Extending the time: solvothermal syntheses, crystal structures, and properties of two non-isostructural thioantimonates with the composition [Mn(tren)]Sb2S4.
The two novel compounds, [Mn(tren)]Sb2S4 (1 and 2), were obtained by the reaction of elemental Mn, Sb, and S in aqueous solutions of tren (tren = tris(2-aminoethyl)amine, C6H18N4) after different reaction times. Compound 1 is formed up to a reaction time of 13 d, and an extension of the reaction time leads to the formation of 2. Both compounds crystallize in monoclinic space groups (1, P2(1)/c; 2, C2/c). In 1, the two unique SbS3 trigonal pyramids share a common S atom to form a Sb2S5 unit. Two S atoms of this group have a bond to Mn2+ yielding a MnSb2S3 heteroring in the boat conformation. The Sb2S5 moieties are joined via common corners into the final undulated [Sb2S4]2- anion which is directed along [001]. The structure of 2 contains the [Mn(tren)]2+ ion, one SbS3 pyramid, and a SbS4 unit. Two symmetry-related SbS4 groups share an edge, forming a Sb2S6 group containing a Sb2S2 ring. This group is joined via corners to two SbS3 pyramids on both sides producing a Sb4S4 ring. The Sb2S2 and Sb4S4 rings are condensed into the final [Sb2S4]2- anion which runs along [010]. The [Mn(tren)] groups are bound to the thioantimonate(III) backbone on opposite sides of the Sb4S4 ring, and a small MnSbS2 ring is formed. In both structures, weak S...H bonds are found which may contribute to the stability of the materials. The two compounds decompose in one step upon heating, and only MnS and Sb2S3 could be identified as the crystalline part of the decomposition products. Both compounds can also be prepared under solvothermal conditions using MnSb2S4 as starting material. Compounds 1 and 2 are obtained from this ternary material in a high yield.
Schaefer
Michael
M
Institut für Anorganische Chemie, Christian-Albrechts-Universität Kiel, Olshausenstrasse 40, D-24098 Kiel, Germany.
Kurowski
Daniel
D
Pfitzner
Arno
A
Näther
Christian
C
Rejai
Zomaje
Z
Möller
Karina
K
Ziegler
Nancy
N
Bensch
Wolfgang
W