23Na, 29Si, and 13C MAS NMR investigation of glass-forming reactions between Na2CO3 and SiO2.
The glass-forming reactions between sodium carbonate (Na2CO3) and silica (SiO2) have been investigated by 23Na, 29Si, and 13C magic-angle spinning (MAS) NMR spectroscopy. The multinuclear MAS NMR approach identifies and quantifies reaction products and intermediates, both glassy and crystalline. A series of powdered batches of initial composition Na2CO3.xSiO2 (x = 1, 2) corresponding to a sodium metasilicate (Na2SiO3) and sodium disilicate (Na2Si2O5) stoichiometry were investigated after periods of isothermal and nonisothermal heat treatments at different temperatures. Analysis of the 23Na quadrupolar coupling parameters has identified the early reaction product in all cases as crystalline Na2SiO3. In the nonisothermal experiment, this reaction is preceded by an early silica-rich melt phase formed around 850 degrees C. The early reactions are controlled by solid-state Na+ diffusion across the reaction zone in the grain interface layer. Crystalline Na2SiO3 precipitates in the interface layer, increasing its thickness between the Na2CO3 and the SiO2 grains and slowing down the rate of Na+ migration. This creates a secondary phase, which is temperature dependent. At low temperatures, where Na+ migration is impaired, the production of Na2SiO3 ceases and silica-richer phases are precipitated. In the case of the sodium disilicate batch, where excess SiO2 is present, a secondary reaction of Na2SiO3 with SiO2 forming a glassy phase is observed. A transient carbon-bearing phase has been identified by 13C NMR as a NaCO3- complex loosely bound to bridging oxygens in the silicate network at the SiO2 grain surface.
Jones
Aled R
AR
Materials Physics, University of Wales Aberystwyth, Penglais, Aberystwyth SY233BZ, Wales, United Kingdom.
Winter
Rudolf
R
Greaves
G Neville
GN
Smith
Ian H
IH