Microtensile dentin bond strength of self-etching resins: effect of a hydrophobic layer.
In this study, the microtensile bond strength of resin composites to dentin was determined when hydrophilic self-etching resins were used with and without an additional layer of a more hydrophobic adhesive. Included were three single-step self-etching adhesives, Adper Prompt L-Pop (3M ESPE), iBond GI (Heraeus Kulzer, Inc) and Xeno III (Caulk/Dentsply), and as a negative control, UniFil Bond (GC America), a self-etching primer with a separate adhesive. Each product was evaluated using a hybrid resin composite from its respective manufacturer, and each was used as directed and then used with an added layer of a more hydrophobic resin from its respective manufacturer. Testing was performed after 72 hours using a "non-trimming" microtensile test at a crosshead speed of 0.6 mm/minute. When the products were used according to manufacturers' directions, iBond had a significantly higher bond strength to dentin than the other three products (p<0.001), which were not significantly different from each other. For the three self-etching adhesive systems, the addition of a layer of a more hydrophobic resin produced significantly higher bond strengths to dentin (p<0.001), while no significant effect was found for the self-etching primer (p=0.40). A significant interaction was found between the variables product and adhesive treatment. The TEM evaluation of Prompt L-Pop and iBond demonstrated reduced nanoleakage with the additional resin layer.
Brackett
William W
WW
Department of Oral Rehabilitation, School of Dentistry, Medical College of Georgia, Augusta, USA. wbrackett@mail.mcg.edu
Ito
Shuichi
S
Tay
Franklin R
FR
Haisch
Larry D
LD
Pashley
David H
DH
D003188:Composite Resins / Q000737:chemistry; D001840:Dental Bonding; D003763:Dental Leakage / Q000145:classification; D003804:Dentin / Q000648:ultrastructure*; D017220:Dentin-Bonding Agents / Q000737:chemistry*; D004852:Epoxy Compounds / Q000737:chemistry; D006801:Humans; D057927:Hydrophobic and Hydrophilic Interactions; D008422:Materials Testing; D008689:Methacrylates / Q000737:chemistry; D046529:Microscopy, Electron, Transmission; D019279:Resin Cements / Q000737:chemistry*; D013499:Surface Properties; D013718:Tensile Strength
D003188:Composite Resins; D017220:Dentin-Bonding Agents; D004852:Epoxy Compounds; D008689:Methacrylates; C408584:Prompt L-Pop; D019279:Resin Cements; C425844:Scotchbond Multi-Purpose Plus; C407604:Solid Bond; C407402:Unifil Bond; C487957:Xeno III; C477386:iBond