Formation of hydroxyapatite-layer on glass plate and its removal-regeneration properties for aqueous cadmium.
A glass plate was coated with calcium hydroxyapatite (CaHAp) by a dip-coating method and employed for the removal of aqueous cadmium. Sol obtained from alcoholic solution of (NH(4))(2)HPO(4) and Ca(NO(3))(2) x 4H(2)O was employed for the precursor of the CaHAp layer. The preparation of CaHAp from the sol needed a rather low calcination temperature of 573 K and the resulting solid mainly contained CaHAp. It was shown that the glass plate coated with CaHAp with the sol could be employed for the removal of aqueous cadmium. Furthermore, it was found that cadmium immobilized on the coated plate could be regenerated into weak acidic solution. A dissolution-precipitation mechanism was suggested for the removal-regeneration of aqueous cadmium.
Department of Chemical Science and Technology, Faculty of Engineering, The University of Tokushima, Minamijosanjima, Tokushima 770-8506, Japan. sugiyama@chem.tokushima-u.ac.jp
Shigeru
S
Sugiyama
Kazuya
K
Fukuta
Ken-Ichiro
K
Sotowa