Heat transfer of impression plasters to an implant-bone interface.
OBJECTIVE
The purpose of this in vitro study was to measure heat generated at the implant-bone interface caused by exothermic setting reaction of 2 impression plasters.


METHODS
The study consisted of 20 titanium-alloy abutment impressions connected to a titanium-alloy cylindrical implant embedded in an acrylic-resin mandible in a 37 degrees C water bath. There were 2 types of impression plaster used, Snow-White (Kerr, Romulus, MI) and Xantano (Kulzer, Dormagen, Germany). Temperature changes were recorded via embedded thermocouples at the cervix and implant surface apex. Analysis of variance for repeated measures was used to compare 2 treatment groups.


RESULTS
Temperature increased less at the implant apex (1.5 degrees-2.1 degrees C) than at the implant cervix (7.4 degrees-10.5 degrees C). Differences between the 2 impression plasters were statisticallysignificant only at the implant cervical level (P < 0.05). A lower temperature increase was shown with the Snow-White compared with the Xantano. Although both plasters generated an exothermic reaction on setting (mean temperature change 22 degrees C), the increase in the temperature rate of the Snow-White was slower than the Xantano.


CONCLUSIONS
Under the conditions of the present study, Snow-White impression plaster appears to be safer to use in implant prosthodontics compared with the Xantano because of its slower and lower exothermic reaction at the implant-bone interface. However, use of the material with the rapid setting time would require more care, such as limiting the volume of material used (e.g., by using a custom tray).
Nissan
Joseph
J
Department of Prosthetic Dentistry, The Maurice and Gabriela Goldschleger School of Dental Medicine, Tel Aviv University, Tel Aviv, Israel. nissandr@post.tau.ac.il
Gross
Martin
M
Ormianer
Zeev
Z
Barnea
Eitan
E
Assif
David
D
D000180:Acrylic Resins / Q000737:chemistry; D002133:Calcium Sulfate / Q000737:chemistry*; D003722:Dental Alloys / Q000737:chemistry; D015921:Dental Implants; D003760:Dental Impression Materials / Q000737:chemistry*; D017267:Dental Prosthesis Design; D004735:Energy Transfer; D006358:Hot Temperature; D006801:Humans; D008334:Mandible / Q000502:physiology*; D008422:Materials Testing; D008953:Models, Anatomic; D013499:Surface Properties; D013816:Thermodynamics; D013821:Thermometers; D014025:Titanium / Q000737:chemistry
D000180:Acrylic Resins; D003722:Dental Alloys; D015921:Dental Implants; D003760:Dental Impression Materials; D014025:Titanium; D002133:Calcium Sulfate