Low temperature properties of acetonitrile confined in MCM-41.
The effect of confinement on the phase changes and dynamics of acetonitrile in mesoporous MCM-41 was studied by use of adsorption, FT-IR, DSC, and quasi-elastic neutron scattering (QENS) measurements. Acetonitrile molecules in a monolayer interact strongly with surface hydroxyls to be registered and perturb the triple bond in the C[triple bond]N group. Adsorbed molecules above the monolayer through to the central part of the cylindrical pores are capillary condensed molecules (cc-acetonitrile), but they do not show the hysteresis loop in adsorption-desorption isotherms, i.e., second order capillary condensation. FT-IR measurements indicated that the condensed phase is very similar to the bulk liquid. The cc-acetonitrile freezes at temperatures that depend on the pore size of the MCM-41 down to 29.1 A (C14), below which it is not frozen. In addition, phase changes between alpha-type and beta-type acetonitriles were observed below the melting points. Application of the Gibbs-Thomson equation, assuming the unfrozen layer thickness to be 0.7 nm, gave the interface free energy differences between the interfaces, i.e., Deltagamma(l/alpha) = 22.4 mJ m(-2) for the liquid/pore surface (ps) and alpha-type/ps, and Deltagamma(alpha/beta) = 3.17 mJ m(-2) for alpha-type/ps and beta-type/ps, respectively. QENS experiments substantiate the differing behaviors of monolayer acetonitrile and cc-acetonitrile. The monolayer acetonitrile molecules are anchored so as not to translate. The two Lorentzian analysis of QENS spectra for cc-acetonitriles showed translational motion but markedly slowed. However, the activation energy for cc-acetonitrile in MCM-41 (C18) is 7.0 kJ mol(-1) compared to the bulk value of 12.7 kJ mol(-1). The relaxation times for tumbling rotational diffusion of cc-acetonitrile are similar to bulk values.
Kittaka
Shigeharu
S
Department of Chemistry, Faculty of Science, Okayama University of Science, 1-1 Ridaicho, Okayama 700-0005, Japan. kittaka@chem.ous.ac.jp
Iwashita
Takafumi
T
Serizawa
Akihiro
A
Kranishi
Miki
M
Takahara
Shuichi
S
Kuroda
Yasushige
Y
Mori
Toshinori
T
Yamaguchi
Toshio
T