Dynamic void behavior in polymerizing polymethyl methacrylate cement.
Cement mantle voids remain controversial with respect to survival of total hip arthroplasty. Void evolution is poorly understood, and attempts at void manipulation can only be empirical. We induced voids in a cement model simulating the constraints of the proximal femur. Intravoid pressure and temperature were recorded throughout polymerization, and the initial and final void volumes were measured. Temperature-dependent peak intravoid pressures and void volume increases were observed. After solidification, subatmospheric intravoid pressures were observed. The magnitude of these observations could not be explained by the ideal gas law. Partial pressures of the void gas at peak pressures demonstrated a dominant effect of gaseous monomer, thereby suggesting that void growth is a pressure-driven phenomenon resulting from temperature-dependent evaporation of monomer into existing trapped air voids.
Muller
Scott D
SD
Department of Trauma and Orthopaedic Surgery, The Medical School, The University of Newcastle upon Tyne, Framlington Place, Newcastle upon Tyne, UK.
McCaskie
Andrew W
AW
D000388:Air; D001843:Bone Cements / Q000138:chemical synthesis / Q000737:chemistry*; D055585:Physical Phenomena; D010825:Physics; D019904:Polymethyl Methacrylate / Q000138:chemical synthesis / Q000737:chemistry*
D001843:Bone Cements; D019904:Polymethyl Methacrylate