Roles of surface Te, Nb, and Sb oxides in propane oxidation to acrylic acid over bulk orthorhombic Mo-V-O phase.
The outermost surfaces and subsurface layers of the orthorhombic (M1) Mo-V-O catalysts promoted with Te, Nb, and Sb oxide species at submonolayer surface coverage were examined by low-energy ion scattering (LEIS). This study indicated that the Nb oxide species was preferentially located at the topmost surface, while the subsurface Te and Sb concentrations declined gradually into the bulk. Although the original Mo-V-O catalyst was essentially unselective in propane oxidation to acrylic acid, significant improvement in the selectivity to acrylic acid was observed when Te, Nb, and Sb oxides were present as the surface species at submonolayer coverage. These findings further suggested that the formation of the surface V-O-M bonds (M = Nb, Te, or Sb) was highly beneficial for both the activity and selectivity of the orthorhombic Mo-V-O catalysts in propane oxidation to acrylic acid. The highest selectivity was observed when both Nb and Te (or Sb) oxide species were present at the surface. The selectivity trends established for the surface-promoted Mo-V-O catalyst parallel those found previously for the corresponding bulk Mo-V-M-O catalysts. These results further indicated that the introduction of surface metal oxide species is a highly promising method to prepare well-defined model catalysts for studies of the structure-activity/selectivity relationships as well as optimize the catalytic performance of the bulk mixed Mo-V-M-O catalysts for selective (amm)oxidation of propane.
Guliants
Vadim V
VV
Department of Chemical and Material Engineering, University of Cincinnati, Cincinnati, Ohio 45221-0012, USA. vadim.guliants@uc.edu
Bhandari
Rishabh
R
Swaminathan
Balasubramanian
B
Vasudevan
Vijay K
VK
Brongersma
Hidde H
HH
Knoester
Arie
A
Gaffney
Anne M
AM
Han
Scott
S