Removal of arsenite and arsenate using hydrous ferric oxide incorporated into naturally occurring porous diatomite.
In this study, a simplified and effective method was tried to immobilize iron oxide onto a naturally occurring porous diatomite. Experimental resultsfor several physicochemical properties and arsenic edges revealed that iron oxide incorporated into diatomite was amorphous hydrous ferric oxide (HFO). Sorption trends of Fe (25%)-diatomite for both arsenite and arsenate were similar to those of HFO, reported by Dixit and Hering (Environ. Sci. Technol. 2003, 37, 4182-4189). The pH at which arsenite and arsenate are equally sorbed was 7.5, which corresponds to the value reported for HFO. Judging from the number of moles of iron incorporated into diatomite, the arsenic sorption capacities of Fe (25%)-diatomite were comparable to or higher than those of the reference HFO. Furthermore, the surface complexation modeling showed that the constants of [triple bond]SHAsO4- or [triple bond]SAsO4(2-) species for Fe (25%)-diatomite were larger than those reference values for HFO or goethite. Larger differences in constants of arsenate surface species might be attributed to aluminum hydroxyl ([triple bond]Al-OH) groups that can work better for arsenate removal. The pH-controlled differential column batch reactor (DCBR) and small-scale column tests demonstrated that Fe (25%)-diatomite had high sorption speeds and high sorption capacities compared to those of a conventional sorbent (AAFS-50) that is known to be the first preference for arsenic removal performance in Bangladesh. These results could be explained by the fact that Fe (25%)-diatomite contained well-dispersed HFO having a great affinity for arsenic species and well-developed macropores as shown by scanning electron microscopy (SEM) and pore size distribution (PSD) analyses.
Jang
Min
M
Department of Civil and Environmental Engineering, University of Wisconsin-Madison, 1415 Engineering Drive, Madison, Wisconsin 53706, USA. muj11@psu.edu
Min
Soo-Hong
SH
Kim
Tak-Hyun
TH
Park
Jae Kwang
JK
D001149:Arsenates / Q000302:isolation & purification*; D018053:Arsenites / Q000302:isolation & purification*; D005290:Ferric Compounds / Q000737:chemistry*; D006863:Hydrogen-Ion Concentration; D007700:Kinetics; D008855:Microscopy, Electron, Scanning; D009584:Nitrogen / Q000737:chemistry; D014961:X-Ray Diffraction
D001149:Arsenates; D018053:Arsenites; D005290:Ferric Compounds; C000499:ferric oxide; C015001:arsenite; D009584:Nitrogen; C025657:arsenic acid