Radiation damage induced by krypton ions in sintered alpha-Al2O3.
Alpha-alumina is a useful thermoluminescence (TL) dosemeter. The knowledge of its behaviour under irradiation is thus of primary importance. The purpose of this paper is to characterise the radiation damage produced by swift krypton ions using various experimental methods, namely TL, optical absorption, fluorescence and electron paramagnetic resonance (EPR). After ion irradiation, the TL intensity is shown to decrease, whereas the optical absorption rises in the whole studied wavelength range. These two phenomena seem to be related to one another. Furthermore, optical absorption measurements highlight the appearance of new absorption bands probably owing to oxygen vacancies. Induced defects are also observed in the EPR spectra of irradiated pellets. They are likely related to electronic holes trapped on oxygen ions. The concentration of these defects increases with ion fluence and fluorescence measurements indicate that some pre-existing defects such as F2(2+) centres follow the same trend up to approximately 4.1 x 10(13) ions cm(-2).
Dalmasso
C
C
Laboratoire de Physique Electronique des Solides, Centre de Recherche sur les Solides et leurs Applications (LPES-CRESA) EA 1174, Université de Nice-Sophia Antipolis, Parc Valrose, F-06108 Nice Cedex 2, France. chrystelle.dalmasso@unice.fr
Iacconi
P
P
Beauvy
M
M
Lapraz
D
D
Balan
E
E
Calas
G
G
D000537:Aluminum Oxide / Q000737:chemistry* / Q000528:radiation effects*; D004307:Dose-Response Relationship, Radiation; D020450:Heavy Ions; D006358:Hot Temperature; D007726:Krypton; D008422:Materials Testing; D011829:Radiation Dosage; D013819:Thermoluminescent Dosimetry / Q000295:instrumentation / Q000379:methods*
D007726:Krypton; D000537:Aluminum Oxide