Electrospun three-dimensional hyaluronic acid nanofibrous scaffolds.
A three-dimensional (3D) hyaluronic acid (HA) nanofibrous scaffold was successfully fabricated to mimic the architecture of natural extracellular matrix (ECM) based on electrospinning. Thiolated HA derivative, 3,3'-dithiobis(propanoic dihydrazide)-modified HA (HA-DTPH), was synthesized and electrospun to form 3D nanofibrous scaffolds. In order to facilitate the fiber formation during electrospinning, Poly (ethylene oxide) (PEO) was added into the aqueous solution of HA-DTPH at an optimal weight ratio of 1:1. The electrospun HA-DTPH/PEO blend scaffold was subsequently cross-linked through poly (ethylene glycol)-diacrylate (PEGDA) mediated conjugate addition. PEO was then extracted in DI water to obtain an electrospun HA-DTPH nanofibrous scaffold. NIH 3T3 fibroblasts were seeded on fibronectin-adsorbed HA-DTPH nanofibrous scaffolds for 24h in vitro. Fluorescence microscopy and laser scanning confocal microscopy revealed that the 3T3 fibroblasts attached to the scaffold and spread, demonstrating an extended dendritic morphology within the scaffold, which suggests potential applications of HA-DTPH nanofibrous scaffolds in cell encapsulation and tissue regeneration.
Ji
Yuan
Y
Department of Materials Science and Engineering, SUNY at Stony Brook, Stony Brook, NY 11794-2275, USA.
Ghosh
Kaustabh
K
Shu
Xiao Zheng
XZ
Li
Bingquan
B
Sokolov
Jonathan C
JC
Prestwich
Glenn D
GD
Clark
Richard A F
RA
Rafailovich
Miriam H
MH
D000818:Animals; D001672:Biocompatible Materials / Q000737:chemistry; D048430:Cell Shape; D004563:Electrochemistry / Q000295:instrumentation / Q000379:methods; D005027:Ethylene Oxide / Q000737:chemistry; D005109:Extracellular Matrix / Q000737:chemistry / Q000648:ultrastructure; D005583:Fourier Analysis; D006820:Hyaluronic Acid / Q000737:chemistry / Q000648:ultrastructure; D008422:Materials Testing; D051379:Mice; D015394:Molecular Structure; D008970:Molecular Weight; D041681:NIH 3T3 Cells; D049329:Nanostructures / Q000737:chemistry / Q000648:ultrastructure; D011092:Polyethylene Glycols / Q000737:chemistry; D011108:Polymers / Q000737:chemistry*; D016062:Porosity; D023822:Tissue Engineering / Q000379:methods
D001672:Biocompatible Materials; D011108:Polymers; C437167:poly(ethylene glycol)diacrylate; D011092:Polyethylene Glycols; D006820:Hyaluronic Acid; D005027:Ethylene Oxide