Fibronectin immobilization using water-soluble carbodiimide on poly-L-lactic acid for enhancing initial fibroblast attachment.
The aim of this study is to evaluate the influence of fibronectin immobilization on poly-L-lactic acid (PLA) films on the initial attachment of human gingival fibroblasts. Carboxylic acid groups are chemically introduced on the PLA films' surface by surface hydrolysis with 0.5 M NaOH. The contact angle of PLA surface with respect to double-distilled water decreases significantly after NaOH hydrolysis. X-ray photoelectron spectroscopy (XPS) also reveals significantly higher intensities of C(C=O)/C(C-O) after NaOH hydrolysis. Fibronectin is immobilized onto the hydrolyzed PLA surface through a condensation reaction between the carboxylic acid groups on the hydrolyzed PLA surface and the amino groups of fibronectin using water-soluble carbodiimide. XPS analysis shows that the fibronectin-immobilized PLA surface is enriched with nitrogen atoms. The immobilization of fibronectin significantly enhances the number of initially attached human gingival fibroblasts on the PLA surface. No obvious differences in morphology are noted between fibroblasts cultured on native PLA and on fibronectin-immobilized PLA. Fibronectin can be immobilized onto the PLA surface after NaOH hydrolysis and this is effective in enhancing the initial attachment of human gingival fibroblasts.
Nagai
Megumi
M
Department of Laboratory Medicine for Dentistry, Nihon University School of Dentistry at Matsudo 2-870-1, Sakaecho Nishi, Matsudo, Chiba 271-8587, Japan. m-nagai@mascat.nihon-u.ac.jp
Hayakawa
Tohru
T
Makimura
Masaharu
M
Yoshinari
Masao
M
D000327:Adsorption; D001665:Binding Sites; D002448:Cell Adhesion / Q000187:drug effects*; D002478:Cells, Cultured; D020099:Coated Materials, Biocompatible / Q000737:chemistry* / Q000494:pharmacology*; D005347:Fibroblasts / Q000166:cytology* / Q000187:drug effects* / Q000502:physiology*; D006801:Humans; D019344:Lactic Acid / Q000737:chemistry*; D008422:Materials Testing; D011091:Polyesters; D011108:Polymers / Q000737:chemistry*; D011485:Protein Binding; D023822:Tissue Engineering / Q000379:methods
D020099:Coated Materials, Biocompatible; D011091:Polyesters; D011108:Polymers; D019344:Lactic Acid; C033616:poly(lactide)