The influence of mold temperature on the fit of cast crowns with commercially pure titanium.
Commercially pure titanium (CP Ti) has been widely applied to fabricate cast devices because of its favorable properties. However, the mold temperature recommended for the manufacture of casts has been considered relatively low, causing inadequate castability and poor marginal fit of cast crowns. This study evaluated and compared the influence of mold temperature (430 degrees C--as control, 550 degrees C, 670 degrees C) on the marginal discrepancies of cast CP Ti crowns. Eight bovine teeth were prepared on a mechanical grinding device and impressions were used to duplicate each tooth and produce eight master dies. Twenty-four crowns were fabricated using CP Ti in three different groups of mold temperature (n = 8): 430 degrees C (as control), 550 degrees C and 670 degrees C. The gap between the crown and the bovine tooth was measured at 50 X magnification with a traveling microscope. The marginal fit values of the cast CP Ti crowns were submitted to the Kruskal-Wallis test (p = 0.03). The 550 degrees C group (95.0 microm) showed significantly better marginal fit than the crowns of the 430 degrees C group (203.4 microm) and 670 degrees C group (213.8 microm). Better marginal fit for cast CP Ti crowns was observed with the mold temperature of 550 degrees C, differing from the 430 degrees C recommended by the manufacturer.
Fragoso
Wagner Sotero
WS
Department of Prosthodontics, School of Dentistry of Piracicaba, State University of Campinas.
Henriques
Guilherme Elias Pessanha
GE
Contreras
Edwin Fernando Ruiz
EF
Mesquita
Marcelo Ferraz
MF
D000818:Animals; D002417:Cattle; D003442:Crowns / Q000592:standards*; D003734:Dental Casting Investment; D003735:Dental Casting Technique / Q000592:standards*; D008422:Materials Testing; D018709:Statistics, Nonparametric; D013696:Temperature; D013816:Thermodynamics; D014025:Titanium / Q000737:chemistry*
D003734:Dental Casting Investment; D014025:Titanium