Core-shell structured SiO2@YVO4:Dy3+/Sm3+ phosphor particles: sol-gel preparation and characterization.
Spherical SiO(2) particles have been coated with YVO(4):Dy(3+)/Sm(3+) phosphor layers by a Pechini sol-gel process, leading to the formation of core-shell structured SiO(2)@YVO(4):Dy(3+)/Sm(3+) particles. X-ray diffraction (XRD), Fourier-transform IR spectroscopy, field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting SiO(2)@YVO(4):Dy(3+)/Sm(3+) core-shell phosphors. The obtained core-shell phosphors have perfect spherical shape with narrow size distribution (average size ca. 300 nm), smooth surface and non-agglomeration. The thickness of shells could be easily controlled by changing the number of deposition cycles (20 nm for one deposition cycle). The core-shell particles show strong characteristic emission from Dy(3+) for SiO(2)@YVO(4):Dy(3+) and from Sm(3+) for SiO(2)@YVO(4):Sm(3+) due to an efficient energy transfer from YVO(4) host to them. The PL intensity of Dy(3+) and Sm(3+) increases with raising the annealing temperature and the number of coating cycles.
Wang
H
H
Key laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, PR China.
Yu
M
M
Lin
C K
CK
Lin
J
J
D005782:Gels; D049449:Luminescence; D008853:Microscopy; D015335:Molecular Probes / Q000138:chemical synthesis; D053758:Nanoparticles / Q000737:chemistry*; D012822:Silicon Dioxide / Q000737:chemistry*; D013057:Spectrum Analysis; D014961:X-Ray Diffraction; D015018:Ytterbium / Q000737:chemistry*
D005782:Gels; D015335:Molecular Probes; D012822:Silicon Dioxide; D015018:Ytterbium