title: CdZnTe array detectors for synchrotron radiation applications.
abstract: An X-ray linear-array detector was fabricated using high-pressure Bridgman-grown CdZnTe. The detector area was 175 x 800 microm and the pitch size was 250 microm. The measured dark current for the test 16-element detector was as low as 0.1 pA at 800 V cm(-1) with excellent uniformity. Energy spectra were measured using a 57Co radiation source. Both a small-pixel effect and charge sharing were observed. For the arrays, an average 5.8% full width at half-maximum (FWHM) at the 122 keV photopeak was obtained with a standard deviation of 0.2%. A large-area detector (1 x 1 cm) of the same material before fabrication exhibited a low-energy tail at the photopeak, which limits the photopeak FWHM to 8%, typically due to hole trapping. At energies below 60 keV, charge sharing between elements was observed. The charge sharing was greatly reduced by providing a path to ground for unwanted charges. A prototype readout electronic system for an eight-channel array detector was developed. A readout system intended for a multielement solid-state detector system was also used. The array detector will be used for high-energy diffraction and Compton scattering measurements at the Advanced Photon Source.
authors: Department of Physics, University of Illinois at Chicago, Chicago, IL 60607-70592, USA.
authors: S S
authors: SS
authors: Yoo
authors: G
authors: G
authors: Jennings
authors: P A
authors: PA
authors: Montano