Polyethylene/clay nanocomposites prepared by polymerization compounding method.
A new technique for the preparation of high density polyethylene/clay nanocomposite, "polymerization compounding," is reported. This technique was based on the chemical anchoring of a Ziegler-Natta catalyst on organically modified clay surface containing an ammonium cation bearing primary hydroxyl groups. The polymerization of ethylene was initiated after adequate activation and the growing polyethylene chains are directly adsorbed on to the clay surface through the hydroxyl-functionalized surfactant. Finally, the nanocomposite was prepared by diluting polyethylene adsorbed clay in the high density polyethylene (HDPE) matrix using a batch mixer at 180 degrees C. The as-synthesized nanocomposite was typically characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM) that revealed the formation of intercalated nanocomposite. Tensile property measurements exhibit substantial increase in stiffness (approximately 50%) and strength (approximately 20%) of nanocomposite as compared to that of neat HDPE. Dynamic mechanical analysis under molten state revealed 25% increase in storage modulus when compared to that of neat HDPE.
Department of Chemical Engineering, Laval University, Sainte-Foy, Quebec GIK 7P4, Canada.
Asmaa
A
Gaboune
Suprakas Sinha
SS
Ray
Abdellatif
A
Ait-Kadi
Bernard
B
Riedl
Mosto
M
Bousmina
D000538:Aluminum Silicates / Q000737:chemistry*; D000077215:Clay; D046529:Microscopy, Electron, Transmission; D036103:Nanotechnology; D020959:Polyethylene / Q000737:chemistry*; D011108:Polymers / Q000737:chemistry*; D014961:X-Ray Diffraction
D000538:Aluminum Silicates; D011108:Polymers; D020959:Polyethylene; D000077215:Clay