MnO2-embedded-in-mesoporous-carbon-wall structure for use as electrochemical capacitors.
We present an in situ reduction method to synthesize a novel structured MnO(2)/mesoporous carbon (MnC) composite. MnO(2) nanoparticles have been synthesized and embedded into the mesoporous carbon wall of CMK-3 materials by the redox reaction between permanganate ions and carbons. Thermogravimetric analysis (TG), X-ray photoelectron spectrum (XPS), X-ray diffraction (XRD), nitrogen sorption, transmission electron microscopy (TEM), and cyclic voltammetry were employed to characterize these composite materials. The results show that different MnO(2) contents could be introduced into the pores of CMK-3 treated with different concentrations of potassium permanganate aqueous solution, while retaining the ordered mesostructure and larger surface area. Increasing the MnO(2) content did not result in a decrease in pore size from the data of nitrogen sorption isotherms, indicating that MnO(2) nanoparticles are embedded in the pore wall, as evidenced by TEM observation. We obtained a large specific capacitance over 200 F/g for the MnC composite and 600 F/g for the MnO(2), and these materials have high electrochemical stability and high reversibility.
Dong
Xiaoping
X
State Key Laboratory of High Performance Ceramics and Superfine Microstructures, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 20005095, People's Republic of China.
Shen
Weihua
W
Gu
Jinlou
J
Xiong
Liangmin
L
Zhu
Yufang
Y
Li
Hua
H
Shi
Jianlin
J