Ultralow temperature synthesis of ordered hexagonal smaller supermicroporous silica using semifluorinated surfactants as template.
Ordered hexagonal smaller supermicroporous silica (JLU-14L and JLU-11L) has been successfully synthesized at ultralow temperature (0 approximately -20 degrees C) by semifluorinated surfactants, which is extensively investigated by X-ray diffraction, N2 adsorption, and transmission electron microscopy. X-ray diffraction shows that the peak intensity of the samples increases with decreasing synthesis temperatures in the range of 0 approximately -20 degrees C, indicating that the ordering of porous silica improves with decreasing synthesis temperature. N2 adsorption/ desorption isotherms show that JLU-14L has both ordered smaller hexagonal supermicropores (1.27 and 1.28 nm) and disordered micropores (0.67 nm). Such hierarchically porous materials with micro/supermicroporosity should be potentially important for fast diffusion of reactants and products in catalytic reactions. The ultralow temperature synthesis is a crucial factor for the formation of ordered smaller supermicropores and the control of microporosity in JLU-14L.
Di
Yan
Y
State Key Laboratory of Inorganic Synthesis and Preparative Chemistry and Department of Chemistry, Jilin University, Changchun 130012, PR China.
Meng
Xiangju
X
Wang
Lifeng
L
Li
Shougui
S
Xiao
Feng-Shou
FS
D000327:Adsorption; D003080:Cold Temperature; D006845:Hydrocarbons, Fluorinated / Q000737:chemistry*; D009584:Nitrogen / Q000737:chemistry; D016062:Porosity; D012822:Silicon Dioxide / Q000138:chemical synthesis* / Q000737:chemistry; D013501:Surface-Active Agents / Q000737:chemistry*
D006845:Hydrocarbons, Fluorinated; D013501:Surface-Active Agents; D012822:Silicon Dioxide; D009584:Nitrogen