Adsolubilization of 2-naphthol into adsorbed layer of PEO-PPO-PEO triblock copolymers on hydrophilic silica.
Adsolubilization of 2-naphthol into an adsorbed layer of poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) triblock copolymers (Pluronics) on hydrophilic silica has been investigated. Four kinds of Pluronics (P103, P105, P123, and F108) were used in order to understand the effect of the hydrophobicity of surfactant on the adsolubilization. The order of the adsorption in the saturation level was found to be P123 approximately P103 > P105 >> F108, meaning that Pluronics with higher hydrophobicity can adsorb preferentially to the silica surface. Indeed, this order was parallel to the order of the adsolubilization amount of 2-naphthol. In the case of co-addition of the Pluronics and 2-naphthol, the adsolubilization amount increased gradually at lower surfactant concentration regions, reached a maximum, and then decreased with increasing concentration of the Pluronics. The maximum amount appeared at critical polymolecular micelle concentration of each Pluronics. On the other hand, the final decrement was not observed when 2-naphthol was added after replacement of the Pluronics supernatant by the Pluronics free solution. These results suggest that adsolubilization behavior is influenced by the existence of the polymolecular micellar aggregates in the solution phase.
Tsurumi
Daisuke
D
Department of Applied Chemistry, Faculty of Science, Tokyo University of Science, Kagurazaka, Shinjuku-ku, Tokyo 162-8601, Japan.
Yoshimura
Tomokazu
T
Esumi
Kunio
K