Cyclic fatigue of three types of rotary nickel-titanium files in a dynamic model.
The cyclic fatigue resistance of three types of nickel-titanium rotary files was compared in a model using reciprocating axial movement. The influence of file size and taper was also investigated and fracture patterns were examined under SEM. The 10 experimental groups consisted of ProFiles, K3s, and RaCe files, size 25 in .04 and .06 tapers, as well as ProFiles and K3s, size 40 in .04 and .06 tapers. Each file was rotated freely at 300 rpm inside a stainless steel tube with a 60 degree and 5 mm radius of curvature. A continuous 3 mm oscillating axial motion was applied at 1 cycle per second by attaching an electric dental handpiece to the most inferior load cell of an Instron machine using a custom-made jig. The number of rotations to failure was determined and analyzed using analysis of variance and Tukey's post hoc tests. Overall, K3 25/.04 files were significantly more resistant to cyclic fatigue compared to any other group in this study. In the 25/.04 category, K3s were significantly more resistant to failure than ProFiles and RaCe files. Also in the same category, ProFiles significantly outlasted RaCe files. In the 25/.06 group, K3s and ProFiles were significantly more resistant to failure than RaCe files, but K3s were not significantly different than ProFiles. In the 40/.04 and 40/.06 groups, K3s were significantly more resistant to cyclic fatigue than ProFiles. SEM observations demonstrated mostly a ductile mode of fracture. The results suggest that different cross-sectional designs, diameters, and tapers all contribute to a nickel-titanium instrument's vulnerability to cyclic failure.
Yao
James H
JH
US Air Force Endodontics Residency Program, Wilford Hall Medical Center, San Antonio, TX, USA.
Schwartz
Scott A
SA
Beeson
Thomas J
TJ
D000704:Analysis of Variance; D003722:Dental Alloys; D003762:Dental Instruments; D003799:Dental Stress Analysis; D004867:Equipment Design; D004868:Equipment Failure; D008855:Microscopy, Electron, Scanning; D003765:Models, Dental; D009532:Nickel; D018915:Root Canal Preparation / Q000295:instrumentation*; D018709:Statistics, Nonparametric; D014025:Titanium
D003722:Dental Alloys; C040654:titanium nickelide; D009532:Nickel; D014025:Titanium