Selective photo-deposition of Cu onto the surface of monodisperse oleic acid capped TiO2 nanorods probed by FT-IR CO-adsorption studies.
A novel, non-aqueous, organometallic route to nanocomposite Cu@TiO2 materials is presented. TiO2 nanorods stabilized with oleic acid (OLA) were used as support for the photo-assisted deposition of Cu using the organometallic Cu(II) precursor [Cu(OCH(CH3)CH2N(CH3)2)2] (1). The copper precursor penetrates through the shell of OLA and is photo reduced to deposit Cu0 directly at the surface of the TiO2 rods. The obtained Cu decorated nanorods were still soluble in nonpolar organic solvents without change of the morphology of nanorods. The Cu@TiO2 colloid was characterized by means of UV-VIS, XRD, AAS, and HRTEM. FTIR CO adsorption studies provide evidence for Cu0 anchored at the titania surface by a characteristic absorption at 2084 cm-1. Comparative studies of Cu-deposition were performed using CuCl2 as simple Cu source which proved that the concept of organometallic disguise of the metal centre results in a higher reaction rate and the circumvention of non-selective reduction, parasitic side reactions and undesired agglomeration of the OLA stabilized titania nanorods.
Hikov
Todor
T
Department II of Inorganic Chemistry - Organometallics & Materials, Ruhr-University Bochum, Universitätsstrasse 150, D-44780, Bochum, Germany.
Schroeter
Marie-Katrin
MK
Khodeir
Lamma
L
Chemseddine
Abdelkrim
A
Muhler
Martin
M
Fischer
Roland A
RA