Single-walled carbon nanotube growth using [Fe(3)(mu(3)-O)(mu-O(2)CR)(6)(L)(3)](n+) complexes as catalyst precursors.
We present herein the VLS growth of SWNTs from oxo-hexacarboxylate-triron precursors, [Fe(3)O(O(2)CCH(3))(6)(EtOH)(3)] and [Fe(3)O(O(2)CCH(2)OMe)(6)(H(2)O)(3)][FeCl(4)], on spin-on-glass surfaces, using C(2)H(4)/H(2) (750 degrees C) and CH(4)/H(2) (800 and 900 degrees C) growth conditions. The SWNTs have been characterized by AFM, SEM and Raman spectroscopy. The characteristics of the SWNTs are found to be independent of the identity of the precursor complex or the solvent from which it is spin-coated. The as grown SWNTs show a low level of side-wall defects and have an average diameter of 1.2-1.4 nm with a narrow distribution of diameters. At 750 and 800 degrees C the SWNTs are grown with a range of lengths (300 nm-9 microm), but at 900 degrees C only the longer SWNTs are observed (6-8 microm). The yield of SWNTs per unit area of catalyst nanoparticle decreases with the growth temperature. We have demonstrated that spin coating of molecular precursors allows for the formation of catalyst nanoparticles suitable for growth of SWNTs with a high degree of uniformity in the diameter, without the formation of preformed clusters of a set diameter.
Ogrin
Douglas
D
Department of Chemistry and Center for Nanoscale Science and Technology, Rice University, Houston, Texas 77005, USA.
Colorado
Ramon
R
Maruyama
Benji
B
Pender
Mark J
MJ
Smalley
Richard E
RE
Barron
Andrew R
AR