Novel core-shell-structured Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 via coprecipitation as positive electrode material for lithium secondary batteries.
We have successfully synthesized a spherical core-shell structure based on Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 via a coprecipitation route. According to the careful examination by scanning electron microscopy (SEM), transmission electron microscopy energy-dispersive spectroscopy (TEM-EDS), and X-ray diffraction (XRD), it was found that the core-shell particle consisted of Li[Ni0.8Co0.2]O2 as the core and Li[Ni0.5Mn0.5]O2 as the shell, of which the thickness was estimated to be 1 to approximately 1.5 microm. Both the core and shell were dense as confirmed by SEM. Though the core-shell-structured Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 delivered a slightly reduced initial discharge capacity, the capacity retention and thermal stability were significantly improved relative to those of the Li[Ni0.8Co0.2]O2 electrode without the Li[Ni0.5Mn0.5]O2 shell. The carbon/Li[Ni0.8Co0.2]O2 pouch cell underwent an explosive ignition during the nail penetration test, whereas the carbon/Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 cell remained stable, demonstrating the superior thermal stability of the core-shell electrode. As a new positive electrode material, the core-shell-structured Li[(Ni0.8Co0.2)0.8(Ni0.5Mn0.5)0.2]O2 is a significant breakthrough in the development of high-capacity lithium secondary batteries.
Center for Information and Communication Materials, Department of Chemical Engineering, Hanyang University, Seoul 133-791, Korea.
Yang-Kook
YK
Sun
Seung-Taek
ST
Myung
Ho-Suk
HS
Shin
Young Chan
YC
Bae
Chong Seung
CS
Yoon