Synthesis of polymer latex particles decorated with organically-modified laponite clay platelets via emulsion polymerization.
We report a new route to colloidal nanocomposites consisting of polymer latex particles covered with Laponite clay nanoplatelets. These composite particles are prepared by seeded emulsion (co)polymerization of styrene and butyl acrylate from Laponite clay suspensions previously functionalized by ion exchange using either a free radical initiator: 2,2-azobis (2-methylpropionamidine) hydrochloride (AIBA) or a cationic vinyl monomer: 2-(methacryloyloxy) ethyl trimethyl ammonium chloride (MADQUAT). The successful intercalation of the cationic reactive molecules was confirmed by elemental analysis, FTIR, 13C solid-state NMR and WAXD. The organically-modified clays were dispersed into water with the help of tetrasodium pyrophosphate and an anionic surfactant. stable latexes, produced under different experimental conditions, were successfully obtained from the clay suspensions. Cryo-TEM images of the resulting latexes showed spherical composite particles with diameters in the 50-250 nm range with clay sheets located on their surface. This paper reports on the effect of the processing conditions on the particle morphology and latex stability, and describes the mechanism of formation of the nanocomposite particles.
Laboratoire de Chimie et Procédés de Polymérisation - CNRS/CPE, Bat. F 308, 43 Bd du 11 Novembre 1918, BP 2177, 69616 Villeurbanne Cedex, France.
Norma Negrete
NN
Herrera
Stéphanie
S
Persoz
Jean-Luc
JL
Putaux
Laurent
L
David
Elodie
E
Bourgeat-Lami
D000538:Aluminum Silicates / Q000737:chemistry*; D000077215:Clay; D020285:Cryoelectron Microscopy; D004655:Emulsions; D007840:Latex / Q000138:chemical synthesis*; D046529:Microscopy, Electron, Transmission; D011108:Polymers / Q000138:chemical synthesis*
D000538:Aluminum Silicates; D004655:Emulsions; D007840:Latex; D011108:Polymers; D000077215:Clay