Bacterial oxidation of sulfide minerals in column leaching experiments at suboptimal temperatures.
The purpose of the work was to quantitatively characterize temperature effects on the bacterial leaching of sulfide ore material containing several sulfide minerals. The leaching was tested at eight different temperatures in the range of 4 to 37 degrees C. The experimental technique was based on column leaching of a coarsely ground (particle diameter, 0.59 to 5 mm) ore sample. The experimental data were used for kinetic analysis of chalcopyrite, sphalerite, and pyrrhotite oxidation. Chalcopyrite yielded the highest (73 kJ/mol) and pyrrhotite yielded the lowest (25 kJ/mol) activation energies. Especially with pyrrhotite, diffusion contributed to rate limitation. Arrhenius plots were also linear for the reciprocals of lag periods and for increases of redox potentials (dmV/dt). Mass balance analysis based on total S in leach residue was in agreement with the highest rate of leaching at 37 and 28 degrees C. The presence of elemental S in leach residues was attributed to pyrrhotite oxidation.
Ahonen
L
L
Department of Microbiology, University of Helsinki, SF-00710 Helsinki, Finland, and Department of Microbiology, The Ohio State University, 484 West 12th Avenue, Columbus, Ohio 43210-1292.
Tuovinen
O H
OH