bond the montmorillonite surface by sharing double corners with Si tetrahedra. This structural interpretation is consistent with surface coverage calculations which showed that the edge sites were saturated in the two highest concentrated samples (34 and 157 micromol/g) at pH 3.
Dähn
Rainer
R
Waste Management Laboratory, Paul Scherrer Institut, Villigen CH-5232, Switzerland. Rainer.Daehn@psi.ch
Scheidegger
André M
AM
Manceau
Alain
A
Curti
Enzo
E
Baeyens
Bart
B
Bradbury
Michael H
MH
Chateigner
Daniel
D