Self-etching bonding systems: in-vitro shear bond strength evaluation.
The purpose of this in vitro study was to compare the dentine shear bond strength of five self-etching bonding agents with that of a total-etch dentine bonding agent (used as control). Sixty recently extracted third molar teeth were mounted in acrylic resin and the occlusal surfaces ground to expose superficial dentine. A standardised smear layer was created by polishing with wet 600-grit SiC paper. Products evaluated were Xeno III (XIII), Clearfil SE Bond (SE), ABF (ABF), Optibond Solo Self-etch (OS), Adper Prompt-L-Pop (PLP) and the control, Scotchbond Multipurpose Plus (SBMP). Resin stubs were bonded to the dentine using the bonding agents according to manufacturer's instructions. Composite stubs were manufactured using an Ultradent jig and two increments of Z100, A1 shade composite. The bonds were subsequently stressed to failure with an Instron testing machine, operating at a crosshead speed of 0.5 mm/min. The data was statistically analysed using ANOVA (alpha < or = 0.05). The mean SBS (MPa) were: SBMP (Control) = 24.1 +/- 7.6; XIII = 17.3 +/- 4.1; SE = 26.2 +/- 7.8; ABF = 25.9 +/- 4.3; OS = 21.9 +/- 3.9 and PLP = 15.4 +/- 3.1. The shear bond strengths of both XIII and PLP to dentine were significantly lower than the control SBMP (p < 0.05). The remaining three products (SE, ABF and OS) displayed bond strengths comparable to the control (p > 0.05). Further research into cut (ground) and un-cut (un-ground) enamel shear bond strength and micro-leakage using these bonding agents are needed.
Brandt
P D
PD
Division of Dental Materials, School of Dentistry, University of Pretoria. pbrandt@medic.up.ac.za
de Wet
F A
FA
du Preez
I C
IC
D000704:Analysis of Variance; D001840:Dental Bonding / Q000379:methods*; D045662:Dental Etching / Q000379:methods*; D006801:Humans; D008964:Molar, Third; D033081:Shear Strength