Two confined phases of argon adsorbed inside open single walled carbon nanotubes.
Isothermal adsorption of Ar on single walled carbon nanotubes (SWNTs) has been studied at 77 and 87 K. The SWNTs have been grown by laser vaporization of a graphite pellet containing 0.6% (atomic) Ni/Co catalyst. The nanotubes have been prepared for argon adsorption measurements by prolonged outgassing of as-grown material in a vacuum at room temperature (295 K), at elevated temperatures of up to 475 K, and by oxidization for 2 h in dry air at 470 K. Formation of two condensed phases of Ar in the interior of SWNTs has been observed at 77 K. The low-density phase is formed at 155(5) microTorr, while the high-density phase, at 120(5) microTorr. At 87 K, only a single phase has been observed at 185(5) microTorr. Condensation at both 77 and 87 K appears to be the first-order phase transition. Onset of the quasi-one-dimensional linear (one-channel) phase and the quasi-two-dimensional monolayer (six-channel) phase formation on the external surface of bundles has been observed at 77 K near 0.0017 and 0.8 Torr, respectively, and at 87 K near 0.018 and 5 Torr, respectively. Isosteric heats of adsorption for the one-channel phase, the first external layer, and the second external layer have been determined to be equal to 137, 107, and 70 meV, respectively.
Jakubek
Zygmunt J
ZJ
Steacie Institute for Molecular Sciences, National Research Council of Canada, 100 Sussex Drive, Ottawa, Ontario K1A 0R6, Canada.
Simard
Benoit
B
D000327:Adsorption; D001128:Argon / Q000737:chemistry*; D020650:Combinatorial Chemistry Techniques / Q000379:methods*; D037742:Nanotubes, Carbon / Q000737:chemistry*; D013499:Surface Properties; D013696:Temperature; D013816:Thermodynamics
D037742:Nanotubes, Carbon; D001128:Argon