Synthesis and photoluminescence of Y2O3:RE3+ (RE=Eu, Tb, Dy) porous nanotubes templated by carbon nanotubes.
Y2O3:RE3+(RE=Eu, Tb, Dy) porous nanotubes were first synthesized using carbon nanotubes as template. The morphology of the coated precursors and porous Y2O3:Eu3+ nanotubes was determined by scanning electron Microscopy (SEM) and transmission electron microscopy (TEM). It was found that the coating of precursors on carbon nanotubes (CNTs) is continuous and the thickness is about 15 nm, after calcinated, the Y2O3:Eu3+ nanotubes are porous with the diameter size in the range of 50-80 nm and the length in micrometer scale. X-ray diffraction (XRD) patterns confirmed that the samples are cubic phase Y2O3 and the photoluminescence studies showed that the porous rare earth ions doped nanotubes possess characteristic emission of Eu3+, Tb3+, and Dy3+. This method may also provide a novel approach to produce other inorganic porous nanotubes used in catalyst and sensors.
Key Laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, PR China.
Guixia
G
Liu
Guangyan
G
Hong
D004419:Dysprosium / Q000737:chemistry*; D005063:Europium / Q000737:chemistry*; D049449:Luminescence; D008854:Microscopy, Electron; D008855:Microscopy, Electron, Scanning; D049329:Nanostructures / Q000737:chemistry; D010087:Oxides / Q000737:chemistry; D010777:Photochemistry; D013816:Thermodynamics; D013910:Thorium / Q000737:chemistry*; D014961:X-Ray Diffraction; D015018:Ytterbium / Q000737:chemistry*
D010087:Oxides; D004419:Dysprosium; D005063:Europium; D013910:Thorium; D015018:Ytterbium