Spectroscopic characterization of zinc oxide nanorods synthesized by solid-state reaction.
Well-crystallized zinc oxide nanorods have been fabricated by single step solid-state reaction using zinc acetate and sodium hydroxide, at room temperature. The sodium lauryl sulfate (SLS) stabilized zinc oxide nanorods were characterized by using X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy and photoluminescence spectroscopy. The X-ray diffraction revealed the wurtzite structure of zinc oxide. The size estimation by XRD and TEM confirmed that the ZnO nanorods are made of single crystals. The growth of zinc oxide crystals into rod shape was found to be closely related to its hexagonal nature. The mass ratio of SLS:ZnO in the nanorods was found to be 1:10 based on the thermogravimetric analysis. Blue shift of photoluminescence emission was noticed in the ZnO nanorods when compared to that of ZnO bulk. FT-IR analysis confirmed the binding of SLS with ZnO nanorods. Apart from ease of preparation, this method has the advantage of eco-friendliness since the solvent and other harmful chemicals were eliminated in the synthesis protocol.
Prasad
Virendra
V
Nanotechnology Research Group, Central Institute for Research on Cotton Technology, Adenwala Road, Matunga, Mumbai-400 019, India.
D'Souza
Charlene
C
Yadav
Deepti
D
Shaikh
A J
AJ
Vigneshwaran
Nadanathangam
N
D008422:Materials Testing; D046529:Microscopy, Electron, Transmission; D043942:Nanotubes / Q000737:chemistry*; D013053:Spectrophotometry; D013056:Spectrophotometry, Ultraviolet; D017550:Spectroscopy, Fourier Transform Infrared; D013818:Thermogravimetry; D014961:X-Ray Diffraction; D015034:Zinc Oxide / Q000737:chemistry*
D015034:Zinc Oxide