Photocatalytic decomposition of an alkylammonium cation in a Langmuir-Blodgett film of a titania nanosheet.
The formation of inorganic-organic hybrid films of a titania nanosheet and an amphiphilic alkylammonium cation has been investigated, and the photocatalytic decomposition of the alkylammonium cation in the film has been pursued. When a solution of the amphiphilic alkylammonium salt (octadecylammonium chloride: ODAH+ Cl-) was spread on an interface between the air and a titania nanosheet suspension, the negatively charged nanosheets were adsorbed onto the floating monolayer of ODAH+ to form a hybrid monolayer. The hybridization was confirmed by pi-A isotherm measurements, atomic force microscopy, and X-ray photoelectron spectroscopy. Multilayered films were fabricated in a layer-by-layer way by transferring the hybrid monolayers onto glass plates. Areas per ODAH+ cation in the films were estimated from the infrared (IR) spectra of the films, but these areas were smaller than those estimated from the pi-A isotherm curves. The orientation of the alkyl chain of ODAH+ in the hybrid film was determined by means of polarized IR spectroscopy. The alkyl chains were tilted 41 +/- 1 degrees and 47 +/- 1 degrees from the surface normal for the films prepared from the 8 and 20 ppm (ppm = mg dm(-3)) suspensions, respectively. Together with X-ray diffraction data of the films, the structure of the hybrid film was discussed. When the films were illuminated with a UV light, the absorption intensities due to the alkyl chain of ODAH+ decreased exponentially, indicating the photocatalytic decomposition of ODAH+ by the titania nanosheets in the films. Deviation from the exponential trend in the decomposition rate was observed in the initial period for the hybrid films prepared from the suspensions at low concentrations. Interestingly, the layered structure of the hybrid film was disturbed significantly after the ODAH+ cations were decomposed.
Department of Applied Chemistry, National Defense Academy, Yokosuka, Kanagawa 239-8686, Japan. umemura@nda.ac.jp
Yasushi
Y
Umemura
Emi
E
Shinohara
Akihiro
A
Koura
Terumichi
T
Nishioka
Takayoshi
T
Sasaki